60-degree natural rubber and production process thereof

A technology of natural rubber and production process, which is applied in the field of 60-degree natural rubber and its production process, and can solve the problem of high production cost

Inactive Publication Date: 2012-06-20
北京市长城机床附件有限责任公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0032] The natural rubber prepared in the prior art has certain defects in aging resistance, elongation at break, rebound value, low temperature resistance, bearing compression, natural frequency, etc., and the production cost of a small amount of products with better performance is relatively low. high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 60-degree natural rubber and production process thereof
  • 60-degree natural rubber and production process thereof
  • 60-degree natural rubber and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0108] Prepare 60 degree natural rubber of the present invention according to the following steps:

[0109] (1) Rubber drying: put 56.1g of natural raw rubber in an oven at 60°C, and bake the rubber for 4 hours;

[0110] (2) Gum breaking: The natural raw rubber after drying is immediately broken. The roller distance is 0.5mm when the glue is broken;

[0111] (3) First mastication: Divide the natural raw rubber into 3 equal parts, each weighing 18.7 kg. The roller distance is 0.5mm, and it is required to roll and turn 90° for the next plasticizing. Roll over 12 times continuously;

[0112] (4) After parking for 4 hours, carry out the second mastication. The second plasticizing roller distance is adjusted to 0.5mm, coiled and turned 90 ° for the next plasticizing, and the rollers are passed continuously for 12 times. After parking for 4 hours, enter the mixing process;

[0113] (5) Mixing: put the masticated raw rubber into the open mill, and wrap it with rolls. After wrap...

Embodiment 2

[0117] Prepare 60 degree natural rubber of the present invention according to the following steps:

[0118] (1) Rubber drying: put 63.2g of natural raw rubber at 70°C, and bake the rubber for 3 hours;

[0119] (2) Gum breaking: The natural raw rubber after drying is immediately broken. The roller distance is 0.3mm when the rubber is broken;

[0120] (3) First mastication: Divide the natural raw rubber into 4 equal parts, each weighing about 15.8kg. The roller distance is 0.3mm, and it is required to roll and turn 90° for the next plasticizing. Roll over 18 times continuously;

[0121] (4) After parking for 5 hours, carry out the second mastication. The second plasticizing roll distance is adjusted to 0.3mm, coiled and turned 90° for the next plasticizing, and the rollers are passed continuously for 18 times. After parking for 5 hours, enter the mixing process;

[0122] (5) Mixing: put the masticated raw rubber into the open mill, and wrap it with rolls. After wrapping th...

Embodiment 3

[0124] Prepare 60 degree natural rubber of the present invention according to the following steps:

[0125] (1) Rubber drying: put 52.85g of natural raw rubber at 30°C, and bake the rubber for 5 hours;

[0126] (2) Gum breaking: The natural raw rubber after drying is immediately broken. The roller distance is 0.9mm when the glue is broken;

[0127] (3) First mastication: Divide the raw natural rubber into 3 equal parts, each weighing 17.62 kg. The roller distance is 0.9mm, and it is required to roll and turn 90° for the next plasticizing. Roll over 10 times continuously;

[0128] (4) After parking for 4 hours, carry out the second mastication. The second plasticizing roller distance is adjusted to 0.9mm, coiled and turned 90 ° for the next plasticizing, and the rollers are passed continuously for 10 times. After parking for 4 hours, enter the mixing process;

[0129] (5) Mixing: Put the masticated raw rubber into the open mill to make it covered with rolls. After complet...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a 60-degree natural rubber and a production process of the 60-degree natural rubber. The raw materials of the 60-degree natural rubber comprise 48%-65% of raw natural rubber, 1%-2.5% of vulcanizator, 5%-21% of high wear-resistant furnace black, 8%-28% of spraying carbon black, 5.5%-17% of active agent, 0.1%-0.6% of accelerator, 0.55%-3.2% of anti-aging agent and 0.5%-3% of plasticizer, and the natural rubber is produced by processes of plasifying and mixing. The 60-degree natural rubber has the advantages of good ageing resistance, good elongation at rupture, excellent wear resistance, good rebound value, good load compression amount and natural frequency; meanwhile, the rubber is low in production cost.

Description

technical field [0001] The present invention relates to a kind of natural rubber and its production process, specifically, the present invention relates to a kind of 60 degree natural rubber and its production process. Background technique [0002] Natural rubber is a natural polymer compound with polyisoprene as the main component, and its molecular formula is (C 5 h 8 )n, 91% to 94% of its components are rubber hydrocarbons (polyisoprene), and the rest are non-rubber substances such as proteins, fatty acids, ash, and sugars. Natural rubber is the most widely used general-purpose rubber. [0003] Natural rubber has high elasticity at room temperature, slightly plastic, has very good mechanical strength, low hysteresis loss, and low heat generation during multiple deformations, so its flex resistance is also very good, and because it is non-polar Rubber, so the electrical insulation performance is good. [0004] Because of unsaturated double bonds, natural rubber is a su...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/00C08K13/02C08K3/04C08K3/06C08K5/09C08K5/47C08K5/18
Inventor 方学金王燕生马薇薇
Owner 北京市长城机床附件有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com