Ultrasonic flat type piezoelectric vibrator

A piezoelectric vibrator and flat-plate technology, applied in the direction of electrical components, impedance networks, etc., can solve problems affecting the performance and service life of ultrasonic piezoelectric ceramic devices, improve mechanical quality, increase sensitivity, and avoid protruding solder joints Effect

Inactive Publication Date: 2011-09-21
王伟
View PDF0 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In addition, in the electrode connection of the ultrasonic flat piezoelectric vibrator, silver paste (silver burning) is usually used, but in practical applications, this method exists in the flat piezoelectric vibrator, which seriously affects the performance of the ultrasonic piezoelectric ceramic device. and service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] Further description will be made below in conjunction with embodiments of the present invention.

[0017] One embodiment of the present invention is realized in the following manner:

[0018] An ultrasonic flat piezoelectric vibrator,

[0019] (1). The material of the ultrasonic flat piezoelectric vibrator is niobium zinc-lead niobium stannate;

[0020] (2). The chemical formula is Pb(Zn1 / 3Nb2 / 3)x(Sn1 / 3Nb2 / 3)yTizZr1-x-y-zO3);

[0021] (3). By setting x and y in the molecular formula of niobium zinc-lead niobate stannate material in the range of 0

[0022] After determining the optimal ratio of each component, manganese oxide (MnO2), antimony oxide (Sb2O3) and niobium oxide (Nb2O5) are added, and the weight of each additive is less than 2%.

[0023] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to an ultrasonic flat type piezoelectric vibrator which is made of niobium zinc-niobium lead stannate. The chemical molecular formula is Pb(Zn1 / 3Nb2 / 3)x(Sn1 / 3Nb2 / 3) yTizZr1-x-y-zO3. A proportioning test is carried out by setting x and y in the molecular formula of the niobium zinc-niobium lead stannate material to be within the ranges of 0<x<0.1 and 0<y<0.1 and respectively setting Ti and Zr to be within the range of 0.4 to 0.44; and the numerical values of x, y and z are determined from a test result, namely, the optimal proportion of each component is determined. In the design scheme, utilization performance is largely enhanced, service life is largely prolonged, the mechanical quality, the factor and the tensile strength of piezoelectric ceramics which are finished are improved, the sensibility of the ultrasonic flat type piezoelectric vibrator is enhanced, the loss is reduced, the tensile strength is improved, and the aging performance is improved. Piezoelectric ceramic chips and a silver electrode are connected through a red copper film the surface of which is coated with a stannum layer, thus, defects such as convex welding points, higher resistance and the like of a traditional product are avoided. The vibrator can carry heavier current, is difficult to break or burn out, and has excellent consistency and reliability; and the rate of finished products is increased to 99% from original 92%.

Description

technical field [0001] The invention relates to a piezoelectric ceramic product, in particular to an ultrasonic flat-plate piezoelectric vibrator. Background technique [0002] Since the discovery of PZT lead zirconate titanate piezoelectric ceramics in 1954, the United States, Japan, the Netherlands and many other countries have conducted detailed research on the system, and derived a series of PZT piezoelectric ceramic materials with superior performance. In-depth, its application range has also been greatly expanded. Based on lead zirconate titanate, ternary and quaternary piezoelectric ceramics improved with various elements also came into being. In 1965, Matsushita Electric Company of Japan introduced Pb(Mg1 / 3Nb2 / 3)03 was added to PZT as the third component to make the first ternary ceramics. It was found that adding some oxides to this ternary piezoelectric ceramics would improve the mechanical and electrical properties. Coupling coefficient KP and high mechanical qua...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H03H9/02H03H9/13
Inventor 王伟
Owner 王伟
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products