Expansion type flame-retardant polypropylene composite material and preparation method thereof

A technology of flame-retardant polypropylene and intumescent flame retardant, which is applied in the field of flame-retardant polypropylene materials, can solve the problems of low flame-retardant efficiency, large addition amount, and large hygroscopicity, and achieve high flame-retardant efficiency and low smoke density , the effect of small amount of smoke

Inactive Publication Date: 2011-07-27
SUN YAT SEN UNIV
View PDF3 Cites 39 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Patent CN101225187A discloses a novel triazine intumescent flame retardant, which is compounded with ammonium polyphosphate (APP) and used in PP to have good flame retardant performance, but the polar group in the reported char-forming agent More, resulting in greater hygroscopicity of the product
[0006] However, the intumescent flame retardants currently used still have the following disadvantages: 1. The flame retardant efficiency is low, and the addition amount is relatively large. Usually, it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Expansion type flame-retardant polypropylene composite material and preparation method thereof
  • Expansion type flame-retardant polypropylene composite material and preparation method thereof
  • Expansion type flame-retardant polypropylene composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0029] The preparation method of the above-mentioned flame retardant polypropylene composite material comprises the following sequential steps: (1) putting intumescent flame retardant, flame retardant synergist, antioxidant, anti-dripping agent and lubricant into a high-speed mixer according to the formula ratio Internal mixing for 8-20 minutes; (2) Put polypropylene into a high-speed mixer, and mix with the above-mentioned mixture for 5-20 minutes; (3) Extrude and granulate with a twin-screw extruder, or mix with a twin-roll mixer evenly.

[0030] The present invention will be further described below through specific examples, but the present invention is not limited to this specific example.

[0031] The triazine char-forming agent in each embodiment adopts the material of following structural formula respectively:

[0032]

Example Embodiment

[0033] Example 1

[0034] Accurately weigh 1.0kg of ammonium polyphosphate (APP), 0.5kg of triazine char-forming agent (CA1), 0.015kg of antioxidant 1010 and 0.005kg of zinc stearate, premix in high-speed dispersant for 8 minutes to obtain Intumescent flame retardant compound, then 3.48Kg of polypropylene pellets were added to the above intumescent flame retardant compound, premixed for 5 minutes, and finally extruded, cooled and pelletized in a twin-screw extruder, The halogen-free flame retardant polypropylene composite material can be obtained. Wherein, the temperature of each zone of the twin-screw extruder is set between 150-200°C. The oxygen index of the obtained intumescent flame-retardant polypropylene composite material was 35.6%, and the UL-94 test reached V-0 level.

Example Embodiment

[0035] Example 2

[0036] Accurately weigh 1.0kg of ammonium polyphosphate (APP), 0.5kg of triazine char-forming agent (CA2), 1680.015kg of antioxidant and 0.005kg of N,N-ethylenebisstearic acid amide (EBS). The dispersant was premixed for 10 minutes to obtain an intumescent flame retardant compound, and then 3.48Kg of polypropylene pellets were added to the above intumescent flame retardant compound, premixed for 5 minutes, and finally extruded in a twin-screw extruder. The halogen-free flame retardant polypropylene composite material can be obtained by extruding, cooling and pelletizing in the middle. Among them, the temperature of each zone of the twin-screw extruder is between 150-200°C. The oxygen index of the polypropylene composite is 29.5%, and the UL-94 test achieves a V-0 rating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an expansion type flame-retardant polypropylene composite material and a preparation method thereof. An expansion type flame retardant of the system is compounded by ammonium polyphosphate (APP) or melamine polyphosphate (MPP) and a novel triazine car-forming agent; and the expansion type flame-retardant polypropylene composite material is obtained by the following steps of: adding 10-40% of the expansion type flame retardant into 60-90% of polypropylene, mixing, extruding for pelleting, or mixing. The expansion type flame-retardant polypropylene composite material hasthe advantages of low smoke, no toxin, environment friendliness, high flame retardant efficiency, less volume of addition, good water resistance and the like; moreover, defects such as poor water resistance, low flame retardant efficiency and the like of traditional expansion type flame retardants are overcome, and the pollution on the environment and the harm to the human body, caused by flame-retardant materials, are effectively reduced.

Description

technical field [0001] The invention relates to the technical field of flame-retardant polypropylene materials, in particular to an intumescent flame-retardant polypropylene composite material and a preparation method thereof. Background technique [0002] Polypropylene (PP) has the advantages of good mechanical properties, processing properties, chemical corrosion resistance, electrical insulation and non-toxic light weight. It is a general-purpose plastic with excellent comprehensive properties and is widely used in household appliances, electronics, and building materials. , the automobile industry, packaging materials, etc. However, polypropylene also has some disadvantages, such as its oxygen index is only 17-18%, which is a flammable material; a large number of molten droplets are produced during combustion, which makes the flame spread, and the fire hazard is relatively high, which limits the use of polypropylene in high Use in occasions where flame retardancy is req...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/14C08K13/02C08K3/32C08K5/3492
Inventor 许家瑞冯才敏张艺刘四委蒋星池振国
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap