Preparation method of plastic product and plastic product

A technology of plastic products and plastics, which is applied in the field of surface metallization of non-metallic materials, and can solve problems such as high energy requirements, poor adhesion between coatings and plastic substrates, and complex metallization processes on plastic surfaces.

Active Publication Date: 2012-04-11
BYD CO LTD
View PDF6 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention aims to solve the technical problems in the prior art that the plastic surface metallization proces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0019] The invention provides a kind of preparation method of plastic product, comprises the following steps:

[0020] 1) molding plastic matrix; described plastic matrix is ​​the thermoplastic or thermosetting plastic that contains electroless plating accelerator, and electroless plating accelerator is evenly distributed in thermoplastic or thermosetting plastic; Described electroless plating accelerator is Ni 2 o 3 、Co 2 o 3 , CuSiO 3 、CuC 2 o 4 , one or more of Cu / Fe / Mn or Cu / Fe / Al ternary co-sintered oxides, Cu / Fe / Al / Mn quaternary co-sintered oxides;

[0021] 2) Laser vaporizes the surface of the plastic substrate, exposing the electroless plating accelerator;

[0022] 3) Electroless copper plating or electroless nickel plating on the surface of the electroless plating promoter in step 2), continue to perform at least one electroless plating and / or electroplating, and form a metal layer on the surface of the plastic substrate.

[0023]The inventors of the present in...

Embodiment 1

[0052] (1) CuC 2 o 4 2H 2 O, vacuum drying to decrystallize water, ball milling until the D50 is below 1 μm, and drying; PP resin, CuC 2 o 4 , talcum powder and antioxidant 1010 are mixed with a high-speed mixer at a mass ratio of 100:15:10:0.2, and then extruded into pipes with a single-screw extruder (Nanjing Rubber and Plastic Machinery Factory), and the extrusion temperature is 180°C .

[0053] (2) Use an infrared laser (Tide, DPF-M12) to irradiate the outer surface of the entire pipe. The laser parameters are: wavelength 1064nm, scanning speed 1000mm / s, step size 9μm, delay 30μs, frequency 40KHz, power 3W, filling spacing 50μm; clean the surface of the pipe.

[0054] (3) immerse in the electroless copper plating solution for 3 hours to form a copper layer with a thickness of 10 μm, immerse in the electroless nickel plating solution for 10 minutes, and form a nickel layer with a thickness of 3 μm on the outside of the copper layer; electroless copper plating solution:...

Embodiment 2

[0057] Adopt the method identical with embodiment 1 to prepare the plastic product of the present embodiment, difference is:

[0058] In step (1), the CuSiO 3 Ball mill until the D50 is less than 2 μm, dry; PC resin, CuSiO 3 , antioxidant 168, and EVA wax are mixed in a mass ratio of 100:20:0.2:0.1, extruded, granulated, and then injection molded into an electrical housing;

[0059] In step (2), the infrared laser is used to print out the metal circuit pattern on the electrical appliance casing; after the laser gasification is completed, the electrical appliance casing is ultrasonically cleaned;

[0060] In step (3), the order of the electroless plating is: first electroless nickel plating for 10 minutes to form a 3 μm thick nickel layer, then electroless copper plating for 3 hours to form an 11 μm thick copper layer, and finally electroless nickel plating for 10 minutes to form a 3 μm thick nickel layer.

[0061] Through the above-mentioned steps, the plastic product used a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a plastic product. The preparation method comprises the following steps: 1) shaping a plastic substrate, wherein the plastic substrate contains a chemical plating accelerator, and the chemical plating accelerator is one or more of Ni2O3, Co2O3, CuSiO3, CuC2O4, Cu/Fe/Mn or Cu/Fe/Al ternary co-sintering oxide and Cu/Fe/Al/Mn quaternary co-sintering oxide; 2) gasifying the surface of the plastic substrate by use of laser, and exposing the chemical plating accelerator; and 3) chemically plating copper or chemically plating nickel, and further carrying out chemical plating and/or electroplating at least once, so as to form a metal layer on the surface of the plastic substrate. The preparation method provided by the invention has the advantages ofsimple process, low energy requirement and low cost; and in addition, the chemical plating accelerator is distributed in the plastic substrate, thus the bonding force of a plating layer formed by chemical plating and the plastic substrate is extremely high. The invention further discloses a plastic product prepared by the method.

Description

[0001] This application is a divisional application with the applicant being BYD Co., Ltd., the filing date is December 30, 2009, the application number is 200910238957.9, and the invention title is "a preparation method of a plastic product and a plastic product". technical field [0002] The invention belongs to the field of surface metallization of non-metallic materials, and in particular relates to a preparation method of a plastic product and a plastic product. Background technique [0003] A metal layer is formed on the surface of the plastic, which is used as a channel for electromagnetic signal transmission, and is widely used in automobiles, industries, computers, communications and other fields. The selective formation of a metal layer on the plastic surface is a core link in the manufacture of such plastic products. There are many methods for plastic surface metallization production lines. In the prior art, metal nuclei are first formed on the surface of the plas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C18/20C23C18/31C23C18/32C23C18/38C08K3/08
Inventor 宫清周良苗伟峰张雄
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap