Aluminum rolling oil additive composition

A technology for rolling oil and additives, applied in additives, lubricating compositions, petroleum industry, etc., can solve problems such as no oleic acid amide, achieve the effects of reducing friction coefficient, reducing cost, and improving annealing performance

Active Publication Date: 2011-11-02
石家庄新泰特种油有限公司
View PDF3 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Oleic acid amide is widely used in internal combustion engine oil and lubricating oil as a friction reducing agent, which can signific

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] (1) Oily agent: 200 g of monoglyceride oleate, 100 g of oleic acid;

[0033] (2) Phosphorus-containing antiwear agent: 150 g of tributyl thiophosphate;

[0034] (3) Oleic acid amide 350 g;

[0035] (4) 28 g of demulsifier, the HLB value of the first type of nonionic polymer surfactant is 5, and the molecular weight is 2000, the HLB value of the second type of nonionic polymer surfactant is 16, and the molecular weight is 5000. The mass ratio of the first type and the second type nonionic polymer surfactant is 1:1;

[0036] (5) Phenolic antioxidant: 2 g of di-tert-butyl-4-methylphenol;

[0037] (6) 170 g of 150N hydrogenated base oil;

[0038] Add the above-mentioned oily agent, hydrogenated base oil, phosphorus-containing anti-wear agent, and phenolic antioxidant into the enamel mixing kettle with agitator in sequence, stir at 60°C for 4 hours, then add oleic acid amide, demulsifier , and stirred at 40°C for 2 hours until the mixture was completely dissolved and bec...

Embodiment 2

[0041] (1) Oily agent: 300g of monoglyceride oleate, 180g of oleic acid;

[0042] (2) Phosphorus-containing antiwear agent: 39g of dipropyl phosphorothioate, 20g of basic diethyl phosphate;

[0043] (3) Oleic acid amide 260g;

[0044] (4) 10g of demulsifier, the HLB value of the first type of nonionic polymer surfactant is 9, and the molecular weight is 15,000, and the HLB value of the second type of nonionic polymer surfactant is 12, and the molecular weight is 8,000. The mass ratio of the first type and the second type nonionic polymer surfactant is 1:2;

[0045] (5) Phenolic antioxidant: 1g of 2,6-di-tert-butyl-p-cresol;

[0046] (6) 250N hydrogenated base oil: 190g;

[0047] Add the above-mentioned oily agent, hydrogenated base oil, phosphorus-containing anti-wear agent, and phenolic antioxidant into the enamel mixing kettle with agitator in sequence, stir at 60°C for 4 hours, then add oleic acid amide, demulsifier , and stirred at 40°C for 2 hours until the mixture wa...

Embodiment 3

[0050] (1) Oily agent: 450g of monoglyceride of oleate;

[0051] (2) Phosphorus-containing antiwear agent: 10g of phosphorothioate amine salt, 10g of triphenyl phosphate, 10g of phosphate amine salt;

[0052] (3) Oleic acid amide 300g;

[0053] (4) 5 g of demulsifier, the HLB value of the first type of nonionic polymer surfactant is 6, and the molecular weight is 5000, and the HLB value of the second type of nonionic polymer surfactant is 12, and the molecular weight is 2000. The mass ratio of the first type and the second type nonionic polymer surfactant is 1:5;

[0054] (5) Phenolic antioxidant: 5g of 2,6-di-tert-butylphenol;

[0055] (6) 210 g of 250N hydrogenated base oil;

[0056]Add the above-mentioned oily agent, hydrogenated base oil, phosphorus-containing anti-wear agent, and phenolic antioxidant into the enamel mixing kettle with agitator in sequence, stir at 70°C for 4 hours, then add oleic acid amide, demulsifier , and stirred at 50°C for 2 hours until the mixt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an aluminum rolling oil additive composition, the present invention is characterized in that the composition comprises the following components by mass percentage: (1) oiliness agent: 30 to 48%; (2) antiwear agent containing phosphorus: 3 to 15%; (3) oleamide: 26 to 35%; (4) de-emulsifier: 0.5 to 2.8%; (5) phenolic antioxidants: 0.1 to 0.5%; (6) hydrogenated base oil: the balance. The oiliness agent is monoolein and/or oleic acid; the antiwear agent containing phosphorus is one or more selected from amine sulfuric-phosphoric diester, phosphorothioate and its amine salt, phosphate ester and its amine salt; the de-emulsifier is a combination of two types non-ionic high-molecular surfactants. According to the invention, an antiabrasive agent oleamide and the phosphatide antiwear agent are combinated with aliphatic acid and fatty acid ester, which achieves the goal of reducing the friction coefficient and improving the annealing performance; and the application amount of the additive and the cost of aluminum rolling oil can be reduced.

Description

technical field [0001] The invention relates to an additive composition, in particular to an aluminum material rolling oil additive composition. Background technique [0002] Aluminum rolling oil is mainly composed of appropriate mineral base oil and modified compound additives. Because the oil film formed by the base oil and the metal surface only produce physical adsorption, the adsorption force is small, and the lubricity is poor, so it is necessary to add additives to the base oil on industrial rolled aluminum to improve the boundary lubrication ability of the oil film. Additives are polar compounds or polymers that can improve certain properties of oil products. It is one of the most economical and effective ways to improve the lubricating properties of mineral base oils. [0003] The main additives in aluminum oil are oily agents, which can physically adsorb long-chain fatty acids, alcohols, and esters with the metal surface. Due to their different polarity and perfor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C10M161/00C10N40/24C10N30/06
Inventor 丁峰甄国芬周增强刘想
Owner 石家庄新泰特种油有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap