Method for manufacturing anti-cracking solid wood composite blue and white porcelain floor

Abstract

The invention discloses a method for manufacturing an anti-cracking solid wood composite blue and white porcelain floor. The method comprises the following steps of: firstly drying the solid wood to produce blanks and processing the blanks into solid wood veneer; then injecting glue on the surface of the solid wood veneer and drying the solid wood veneer for one or more times; and finally, hot-pressing and compounding a layer of anti-cracking layer on a base material to produce the finished products. Glue, chemicals or coatings are injected for two times on the surface of the solid wood veneer in a negative-pressure vacuum tank injection mode and water of the solid wood veneer is dried so as to completely close or block pits or wood eyes of the solid wood; the solid wood veneer has low water-adsorbing capacity and is difficult to crack or deform after being used for a long time; when the solid wood veneer is compounded on the base material, anti-cracking layers such as a non-woven fabric and the like are adopted to better avoid cracking; and the service life is prolonged, the using effect is good, and the products produced by the method has a visual effect similar to that of blue and white porcelain. The method has the characteristics of capability of reducing water-adsorbing capacity and avoiding cracking, long service life, good using effect, and visual effect similar to that of the blue and white porcelain. The method can be applied in the field of solid wood composite products such as furniture industries and the like.

Description

technical field [0001] The invention relates to a method for manufacturing an anti-crack composite wood floor, in particular to a method for manufacturing an anti-crack solid wood composite blue-and-white porcelain floor. Background technique [0002] As the requirements of people's living environment are getting higher and higher, people are very fond of wooden floors that can create a warm, comfortable and natural atmosphere. Now people especially like solid wood composite floors, because solid wood composite floors can make people feel Natural atmosphere, high-grade and thick, combines the long-standing traditional Chinese culture with modern fashion factors, integrates into it, endows solid wood composite flooring with new connotations, and makes it more humane, practical and modern. [0003] Consumers in the market now like some South American materials (such as: jatoba, dragonfly sandalwood (erqiaodou), red sandalwood, black locust, acacia, etc.) to make solid wood com...

AI Technical Summary

Problems solved by technology

[0003] Consumers in the market now like some South American materials (such as: jatoba, dragonfly sandalwood (erqiaodou), red sandalwood, black locust, acacia, etc.) to make solid wood composite flooring, but currently in the process of solid wood veneer processing It is only through simple paint processing without blocking or closing the pits or wood eyes on the surface of the solid wood, so that the solid wood composite floor made of solid wood veneer compounded on the substrate absorbs more water during use, making it easier to crack (except Solid wood composite flooring with a thickness of ≤0.6mm is not easy to crack), thick-skinned solid wood composite floors above 0.6mm are easy to crack, especially thick-skinned solid wood composite floors above 2.0mm are very easy to crack, so the service life will not be long enough , once cracked, the use effect is not ideal