Carlin-type gold mine tailing sintered wall material and preparation method thereof

A technology for wall materials and gold tailings, which is applied in the field of Karin-type gold tailings sintered wall materials and its preparation, can solve problems such as the difficulty in utilizing Karin-type gold tailings, and achieve low production costs and high slag consumption Big, Intensive Satisfying Effect

Inactive Publication Date: 2013-04-10
中国建材检验认证集团贵州有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to overcome the defect that the existing Karin-type gold tailings are difficult to utilize, and to provide a Karin-type gold tailings sintered wall material and its preparation method, which can utilize Karin-type gold tailings in large quantities, Up to 90% tailings can be mixed in the sintered wall material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Example 1: Take 70kg of Karin-type gold tailings and 30kg of shale, and pass them together on a pair of rollers with a spacing of 2mm, stir with two shafts, adjust the moisture content to 18-23%, age for 24 hours, and extrude to form a solid embryo body. After drying, place the green body in a tunnel kiln and sinter at 1050°C for 1 hour to obtain a Karin-type gold tailings sintered brick with a compressive strength of 35.8Mpa.

Embodiment 2

[0015] Example 2: Take 60kg of Karin-type gold tailings and 40kg of shale, put them together on the pair of rollers with a spacing of 2mm, stir with two shafts, adjust the moisture content to 18-23%, age for 48 hours, and extrude to a hollow rate of 35% The green body was dried naturally, and then the green body was placed in a wheel kiln and sintered at 1000°C for 1 hour to obtain a Karin-type gold tailings sintered brick with a compressive strength of 23.8Mpa.

Embodiment 3

[0016] Example 3: Take 70kg of Karin-type gold tailings and 30kg of coal gangue, and pass them together on a pair of rollers with a spacing of 2mm, stir with two shafts, adjust the moisture content to 18-23%, age for 36 hours, and extrude to form a solid embryo body. After drying in a tunnel kiln, the green body was sintered at 950°C for 1 hour to obtain a Karin-type gold tailings sintered brick with a compressive strength of 17.2Mpa.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a Carlin-type gold mine tailing sintered wall material and a preparation method thereof. The wall material is prepared by sintering the following components, by weight: 10-90 parts of Carlin-type gold mine tailing, 90-10 parts of auxiliary materials, and 18-30 parts of water. The auxiliary materials are one or more than two selected from clay, shale and gangue. Compared toprior art, according to the invention, the sintered wall material is prepared by using a main material of Carlin-type gold mine tailing. The method is advantaged in high slag take, low production cost, good product property, and the like. The strength of the wall material satisfies requirements. The preparation method provided by the invention is compatible with that of traditional sintered bricks, and can be popularized in traditional sintered brick factories.

Description

technical field [0001] The invention relates to the technical field of wall materials, in particular to a Karin-type gold tailings sintered wall material and a preparation method thereof. Background technique [0002] my country is a populous country, which consumes a lot of building materials every year. The sintered wall material has the advantages of good durability, convenient material acquisition, simple process, and cheap price, making it a widely used building material. In the process of producing clay sintered wall materials, a large amount of clay resources are consumed and farmland is destroyed. Therefore, my country needs to use a large number of various waste residues to replace clay to produce sintered wall materials. [0003] Gold mine tailings is a kind of waste residue from the gold mining and dressing industry, and it is also the second largest metal tailings discharged in my country. In my country, the utilization rate of gold tailings is very low, an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B30/00C04B18/12
CPCY02W30/91
Inventor 彭建军贺深阳万军梁嘉琪王勇彭能华刘恒波高遇事
Owner 中国建材检验认证集团贵州有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap