High-density polyethylene material and application thereof

A technology of high-density polyethylene and terephthalic acid, applied in the direction of fiber mechanical structure, etc., can solve the problems of inconvenient construction of optical cable protection sleeve, poor product stability, high friction coefficient, etc., achieve good self-lubricating performance, reduce friction coefficient, good gloss effect

Active Publication Date: 2013-12-18
江苏爱特恩高分子材料有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is: the friction coefficient of existing high-density polyethylene is high, which leads to high energy consumption in the preparation process, poor product stability, and inconvenient construction of the optical cable protection sleeve made

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-density polyethylene material and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Example 1: 100 parts by weight of high-density polyethylene, 80 parts of calcium terephthalate, 8 parts of active silicone oil, 5 parts of antioxidant 1010, mixed evenly by a vacuum kneader, and then using a twin-screw extruder at 170 ° C Extrude the mixed material into strips at high temperature and 1400 rpm, place it on the cross-section of the mold with a high-speed rotating cutter to cut it into pellets, and then cool it to get the finished product.

Embodiment 2

[0015] Embodiment 2: 100 parts by weight of high-density polyethylene, 70 parts of magnesium terephthalate, 8 parts of simethicone, 5 parts of antioxidant 168, after mixing uniformly by a vacuum kneader, use a twin-screw extruder to Extrude the mixed material into strips at a high temperature of 220°C and a speed of 1600 rpm, place it on the cross-section of the mold with a high-speed rotary cutter to cut it into pellets, and then cool it to obtain a finished product.

Embodiment 3

[0016] Embodiment 3: 100 parts by weight of high-density polyethylene, 5 parts of zinc terephthalate, 5 parts of 201 methyl silicone oil, 4 parts of antioxidant 264, after mixing uniformly by a vacuum kneader, use a twin-screw extruder to Extrude the mixed material into strips at a high temperature of 180°C and a speed of 1500 rpm, place it on the cross-section of the mold with a high-speed rotary cutter, cut it into pellets, and then cool it to obtain a finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-density polyethylene material and application thereof. The material comprises the components in percent by weight: 100% of high-density polyethylene, 5-80% of para-phthalic metal salt, 1-8% of silicone oil and 0.5-5% of antioxidant. The para-phthalic metal salt is selected from calcium terephthalate, magnesium terephthalate, zinc terephthalate, potassium terephthalate, sodium terephthalate, barium terephthalate, lead terephthalate, aluminum terephthalate, ferrum terephthalate or a mixture thereof. The silicone oil is selected from active silicone oil, dimethyl silicone oil, 201 methyl silicone oil or a mixture thereof. The antioxidant is selected from tris(2,4-ditert-butylphenyl) phosphate, pentaerythrite tetra [beta-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionate], 2,6-di-tert-butyl-4-methylphenol, 2,2'-methylenebis[6-(1,1-dimethylethyl)-4-methyl-phenol or a mixture thereof. The polyethylene material provided by the invention has a small friction coefficient and favorable self-lubricity and can be used for manufacturing optical cable protection sleeves.

Description

technical field [0001] The invention relates to a high-density polyethylene material and its application. Background technique [0002] Polymers usually have high viscosity after melting. During processing, when the molten polymer passes through narrow slits, gates and other flow channels, the polymer melt must produce friction with the surface of the processing machine. These frictions reduce the fluidity of the melt. At the same time, severe friction will make the surface of the equipment rough, lack luster or flow lines, and increase energy consumption; while excessive friction inside the polymer will reduce the stability of the polymer. Cracks are prone to appear on the surface of the product during processing. Lubricant is a kind of processing aid that can reduce the friction between materials and the surface of materials and processing equipment, and reduce the generation of frictional heat. [0003] Optical cables are usually buried underground. In order to effectiv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08K5/098G02B6/44
Inventor 方春平丁玉兰吴杰
Owner 江苏爱特恩高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products