A kind of production method and device of pasty zinc flake pigment

A production method and technology for zinc flakes, which are applied in the directions of fibrous filler, dyeing physical treatment, dyeing low molecular organic compound treatment, etc., to achieve the effect of smoothing the surface of zinc flakes, improving dispersibility, and uniform flaky degree.

Inactive Publication Date: 2011-12-14
BEIJING BGRIMM ZINC INDAL +1
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, most anti-corrosion coatings are mainly powdered zinc flake pigments, and the application of paste zinc flake pigments is still in its infancy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of production method and device of pasty zinc flake pigment
  • A kind of production method and device of pasty zinc flake pigment
  • A kind of production method and device of pasty zinc flake pigment

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0029] The technical solutions of the present invention will be further described below in conjunction with the accompanying drawings and through specific implementation methods.

[0030] figure 1 It is a structural schematic diagram of the production device of the pasty zinc flake pigment in the specific embodiment of the present invention. Such as figure 1 As shown, the production device includes a grinder 101 , a first solid-liquid separator 102 , a stirring tank 103 , a second solid-liquid separator 104 and a kneader 105 .

[0031] The grinding machine is used to grind the material containing spherical zinc powder, grinding modifier and grinding aid solvent prepared in proportion. The grinding machine is a stirring grinding machine or a drum grinding machine, and the grinding balls are stainless steel balls, alumina balls Or zirconia balls, the diameter of the grinding balls is 1 to 15 mm, preferably 3 to 7 mm, the weight ratio of grinding balls to spherical zinc powder ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production method and device for a pasty zinc flake pigment. Spherical zinc powder, a grinding modifier and a grinding aid solvent are compounded, the compounded material is put into a grinder for grinding, and the material obtained after grinding is ground. The slurry is sent to the solid-liquid separator for the initial solid-liquid separation to obtain the initial paste zinc flakes, put the initial paste zinc flakes into the mixing tank, add an organic solvent containing a surface modifier, and treat the initial paste zinc flakes surface For modification, send the surface-modified primary paste zinc flake slurry into a solid-liquid separator for solid-liquid separation again to obtain a secondary paste zinc flake, and send the secondary paste zinc flake and dispersant into the In the kneader, high-speed kneading is carried out to obtain pasty zinc flake pigments. By adopting the technical solution of the invention, it is possible to produce paste-like zinc flakes with high metal zinc content and good quality.

Description

technical field [0001] The invention relates to the technical field of production of flake metallic pigments, in particular to a production method and device for pasty zinc flake pigments. Background technique [0002] Zinc flake pigments are mainly used in the preparation of inorganic salt coatings, inorganic zinc-rich coatings, zinc-chromium anti-corrosion coating liquids, chromium-free zinc-aluminum anti-corrosion coating liquids, etc. less, dense coating, and good corrosion resistance, especially the zinc-chromium anti-corrosion coating solution prepared with zinc flake pigment as the main raw material, the salt spray corrosion resistance is obviously better than that of electro-galvanized and hot-dip galvanized, and Pollution is small, it is a high-tech that replaces traditional galvanizing, solves wastewater pollution and improves anti-corrosion performance, and is also a new green coating technology. However, at present, most anti-corrosion coatings are mainly powder...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09C1/62C09C3/04C09C3/10C09C3/08
Inventor 王爱平刘葵王彦军
Owner BEIJING BGRIMM ZINC INDAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com