High-damping rubber composition and application thereof to vibration isolating supporting seat

A rubber composition and high damping technology, which is applied in the direction of earthquake resistance, building structure, building components, etc., can solve the problems of high price, high product cost, and difficult promotion, and achieve the goal of improving damping, high bonding strength, and reducing costs Effect

Inactive Publication Date: 2012-02-01
JIANGSU YANGZHOU HELI RUBBER PROD
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] High-damping vibration-isolation rubber bearing is a new type of vibration-isolation rubber bearing, which has the performance of ordinary vibration-isolation rubber and damper, but the damping ratio of ordinary natural rubber vibration-isolation rubber bearing is about 5%, while using Rubber with high damping characteristics, such as butyl rubber, has low bonding strength with the metal skeleton, which cannot meet the 50-year service life of the vibration-isolation rubber bearing
In addition, natural rubber resources are scarce and expensive, making the product cost extremely high and promotion difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Take: (main ingredient) 100 kg of first-grade smoked sheet glue;

[0016] (Vulcanizing agent) 1 kg of insoluble sulfur;

[0017] (Auxiliary cross-linking agent) 0.5 kg of N-cyclohexyl-2-benzothiazole sulfenamide, 1 kg of 2,2'-dithiodibenzothiazole, 2 kg of nano-zinc oxide, and 1 kg of stearic acid;

[0018] (Plasticizer) 6 kg of engine oil, 7 kg of naphthenic oil;

[0019] (High damping material) 7 kg of nano-scale flake mica powder, 15 kg of nano-scale graphite;

[0020] (Reinforcing agent) High wear-resistant carbon black (N330) 40 kg.

[0021] The above materials are masticated, mixed, sliced, formed, and vulcanized to obtain a shock-isolation rubber bearing with high damping properties.

Embodiment 2

[0023] Take: (main ingredient) 100 kg of first-grade smoked sheet glue;

[0024] (Vulcanizing agent) 1.5 kg of insoluble sulfur;

[0025] (Auxiliary cross-linking agent) 1 kg of N,N'-m-phenylene bismaleimide, 1 kg of N-cyclohexyl-2-benzothiazole sulfenamide, 2,2'-dithiodiphenyl 1 kg of thiazole, 5 kg of nano zinc oxide, 1 kg of stearic acid;

[0026] (plasticizer) engine oil 10 kg;

[0027] (High damping material) 8 kg of nano-scale mica powder, 18 kg of nano-scale graphite;

[0028] (Reinforcing agent) High wear-resistant carbon black (N330) 45 kg.

[0029] The above materials are masticated, mixed, sliced, formed, and vulcanized to obtain a shock-isolation rubber bearing with high damping properties.

Embodiment 3

[0031] Take: (main ingredient) 100 kg of first-grade smoked sheet glue;

[0032] (Vulcanizing agent) 1.5 kg of insoluble sulfur;

[0033] (Auxiliary cross-linking agent) 1 kg of N,N'-m-phenylene bismaleimide, N-cyclohexyl-2-benzothiazole sulfenamide and 2,2'-dithiodibenzothiazole 2.0 kg, 5 kg of nano zinc oxide, 1 kg of stearic acid;

[0034] (Plasticizer) 6 kg of engine oil, 7 kg of naphthenic oil;

[0035] (High damping material) 8 kg of nano-scale mica powder, 18 kg of nano-scale graphite;

[0036] (Reinforcing agent) 45 kg of high wear-resistant carbon black (N330), 10 kg of nano-scale high clay.

[0037] The above materials are masticated, mixed, sliced, formed, and vulcanized to obtain a shock-isolation rubber bearing with high damping properties.

[0038] Finally, it should be noted that the rubber composition of the present invention can also be applied to other shock-absorbing products.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-damping rubber composition and application thereof to a vibration isolating supporting seat, relating to improvement on a high-damping rubber formula and application thereof to a vibration isolating supporting seat. According to the invention, the intensity and high damping performance are ensured, high damping performance is achieved, framework bonding strength is high, and aging resistance is realized. The high-damping rubber composition comprises 100 parts of smoke sheet rubber, 1-2.5 parts of vulcanizing agent, 5-10 parts of crosslinking aid, 20-35 parts of high-damping additive, 10-15 parts of plasticizing agent and 40-50 parts of reinforcing agent. The composition is taken as a rubber overlay of the vibration isolating supporting seat. In the invention, the smoke sheet rubber is taken as a main body and the high-damping additive is used, so that a rubber material with high strength, high framework bonding strength, aging resistance and high damping performance can be prepared under the actions of the crosslinking aid, the vulcanizing agent, the reinforcing agent and the plasticizing agent. The high-damping rubber composition is particularly suitable to be applied to a shockproof vibration isolating supporting seat. Compared with the prior art, the invention has the advantages: the damping performance is enhanced while the strength and aging resistance of a product are ensured, and the cost is reduced greatly.

Description

technical field [0001] The invention relates to the improvement of high damping rubber formula and its application on shock-absorbing rubber bearings. Background technique [0002] High-damping vibration-isolation rubber bearing is a new type of vibration-isolation rubber bearing, which has the performance of ordinary vibration-isolation rubber and damper, but the damping ratio of ordinary natural rubber vibration-isolation rubber bearing is about 5%, while using Rubber with high damping characteristics, such as butyl rubber, has low bonding strength with the metal skeleton, which cannot meet the 50-year service life of the vibration-isolation rubber bearing. In addition, natural rubber resources are scarce and expensive, making the product cost extremely high and promotion difficult. Contents of the invention [0003] Aiming at the above problems, the present invention provides a high damping rubber composition with good damping performance, high bonding stre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08K13/02C08K3/34C08K3/04E01D19/04E04B1/36E04B1/98
Inventor 宋继良陈理想高俊郭华
Owner JIANGSU YANGZHOU HELI RUBBER PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap