High-insulation low-static anti-wrinkle heat-seal type functional film

A wrinkle heat-sealable, functional film technology, applied in the direction of flexible coverings, packaging, wrapping paper, etc., can solve the problems of uncompact surface, poor barrier property, high heat-sealing temperature affecting packaging speed, etc., to achieve bright surface, heat seal easy effect

Inactive Publication Date: 2011-03-23
JIESHOU CITY TIANHONG PACKAGING MATERIAL
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, during the use of films, in order to achieve different effects of product packaging, the requirements for films are getting higher and higher, especially biaxially oriented polypropylene films (BOPP), which are widely used in outer film packaging such as tobacco. Wrinkles cannot be produced on the surface of the film in a long-term natural environment. The film produced by the existing film production process has poor chemical resistance and is easy to react with heavy-colored inks, especially bright red and green, to cause wrinkles. The other is the shrinkage rate. The surface of the small package is not compact and affects the appearance of the product, the high heat sealing temperature affects the packaging speed, and the barrier property is poor
As a result, the film is always unsatisfactory when used

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1, a high-barrier, low-static anti-wrinkle heat-sealable functional film, characterized in that the components of the functional film and the content ratio of each component are as follows:

[0024] PVC 910-920‰

[0025] Stabilizer 15-20‰

[0026] H-16 15-20‰

[0027] AC31 61-2‰

[0028] MBS 25-30‰

[0029] Oxidized polyethylene 4-5‰

[0030] Silica 0.08-0.1‰

[0031] ACR 5-6‰

[0032] Epoxidized soybean oil 8-10‰

[0033] Among them, PVC is polyvinyl chloride polyhydrogen. The stabilizer is a general dosage form, specifically octyltin maleate. AC316 is polyethylene wax. MBS is a terpolymer of methyl methacrylate (M), butadiene (B) and styrene (S). ACR is an acrylate copolymer.

[0034] According to the above components, PVC 916‰, stabilizer 17‰, H-1618‰, AC3161.8‰, MBS 2.7‰, oxidized polyethylene 4.6‰, silicon dioxide 0.09‰, ACR 5.5‰, epoxy soybean oil 9‰ After the proportion of the components is fully mixed, it can be added to a blow molding mac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-insulation low-static anti-wrinkle heat-seal type functional film which comprises the following components of PVC, stabilizing agent, H-16, AC316, MBS, oxidized polyethylene, silicon dioxide, ACR and epoxidized soybean oil, wherein PVC is polyvinyl chloride and poly aluminum hydrogen; the stabilizing agent is a common agent, in particular OM1; AC316 is tissuemat E; MBS is the terpolymer of methyl methacrylate (M), butadiene (B) and styrene (S); and ACR is acrylate copolymer. The components are fully mixed and then made into a film by using a blow molding machine. The high-insulation low-static anti-wrinkle heat-seal type functional film is prepared by the following steps of: fully mixing the components in proportion by weight and finally loading in the blow molding machine. The products produced by the technology has the advantages of no poison, high diaphaneity, bright surface, impact resistance, tear resistance, no combustion, no moisture absorption, and simple and firm heat seal, and is particularly suitable for meeting requirements of various high-speed automatic packaging machines.

Description

technical field [0001] The invention relates to a packaging film, in particular to a high-barrier, low-static anti-wrinkle heat-sealable functional film. Background technique [0002] At present, during the use of films, in order to achieve different effects of product packaging, the requirements for films are getting higher and higher, especially biaxially oriented polypropylene films (BOPP), which are widely used in outer film packaging such as tobacco. Wrinkles cannot be produced on the surface of the film in a long-term natural environment. The film produced by the existing film production process has poor chemical resistance and is easy to react with heavy-colored inks, especially bright red and green, to cause wrinkles. The other is the shrinkage rate. The surface of the small package is not compact, which affects the appearance of the product, and the high heat sealing temperature affects the packaging speed, and the barrier property is poor. As a result, the film is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L51/00C08L23/30C08L33/04C08K13/02C08K5/57C08K3/36C08K5/1515B65D65/38
Inventor 吴磊胡伟张德顺王若愚梅艳玲王建华
Owner JIESHOU CITY TIANHONG PACKAGING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products