Production method of fiber cement-stone compound plate and product thereof

A fiber cement, production method technology, applied in covering/lining, building, building structure, etc., to achieve the effect of easy laying and installation, broad application prospects, and not easy to deform

Inactive Publication Date: 2013-08-21
梅志江
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This connection method is one of the composite methods, and there is no new technical solution for the method of modification and enhancement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of fiber cement-stone compound plate and product thereof
  • Production method of fiber cement-stone compound plate and product thereof
  • Production method of fiber cement-stone compound plate and product thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0036] Stone composite panel of the present invention, as figure 1 As shown, it is composed of a stone panel 1 and a base plate 3 including cement components, through a bonding layer 2 including viscosity-modified cement as a bonding material, and then pressed and composited. Composite panels. The stone constituting the panel 1 can be granite, marble or marble decorative board, its surface 11 is polished, and its back side 12 will be roughened, or several lengths and widths are engraved on the back side 12 and are (0.5~0.8 )mm groove line.

[0037] At the same time, prepare the mixed cementitious material that constitutes the bonding layer 2, including high-strength and fast-hardening 2.5Mpa cement, as the main material, such as sulphoaluminate cement, and add a polyacrylate aqueous solution with a weight of 40% to 50% of the cement. , the concentration of the aqueous solution is 2% to 5%, and it is stirred into a slurry, so that the viscosity-modified cement slurry can incr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a fiber cement-stone compound plate and a product thereof. The product comprises a panel 1 and a cement-containing base material plate 3, and the compound plate is formed by bonding through a bonding layer 2 constituted by polyacrylic ester-modified cement slurry and performing pressure forming, wherein the preparation of the base material plate 3 is as follows: sequentially injecting materials of various layers into a mold frame for respectively forming a bottom layer, a lower interlayer, a middle layer, an upper interlayer and a surface layer, wherein the bottom layer and the surface layer are made of modified cement, the upper and the lower interlayers are of glass fiber nets, the components of the middle layer comprise cement, light ceramsite, fiber and polyacrylic ester emulsion or the middle layer is made of foam cement mortar with gas content of 20%-50%; and the thickness of the base material plate 3 is 12mm-16mm, and the base material plate is further bonded with the panel made of stone for forming the compound plate. The product is high in bending strength and flexural strength, low in thermal expansion coefficient and hygroscopic expansion coefficient, heat-insulating, weather-resistant, simple and convenient to mount and suitable for various floors.

Description

technical field [0001] The invention relates to a stone composite board, in particular to a production method and a product of a composite board made of cement and stone. Background technique [0002] Stone, especially its board, in order to maintain its rigidity and high strength and improve its bending resistance, the way of stone composite board is often used. But there are many types and methods of compounding. Combining with organic materials, the performance is improved a lot, but the cost is increased; using inorganic cementitious materials, especially cement, to modify the cost is greatly reduced, but the performance is difficult to ideal. The cost of using metal to strengthen, such as aluminum honeycomb panel-stone composite panel, is still higher than that of inorganic composite materials. When choosing composite materials, the thermal expansion coefficient and the similarity of the wet expansion coefficient of the two should also be considered. Although reports...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/077E04F13/076
Inventor 梅志江
Owner 梅志江
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap