Metallized polyimides film and flexible circuit board using the same

A technology of polyimide film and metal film, which is applied in the direction of circuit substrate materials, improvement of metal adhesion of insulating substrates, metal layered products, etc., can solve problems such as polyimide film peeling, and achieve high industrial value Effect

Active Publication Date: 2011-01-19
SUMITOMO METAL MINING CO LTD
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] However, since the wire bonding of the inner lead portion of the wiring with a pitch of 25 μm is performed at 400° C. or higher under pressure, high heat and pressure are concentrated on the narrow tip of the inner lead. Next, there is a problem that the top end of the inner lead and the polyimide film peel off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metallized polyimides film and flexible circuit board using the same
  • Metallized polyimides film and flexible circuit board using the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0102] First, use an oxygen transmission rate of 450cm 3 / (m 2 24 hours 1013hPa), water absorption rate is 1.8%, thermal expansion coefficient is 11ppm / ℃ in TD direction, and if figure 1 As shown in the X-ray diffraction results of the film shown, only a peak with a full width at half maximum of 1.0° was found at 2θ=14°, and a long polyimide film with a thickness of 35 μm mainly composed of biphenyltetracarboxylic acid (manufactured by Kaneka Co., Ltd. 35FP), using a sputtering device consisting of an uncoiler, a sputtering device, and a winding machine, on one side of the polyimide film, an average thickness of The chromium-nickel alloy layer of 20 mass % Cr is used as the metal film. Then, likewise, an average thickness of copper film.

[0103] Next, a copper layer having a thickness of 8 μm was formed on the copper film by electrolytic copper plating to obtain a metallized polyimide film. The electrolytic plating bath used was a copper sulfate plating bath with a cop...

Embodiment 2

[0107] A flexible wiring board was produced in the same manner as in Example 1 except that the metallized polyimide film obtained in Example 1 was used, and the wiring pitch was 25 μm, and the rate of poor bonding was obtained in the same manner as in Example 1. It can be seen that the bonding ratio of the inner lead and the polyimide film is 0.005%, and there is sufficient dimensional reliability even if a fine pitch is formed.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a metallized polyimides film and a flexible circuit board using the same. The technical scheme aims to provide a metallized polyimides film whose close strength of initial stage is over 900N / m, and over 600 N / m after a PCT test, and to provided a flexible circuit board using such films. The polyimides film is 35 Mum in thickness, 300-500cm3 / m2 / 24 hours in oxygen permeating rate tested under 1013 hPa, 1-3% in water absorption rate, and 10ppm / DEG CC18 ppm / DEG C. A metal thin film is formed by using any one metal of nickel, chromium and nickel-chrome alloy through a dry plating method on the surface of the polyimides film, and a copper thin film is formed on top of the metal thin film, and a copper layer is disposed on the copper thin film through a wet plating method. The total thickness of the metal film, the copper thin film and the copper layer is less than 20 Mum.

Description

technical field [0001] The present invention relates to a metallized polyimide film and a flexible circuit board obtained by using the film; more specifically, it relates to a metallized polyimide film having an initial adhesion strength of 900 N / m or more and after a PCT test, an adhesion strength of 600 N / m or more. A polyimide film, and a flexible circuit board obtained by using the film. Background technique [0002] The substrates that form electronic circuits and carry these electronic components include hard plate-like "rigid circuit boards" and film-shaped "flexible circuit boards" that are flexible and can be bent freely (hereinafter, sometimes referred to as "FPC"). ). In particular, FPC produces this kind of flexibility and can be used in parts that require flexibility, such as circuit boards for LCD drivers, hard disk drives (HDD), digital versatile disc (DVD) modules, and hinges of mobile phones. Demand is gradually increasing. [0003] However, such a flexib...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H05K1/03H05K3/38B32B15/088B32B27/34
CPCB32B15/015B32B15/088B32B15/20H05K3/46
Inventor 曾根博文小笠原修一
Owner SUMITOMO METAL MINING CO LTD