Copperplate board coating

A copper plate card and coating technology, which is applied in the direction of paper coating, coating, pigmented coating, etc., can solve the problems of steam and energy consumption, low coating solid content, and low coating amount, so as to save the use of slurry , Increase the solid content of the coating, and the effect of good printing effect

Active Publication Date: 2012-01-18
HAINAN JINHAI PULP & PAPER
View PDF5 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing paint formulations for copperplate cards have low solid content of the paint, which requires more steam and energy consumption during the drying process; in addition, the coating amount of the paint is relatively low, and a large amount of fiber is consumed, increasing the demand for wood

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Copperplate board coating
  • Copperplate board coating
  • Copperplate board coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0022] Coating formulations for copperplate cards are shown in Table 1-Table 4.

[0023] Table 1 Coating formula of copper plate card

[0024] Raw materials (parts by weight)

Embodiment one

Embodiment two

Embodiment three

Embodiment Four

Embodiment five

calcium carbonate

100

100

100

100

100

Sodium polyacrylate

0.2

0.3

0.5

0.2

0.3

Sodium carboxymethyl cellulose

0.2

0.15

0.1

0.1

0.15

caustic soda

0.5

0.5

0.6

0.6

0.5

potato starch

6

2

0

4

8

Styrene-butadiene latex

6

12

9

10

15

PAPU

0.2

0.5

0.5

0.5

0.5

Styrene-acrylic copolymer

0.2

0.2

0.2

0.2

0.2

sodium stearate

1

0.5

0.2

0.2

0.2

[0025] Table 2 Coating formula of c...

experiment example 1

[0034] ①Paint preparation and coating:

[0035] According to the paint formula in Example 1, each raw material was added in turn, and the paint was uniformly dispersed at a high speed, with a solid content of 68%; the coating speed was 600 m / min, and it was produced under the scraper coating method.

[0036] ② Coating sequence and paper weight:

[0037] Apply the base coat first, and then the top coat;

[0038] The paper gram weight is 200 grams.

[0039] ③Printing and paper properties:

[0040] The physical properties of the finished paper are excellent, and the printing color is gorgeous.

experiment example 2

[0042] ①Paint preparation and coating:

[0043] According to the coating formula of Example 2, each raw material was added in sequence, and the coating was uniformly dispersed at a high speed, and the solid content was 70%; the coating speed was 620 m / min, and it was produced under the scraper coating method.

[0044] ② Coating sequence and paper weight:

[0045] Apply the base coat first, and then the top coat;

[0046] The paper gram weight is 250 grams.

[0047] ③Printing and paper properties:

[0048] The physical properties of the finished paper are excellent, and the printing color is gorgeous.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides a new copperplate board coating. The copperplate board coating comprises the following raw materials, by weight, 5-100 parts of a pigment, 0-20 parts of starch, 0.2-5 parts of caustic soda, 0.05-3 parts of a rheology and water retaining agent, 1-30 parts of latex, 0.1-10 parts of a hydration resistant agent, 0.1-10 parts of a water repellent agent, 0.1-10 parts of alubricant and 0.1 to 8 parts of a dispersing agent. With the formula of the high solid content coating provided by the present invention, the gram weight of the base paper can be reduced in the context of production of the copper board with the same specification, such that the ratio of the base paper in the copper board is reduced, the slurry cost is decreased, the requirement of wood is reduced, the economic benefits and the social benefits are significantly improved; due to the reduction of the gram weight of the base paper, the speed can be improved during the base paper papermaking, the machine efficiency and the productivity can be improved; with the improvement of the coating amount, the paper covering and the smoothness are improved, such that the final product has a better printing effect.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a copper plate card coating. Background technique [0002] Copperplate cards are mainly used in brochures, book covers, children's books and other technical fields that require high printing color quality. Soft and elegant, excellent printing characteristics such as color reproduction. [0003] The quality of copperplate cards depends largely on the physical properties of the paint. Existing paint formulations for copperplate cards have low solid content of the paint, which requires more steam and energy consumption during the drying process; in addition, the coating amount of the paint is relatively low, and a large amount of fiber is consumed, increasing the demand for wood. Therefore, the optimization of the coating formula will help to improve the overall quality of the copper card. Contents of the invention [0004] The purpose of the invention is to overcome the d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H19/38D21H19/44D21H19/54D21H19/64D21H21/14D21H21/08
Inventor 陈汉彬徐智龙李娟孙丁丁
Owner HAINAN JINHAI PULP & PAPER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com