Anhydrous stemming for blast-furnace tapping hole

An anhydrous taphole and tap hole technology, applied in the field of refractory materials, can solve the problem of difficult to deal with long-term slag and iron scouring, and achieve the effect of good air permeability and stable volume

Inactive Publication Date: 2011-02-09
HUNAN XIANGGANG RUITAI TECH +1
View PDF4 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, if the opening is opened immediately after only about 30 minutes of sintering, the strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example one:

[0029] (1) Weigh the raw materials according to the following ratio:

[0030] Coke 2~0㎜ 16%

[0031] Super high aluminum material 3~1㎜ 10%

[0032] Super high aluminum material 1~0㎜ 5%

[0033] Brown corundum ≤0.088㎜ 5%

[0034] Silicon carbide (90#) 1~0㎜ 10%

[0035] Silicon carbide (90#) ≤0.088㎜ 10%

[0036] Guangxi clay ≤0.088㎜ 16%

[0037] High temperature asphalt ≤0.088㎜ 8%

[0038] Sericite ≤0.088㎜ 10%

[0039] Refined quartz sand 40~70 mesh 10%

[0040] Resin (liquid) 3%

[0041] Tar (mixed tar and anthracene oil) Proportion 1.15~1.16 13%

[0042] (2) Weigh the above solid powder in proportion, then pour it into a heated mixer for dry mixing for 5 minutes, then add the liquid binder (first add the resin, and then add the tar or mixed oil), and mix 40 Minutes, then take the mud to make the Marsha value. If the Marsha value is higher than 1MPa, increase the oil appropriately until the Marsha value drops below 1MPa, then discharge the material, squeeze the mud through ...

Example Embodiment

[0043] Embodiment two:

[0044] (1) Weigh the raw materials according to the following ratio:

[0045] Coke 2~0㎜ 16%

[0046] Super high aluminum material 3~1㎜ 10%

[0047] Brown corundum 1~0㎜ 5%

[0048] Brown corundum ≤0.088㎜ 5%

[0049] Silicon carbide (90#) 1~0㎜ 10%

[0050] Silicon carbide (90#) ≤0.088㎜ 10%

[0051] Guangxi clay ≤0.088㎜ 16%

[0052] High temperature asphalt ≤0.088㎜ 8%

[0053] Sericite ≤0.088㎜ 10%

[0054] Refined quartz sand 40~70 mesh 10%

[0055] Resin (liquid) 3%

[0056] Tar (mixed tar and anthracene oil) Proportion 1.15~1.16 13%

[0057] (2) Weigh the above solid powder in proportion, then pour it into a heated mixer for dry mixing for 5 minutes, then add the liquid binder (first add the resin, and then add the tar or mixed oil), and mix 40 Minutes (rotating speed is 14 rpm), and then take the mud to make the Marcia value. If the Marcia value is higher than 1MPa, increase the oil appropriately until the Marcia value drops below 1MPa, then discharge the material and ...

Example Embodiment

[0058] Embodiment three:

[0059] (1) Weigh the raw materials according to the following ratio:

[0060] Coke 2~0㎜ 16%

[0061] Brown corundum 3~1㎜ 10%

[0062] Brown corundum 1~0㎜ 5%

[0063] Brown corundum ≤0.088㎜ 5%

[0064] Silicon carbide (90#) 1~0㎜ 10%

[0065] Silicon carbide (94#) ≤0.088㎜ 10%

[0066] Guangxi clay ≤0.088㎜ 16%

[0067] High temperature asphalt ≤0.088㎜ 8%

[0068] Sericite ≤0.088㎜ 10%

[0069] Refined quartz sand 40~70 mesh 10%

[0070] Resin (liquid) 3%

[0071] Tar (mixed tar and anthracene oil) Proportion 1.15~1.16 12%

[0072] (2) Weigh the above solid powder in proportion, then pour it into a heated mixer for dry mixing for 5 minutes, then add the liquid binder (first add the resin, and then add the tar or mixed oil), and mix 40 Minutes, then take the mud to make the Marsha value. If the Marsha value is higher than 1MPa, increase the oil appropriately until the Marsha value drops below 1MPa, then discharge the material, squeeze the mud through a mud squeezer, put...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anhydrous stemming for a blast-furnace tapping hole. Tar oil with specific weight of 1.15-1.16 or mixed oil of tar oil and anthracene oil is used as a binding agent, more than 50% of coarse and middle particles are added into a particle composition of the formulation, the content of fine powder with the particle size not more than 0.088 mm is controlled below 50%, a great amount of sericite is added into the formulation, and 40-70 mesh refined quartz sand is added. The stemming has good air permeability and rapid sintering performance and can be rapidly hardened within 20-30 min, the gas can be exhausted through ventilation holes, the strength of the stemming can be rapidly increased within short time and can satisfy about 30 min continuous opening tapping of single tapping holes of large and medium blast furnaces.

Description

Technical field [0001] The invention belongs to refractory materials, in particular to a formula of anhydrous taphole mud suitable for tapholes of large and medium-sized blast furnaces in steelworks and a production process thereof. Background technique [0002] At present, large and medium-sized blast furnaces in steelmaking plants have 2 to 4 tapholes (also known as tapholes), and generally the two tapholes tap iron alternately. However, in some special cases (such as the failure of a certain taphole mud gun or tapping machine, the need for pouring or overhaul of the tap trough, and other situations) it is necessary or only possible to use a single taphole for continuous tapping instead of Multiple tapholes can alternately tap iron, so the performance of the taphole clay required in this case is completely different from that required for multiple tapholes to tap iron alternately. When continuous tapping of single tap hole, the tap interval time of the same tap hole is ob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B35/66
Inventor 陆晓峰章兴高姚建材吕建江刘利华
Owner HUNAN XIANGGANG RUITAI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap