Methods of Improving the Strength of Carbon Fiber

A carbon fiber and strength technology, which is applied in the fields of carbon fiber, fiber processing, textiles and papermaking, etc., can solve the problems of unsatisfactory "repair" efficiency and high cost, achieve ideal effect and efficiency, improve strength, and increase strength.

Inactive Publication Date: 2011-12-28
CHINA PETROLEUM & CHEM CORP
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is very gratifying that it is highly targeted for the repair of carbon fiber surface structure defects, but...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Methods of Improving the Strength of Carbon Fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～12

[0022] 1. Carbon fiber surface functionalization treatment

[0023] The self-produced unglued PAN-based carbon fiber was used for the test. The specification of the carbon fiber was: 3K, and the average diameter of the single fiber was 7.5 μm. The carbon fiber is soaked in the nitric acid aqueous solution of the required concentration, and the soaking temperature and bath ratio are controlled. After the set soaking time, the carbon fiber is washed with deionized water until the washing liquid is neutral. The soaking process conditions of each embodiment are shown in Table 1.

[0024] Table 1.

[0025] concentration of nitric acid solution

(mol / L)

bath ratio *

(weight ratio)

soaking temperature

(℃)

Soaking time

(hr)

Example 1

17.9

14∶1

121

2.1

Example 2

17.4

15∶1

122

2.5

Example 3

20.0

10∶1

100

0.5

Example 4

19.2

1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Login to view more

Abstract

A method for improving the strength of carbon fibers, comprising: 1) soaking the carbon fibers in an aqueous solution of nitric acid, washing the carbon fibers with deionized water until the washing liquid is neutral after soaking; 2) preparing a carbon nanotube dispersion into a spraying liquid, carbon The nanotubes are functionalized carbon nanotubes, which are obtained from hydroxylated carbon nanotubes, carboxylated carbon nanotubes or aminated carbon nanotubes. The dispersion liquid is a mixture of ionic liquid and water, and the ionic liquid is obtained from 1,3 -Dimethylimidazole p-toluenesulfonate, 1-butyl-3-methylimidazole p-toluenesulfonate, 1-octyl-3-methylimidazole chloride or 5-bromo-2-methyl-3 - One of the nitropyridines, the content of carbon nanotubes in the spraying liquid is 16-48g/L; 3) The spraying liquid is applied with positive static electricity of 10-40kV, and the carbon fiber tow is flattened and grounded to form a spraying liquid acceptor, and then passes through Electrostatic spraying sprays the spray liquid on the carbon fiber surface. The tensile strength of carbon fiber can be increased by more than 100%.

Description

technical field [0001] The invention relates to a method for improving the strength of carbon fibers, in particular to a method for coating carbon nanotubes on the surface of carbon fibers by an electrostatic spraying method to compensate for surface structural defects and increase the strength of carbon fibers. Background technique [0002] Carbon fiber can almost be considered as the non-metallic material with the highest specific strength and specific modulus so far, and has been widely used in transportation, sports equipment, construction and even aerospace fields. However, the strength and elastic modulus of existing carbon fiber products are actually far from the theoretical value. Taking the tensile strength as an example, it is generally only 3-5% of the theoretical value. The root cause of this phenomenon is that carbon fibers generally have structural defects, especially acrylonitrile-based carbon fibers, because their precursors are prepared by solution spinning,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M11/64D06M11/74D06M13/352D06M13/392D06M101/40
Inventor 程博闻季春晓康卫民陆正鸣黄翔宇严国良朱宗元李全祥刘礼华
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap