Material for aluminium electrolysis crust breaking chip

A shell hammer and aluminum electrolysis technology, applied in the material field of aluminum electrolysis shell hammer, can solve the problems of poor corrosion resistance, poor wear resistance, low steel hardness, etc., to achieve high corrosion resistance and reduce production. Cost and effort, the effect of extending the replacement cycle

Active Publication Date: 2012-02-01
GUIZHOU BRANCH CHINA ALUMINUM IND
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The steel of these materials has low hardness, low melting point, poor wear resistance and poor corrosion resistance, so the service life is short and needs to be replaced every 3-4 months

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] The material used for the shelling hammer is 0.7% carbon, 0.8% silicon, less than 0.05% phosphorus, less than 0.05% sulfur, less than 0.05% Ni, 53% tungsten carbide, 5.3% titanium carbide, and the rest is iron. The process of powder metallurgy is used for roasting and one-time forming.

Embodiment 2

[0011] The material used for the shelling hammer is 1.0% carbon, 0.5% silicon, less than 0.05% phosphorus, less than 0.05% sulfur, less than 0.05% Ni, 60% tungsten carbide, 9.2% titanium carbide, and the rest is iron. The process of powder metallurgy is used for roasting and one-time forming.

Embodiment 3

[0013] The material used for the shelling hammer is 0.26% carbon, 0.7% silicon, less than 0.05% phosphorus, less than 0.05% sulfur, less than 0.05% Ni, 70% tungsten carbide, 10% titanium carbide, and the rest is iron. The process of powder metallurgy is used for roasting and one-time forming.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a material for an aluminium electrolysis crust breaking chip. The invention is characterized in that the material comprises the following components by weight percent: 50%-70% of tungsten carbide, 5%-10% of titanium carbide, 0.01%-1.0% of carbon, 0.5%-1.0% of silicon, less than 0.05% of phosphorus, less than 0.05% of sulfur, less than 0.05% of nickel and the balance iron. The invention discloses the high hardness crust breaking material; and the material for the crust breaking chip is designed again and uses tungsten carbide as the basic material, thus the service life of the crust breaking chip can be increased, the replacement cycle can be prolonged, the production cost can be reduced and the labor intensity is lowered.

Description

technical field [0001] The invention relates to a material for aluminum electrolytic shelling hammer. Background technique [0002] At present, the material used for electrolytic aluminum shelling hammers is generally forged Q235, cast ZG235-270 steel or other ordinary carbon steel. The steel of these materials has low hardness, low melting point, poor wear resistance, and poor corrosion resistance, so the service life is short, and it needs to be replaced every 3-4 months. Patent 200610050934.1 designed a shelling hammer made of ZG30Cr26Ni5 or ZG30Cr20Ni10 steel in accordance with GB / T8492-1987; 0.2-1.5%, Cr 25.0-35.0%, P and S<0.05%, mixed rare earth 0.075-0.1%) as the shelling hammer, the common feature of these two materials is to increase the Cr content in the hammer , Improve the hardness and melting point of steel. However, the improvement of material wear performance requires not only a high hardness, but also high strength and toughness. At the same time, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C29/08C25C3/14
Inventor 秦庆东邱仕麟黄海波
Owner GUIZHOU BRANCH CHINA ALUMINUM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com