Hydrogenation catalyst carrier and preparation method thereof

A catalyst carrier and hydrogenation catalyst technology, which is applied in catalyst carriers, chemical instruments and methods, physical/chemical process catalysts, etc., can solve the problems of insufficient nitrogen resistance of medium-oil catalysts, and achieve good nitrogen resistance and good nitrogen resistance. Ability, the effect of the appropriate amount of acid

Active Publication Date: 2013-10-09
CHINA PETROLEUM & CHEM CORP +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Aiming at the deficiencies of the prior art and the problem of insufficient nitrogen resistance of medium-oil catalysts, the present invention prepares a hydrogenation catalyst carrier, wherein the amorphous silica-alumina as the acidic component is first subjected to hydrothermal treatment, and the catalyst carrier of the present invention has Larger pore volume and specific surface area, appropriate acid content, and good nitrogen resistance. The catalyst prepared by the carrier of the present invention is suitable for the hydroprocessing of heavier and lower-quality vacuum distillate oils and producing more middle distillate oils. process or hydrocracking process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hydrogenation catalyst carrier and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The preparation method of catalyst carrier of the present invention is as follows:

[0026] (1) Hydrothermal treatment of amorphous silica-alumina dry rubber powder

[0027] The physical and chemical properties of the amorphous silica-alumina colloidal powder used in the catalyst carrier of the present invention before hydrothermal treatment are: the dry weight is 50% to 80%, and the surface area is 300 to 600m 2 / g, the pore volume is 0.4~1.2cm 3 / g. The amount of infrared acid (determined by pyridine infrared adsorption spectrometry) is between 0.4-1.5 mmol / g, which can be commercially available amorphous silica-alumina dry rubber powder, or can be prepared according to conventional methods in this field.

[0028] The hydrothermal treatment is carried out with saturated steam, the treatment pressure is 0.05-0.3MPa, the treatment temperature is 450-750°C, and the treatment time is 0.5-5h.

[0029] The properties of amorphous silicon-alumina after hydrothermal treatme...

Embodiment 1

[0037] Get amorphous silica-alumina dry rubber powder 1000g (commercially available commodity, dry basis is 70.13%, specific surface area is 458m 2 / g, the pore volume is 0.75cm 3 / g, the silicon oxide weight content is 45%, the infrared acid content is 1.0mmol / g), the hydrothermal treatment temperature is 500°C, the treatment pressure is 0.2MPa, and the treatment time is 2h. The obtained code is GL-1, and the properties of the product are shown in Table 1.

Embodiment 2

[0039] Take 1000 g of amorphous silica-alumina dry rubber powder (same as in Example 1), the hydrothermal treatment temperature is 600° C., the treatment pressure is 0.2 MPa, and the treatment time is 2 hours. The obtained code is GL-2, and the properties of the product are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a hydrogenation catalyst carrier which comprises, by weight, 0 to 40% of a molecular sieve, 20 to 75% of amorphous silica-alumina and 5 to 75% of alumina. The hydrogenation catalyst carrier has the following properties: a specific surface area is 200 m<2> / g to 500 m<2> / g; a pore volume is 0.40 cm<3> / g to 0.80 cm<3> / g. A preparation method for the hydrogenation catalyst carrier comprises the following steps: carrying out hydrothermal treatment on amorphous silica-alumina dry glue powder; weighing the above-mentioned components of the catalyst carrier in desired proportion; carrying out mixing and milling, molding, drying and activation on the components so as to obtain the catalyst carrier. Compared to conventional hydrogenation catalyst carriers, the catalyst carrier provided in the invention has the following advantages: the catalyst carrier has a greater pore volume, a greater specific surface area, a proper amount of acid and good nitrogen resistance; a catalyst prepared from the catalyst carrier is applicable to hydrotreatment of vacuum distillates which are heavier and poorer but can produce more middle distillates.

Description

technical field [0001] The invention relates to a hydrogenation catalyst carrier and a preparation method thereof, in particular to a hydrocracking catalyst carrier capable of treating inferior feedstock with high nitrogen resistance and a preparation method thereof. technical background [0002] In recent years, hydrocracking capacity has continued to increase worldwide, with the fastest growth in the Asia-Pacific region. The continuous growth of my country's economy has also strongly driven the domestic refined oil market to continue to rise. At present, the processing capacity of my country's existing hydrocracking units has exceeded 40.0Mt / a. However, due to the deterioration of crude oil quality year by year, a substantial increase in imported high-sulfur crude oil, and in order to improve economic benefits, refineries have generally adopted crude oil vacuum deep-drawing technology, which has increased the dry point of vacuum distillate oil from 520°C to 520°C. At arou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J32/00
Inventor 刘昶王凤来杜艳泽关明华
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com