A technology of high-speed railway and manufacturing method, applied in the field of aluminum material for high-speed railway catenary and its manufacturing, can solve the problems of power supply system damage, paralysis of the overall operation power supply system, etc., and achieve the effect of improving corrosion resistance

Active Publication Date: 2011-01-05
FOSHAN GOLDEN SOURCE ALUMINUM PROD
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The components of the catenary system are the joints and links of the catenary system. Any damage to the components of the catenary means the destruction of the power supply system and paralyzes the overall operation and power supply system.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach 1

[0022] Aluminum material contains 0.9% silicon, 0.18% iron, 0.07% copper, 0.05% zinc, 0.85% magnesium, 0.2% chromium, 0.6% manganese, 0.1% titanium and other The amount of aluminum and the impurities brought in during the preparation. The tensile strength ab of the aluminum material is 390, the yield point Q0.2 is 360, and the elongation S is 16%.

Embodiment approach 2

[0024] Aluminum material contains calculated by weight percentage: 0.83% silicon, 0.15% iron, 0.04% copper, 0.04% zinc, 0.78% magnesium, 0.12% chromium, 0.45% manganese, 0.08% titanium, The remaining amount of aluminum and impurities brought in during preparation. The tensile strength ab of the aluminum material is 360, the yield point Q0.2 is 350, and the elongation S is 14%.

Embodiment approach 3

[0026] Aluminum material contains calculated by weight percentage: 0.9% silicon, 0.18% iron, 0.04% copper, 0.05% zinc, 0.78% magnesium, 0.2% chromium, 0.6% manganese, 0.1% titanium, The remaining amount of aluminum and impurities brought in during preparation. The tensile strength ab of the aluminum material is 370, the yield point Q0.2 is 320, and the elongation S is 13%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to view more

Abstract

The invention discloses an aluminium material for contact nets on a rapid transit railway and a manufacturing method thereof. The aluminium material comprises the following components by weight percent: 0.83%-0.9% of silicon, not more than 0.18% of iron, 0.04%-0.07% of copper, not more than 0.05% of zinc, 0.78-%-0.85% of magnesium, 0.12%-0.2% of chromium, 0.45%-0.6% of manganese and not more than 0.1% of titanium, and the balance of aluminium and impurities brought while the aluminium material is manufactured. The manufacturing method of the aluminium material comprises the steps of casting, annealing, extruding and quenching. In the invention, the aluminium material has a performance exceeding the international standard, high tensile strength ab of not less than 330, high yield point Q0.2 of not less than 310 and high elongation rate S of not less than 13% and improves the corrosion stability, the impact toughness and the bending property.

Description

technical field [0001] The invention relates to a material and a manufacturing process of a special aluminum material for a high-speed railway catenary. Background technique [0002] Catenary is a huge space mechanical system, which uses components to achieve orderly connection and connection, and connects contact wires, catenary cables, support devices, insulating components, electrical equipment and pillars into a system that can transmit electric energy and has support. Functional, yet mechanically robust system as a whole. This system should be able to withstand the invasion of various meteorological conditions in nature and ensure good power transmission to electric locomotives running at high speed. [0003] The components of the catenary are the joints and links of the catenary system. Any damage to the components of the catenary means the destruction of the power supply system, which will paralyze the overall operation and power supply system. In a certain sense, c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/02C22C1/06C22F1/043
Inventor 谭柳玉
Owner FOSHAN GOLDEN SOURCE ALUMINUM PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap