Flame-retardant plastics for communication cables and preparation method thereof

A technology of flame-retardant plastics and communication cables, which is applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problems of high risk, high cost of trial production, and high cost of certification, and achieve simple processing technology and better flame-retardant performance. , Flame retardant grade with high performance effect

Inactive Publication Date: 2011-01-26
DONGGUAN YUEFENG ELECTRONICS TECH
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] 3) Long trial production cycle, high cost of trial production, high certification cost, and long certification cycle: This kind of problem is a problem that every enterprise must face: relatively high investment, long test cycle, relatively large risk, market The competition is fierce!

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The following examples will be more helpful to understand the present invention, but do not limit the content of the present invention.

[0020] In this embodiment, the flame-retardant plastic for communication cables includes the following components by weight percentage:

[0021] Polyvinyl chloride powder: 46.0 parts

[0022] Calcium carbonate: 24.0 parts

[0023] Calcium zinc stabilizer: 2.5 parts

[0024] Antimony trioxide: 2.0 parts

[0025] Polyethylene wax: 0.5 parts

[0026] Diisononyl phthalate: 9.0 parts

[0027] Didecyl phthalate: 15.0 parts

[0028] Soybean Oil: 1.0 parts.

[0029] Among the aforementioned raw materials, the polyvinyl chloride resin is preferably S-65 type resin, so as to obtain better processability, heat resistance, cold resistance, surface and deformability. The calcium carbonate (CaCO3) acts as a filler to reduce the overall cost of the formula. The calcium-zinc stabilizer is preferably 328W type stabilizer, which has better heat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses flame-retardant plastics for communication cables and a preparation method thereof. The flame-retardant plastics for communication cables comprises the following components in parts by weight: 46 parts of polyvinyl chloride powder, 24 parts of calcium carbonate, 2.5 parts of calcium-zinc stabilizer, 2.0 parts of antimony trioxide, 0.5 part of polyethylene wax, 9.0 parts of diisononyl phthalate, 15.0 parts of didecyl phthalate and 1 part of soybean oil. The plastics prepared according to the formula of the invention can achieve the combustion level of CMR. Compared with other communication cable formulae, such as CMX and CM / CMG, the invention has the advantages of better flame retardancy, higher environment-friendly performance, higher temperature level and wider application range. Compared with other communication cables made of LSZH and TELFON materials, the invention has the advantages of no need of special processing equipment, simple processing technique and low cost.

Description

technical field [0001] The invention relates to the technology in the field of communication cable insulation materials among industrial polymer materials, in particular to a flame-retardant plastic for communication cables and a preparation method thereof. Background technique [0002] At present, domestic companies that can use PVC to produce ordinary communication cable formulas are more common in companies that pass combustion performance tests such as CMX and CM / CMG levels of combustion performance tests, but if they can pass CMR or even higher levels of combustion such as CMP level but very few. In order to solve this kind of problem that cannot be burned, most CMR and CMP combustion grade wires are made of plastics based on LSZH, TELFON or other materials to produce communication cables, but the corresponding machine equipment costs, manufacturing costs and processing costs will greatly increase; on the other hand, some foreign companies also consider the choice of p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L23/06C08K13/02C08K3/26C08K3/22C08K5/12C08K5/1515H01B3/44
Inventor 孙伟
Owner DONGGUAN YUEFENG ELECTRONICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap