Method for producing vanadiferous pigiron by adopting vanadiferous converter steel slag

A converter steel slag and pig iron technology is applied in the field of metallurgy, which can solve the problems of low vanadium recovery rate and high cost, and achieve the effects of avoiding waste, simple process steps and broad application prospects.

Inactive Publication Date: 2011-07-20
PANZHIHUA GANGCHENG GROUP
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it is limited by the low vanadium recovery rate and high cost due to the high impurities.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The specific implementation of the present invention will be further described below in conjunction with the examples, and the present invention is not limited to the scope of the examples.

[0019] Embodiment adopts the inventive method to produce vanadium-containing pig iron

[0020] 1. Material ingredients

[0021] The main chemical composition of the vanadium-containing converter steel slag used is shown in Table 1, and the weight ratio of each material is shown in Table 2.

[0022] Table 1 Main chemical composition (wt%) of vanadium-containing converter steel slag

[0023] CaO

[0024] Table 2 Chemical dosage ratio of each material

[0025] product name

[0026] 2. Smelting

[0027] The furnace is opened by the coke furnace method. Before starting the furnace, empty the furnace chamber and preheat the mixture of low vanadium steel slag, iron-containing materials and coke. After charging, power transmission, arc starting, temperature rise, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for producing vanadiferous pigiron by adopting vanadiferous converter steel slag, which belongs to the field of metallurgy. The invention aims to provide a method for producing vanadiferous pigiron by adopting low-grade vanadiferous converter steel slag, comprising the following steps of: a, material mixing: evenly mixing vanadiferous converter steel slag, ferruginous materials, coke, river sand and fluorite in a certain weight proportion; b, smelting: heating the materials in the step a to the temperature of 1600-1650 DEG C, and preserving the heat for 2-4 hours for smelting to obtain iron scraps and molten iron; and c, separation: separating the iron scraps and the molten iron obtained in the step b, and cooling the molten iron to obtain vanadiferous pigiron. The method of the invention has simple technical steps, supplies a new way for recovering vanadium resources in the vanadiferous converter steel slag, in particular low-grade vanadiferous converter steel slag, and has wide application potential.

Description

technical field [0001] The invention relates to a method for producing vanadium-containing pig iron by using vanadium-containing converter steel slag, belonging to the field of metallurgy. Background technique [0002] Converter steel slag is the second largest metallurgical solid waste, and its comprehensive utilization rate is only about 10% at present, and most of it is used in low-grade applications such as cement iron correction material, dry-mixed mortar and road aggregate, which not only reduces The economic utilization value of the converter steel slag also wastes resources such as vanadium and iron in the converter steel slag. [0003] Yang Subo et al., Extraction and recovery of vanadium in vanadium-containing converter slag, "Steel", No.4, (2005) discloses the high-grade vanadium-containing converter slag (V 2 o 5 >2%) use the overfire method to extract vanadium, carry out pyrometallurgical treatment on the vanadium-containing converter steel slag to obtain v...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21B11/00C21B13/00C21B5/00
CPCY02P10/20
Inventor 蒋光旭彭绍强钱强戚明强戈文荪何为
Owner PANZHIHUA GANGCHENG GROUP