Cellulosic and lignocellulosic structural materials and methods and systems for manufacturing such materials

A technology of lignocellulose and cellulose, applied in the system field of materials, can solve problems such as incompatibility

Inactive Publication Date: 2011-05-18
XYLECO INC
View PDF30 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Softer woods with lower flexural modulus are often available at lower cost, and in some cases may have desirable aesthetic properties, but are unsuitable for some applications due to their mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cellulosic and lignocellulosic structural materials and methods and systems for manufacturing such materials
  • Cellulosic and lignocellulosic structural materials and methods and systems for manufacturing such materials
  • Cellulosic and lignocellulosic structural materials and methods and systems for manufacturing such materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0209] Example 1-Method for determining the molecular weight of cellulose and lignocellulosic materials by gel permeation chromatography

[0210] This example illustrates how to determine the molecular weight of the materials discussed herein. The cellulosic and lignocellulosic materials used for analysis are processed as follows:

[0211] Get a 1500 lb pallet (skid) from International Paper with 30lb / ft 3 The original bleached white kraft cardboard of the bulk density. Fold the material flat and add it to a 3hp Flinch Baugh shredder at a rate of about 15 to 20 pounds per hour. The shredder is equipped with two 12-inch rotating blades, two fixed blades and a 0.30-inch discharge creen. Adjust the gap between the rotating blade and the fixed blade to 0.10 inches. The output from the paper shredder is similar to the shredded flower (as above). The material similar to shredded flowers is added to the SC30 Munson rotary knife cutting machine. The discharge screen has 1 / 8 inch holes...

Embodiment 2

[0234] Example 2-Radiation treatment of boxwood samples

[0235] The 1 / 8 inch thick boxwood board is treated with electron beam radiation (5MeV electron beam) at a dose of 1MRad to 100MRad. The number after “B” in the table below indicates the received dose (for example, B means no exposure Wood plank, B1 means plank that received 1MRad, and B10 means plank that received 10MRad). Then ASTM D 790 and D 143 were used to test the bending strength of the wood board (crosshead speed of 0.1 inch / min and span / thickness of 14:1), and ASTM D 638 to test the tensile strength (using type I specimens and 0.2 inch / Minute crosshead speed). The results of this test are shown in Tables I and II below.

[0236] Table I Summary of test results-bending strength

[0237] Sample identification

average

Bending strength (psi) single value

B

11600

10800，11900，10800，12000，12600

B1

13300

13600，12700，13800，13300

B3

20200

21400，20000，18700，20700

B5

16500

16100，15600，16700，17600

B7

...

Embodiment 3

[0240] Example 3-Preparation of sheared fibrous material from bleached kraft paperboard

[0241] A 1500 lb pallet obtained from International Paper has 30lb / ft 3 The original bleached white kraft cardboard of the bulk density. Fold the material flat and add it to a 3hp Flinch Baugh shredder at a rate of about 15 to 20 pounds per hour. The shredder is equipped with two 12-inch rotating blades, two fixed blades and a 0.30-inch discharge screen. Adjust the gap between the rotating blade and the fixed blade to 0.10 inches. The output from the shredder is similar to shredded paper. The material similar to shredded flowers is added to the SC30 Munson rotary knife cutting machine. The discharge screen has 1 / 8 inch holes. The gap between the rotating blade and the fixed blade is set to about 0.020 inches. The rotary knife cutting machine cuts the paper pieces that pass through the blade, which resemble shredded paper flowers. The material obtained from the first shear was recharged...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

Methods of treating wood and wood products include irradiating untreated wood having a first molecular weight with ionizing radiation to cause an increase in the molecular weight of a cellulosic component of the wood to a second, relatively higher molecular weight.

Description

Technical field [0001] The present invention relates to cellulosic and lignocellulosic structural materials, such as wood and wood fiber-based composite materials, and systems and methods for manufacturing such materials. Background technique [0002] Wood is the fibrous tissue present in the stems of woody plants such as trees and shrubs. According to an article by the University of Minnesota Extension, wood is generally composed of cellulose (about 50%), hemicellulose (about 15%-25%), and lignin (about 15%-30%). (http: / / www.extension.umn.edu / distribution / naturalresources / components / 6413chl.html.) [0003] Wood is used in many applications, such as building materials (including frame wood, decorative wood products, flooring, etc.), used in ships, toothpicks, butts, cabinets, furniture, sports equipment, and parts of weaving and knitting machines. In addition, many products are made by processing wood or wood fibers into other materials. For example, many products are made by di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27K5/00B27N1/00B05D7/06B05D3/06B05D3/00B32B21/14C08B15/10C08J3/28
CPCA63B2209/00C08B15/10B32B21/14B05D3/068C08J2397/02B27N1/00B05D3/002B05D7/06C08H8/00C08J3/28B27K5/003C08B15/04A63B59/06A63B2102/18A63B59/50A63B59/52B27K5/00D21C5/00D21H11/20B27K5/0035B27K5/004B27K5/0045
Inventor M·梅多夫
Owner XYLECO INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap