Pressure casting process for lock

A casting process and pressure technology, applied in the field of lock pressure casting process, can solve the problems of difficult to achieve mechanization and automation, low precision, strength, hardness, increase processing equipment and working hours, etc., to improve metal utilization, good product quality, The effect of reducing processing equipment and man-hours

Inactive Publication Date: 2012-07-04
南通顶点科技服务有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, die-casting alloys are no longer limited to non-ferrous metals such as zinc, aluminum, magnesium and copper, and are gradually expanded to be used for die-casting cast iron and steel castings. However, the traditional lock die-casting method has disadvantages: poor product quality, precision, strength, hardness Low, large processing volume, increased a large number of processing equipment and man-hours, low production efficiency, difficult to achieve mechanization and automation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] In order to deepen the understanding of the present invention, the present invention will be further described below in conjunction with examples, which are only used to explain the present invention and do not constitute a limitation to the protection scope of the present invention.

[0019] A specific embodiment of the locking pressure casting process of the present invention comprises the following steps:

[0020] A. Install the mold;

[0021] B. Preheat the mold, the preheating temperature is 180-220°C;

[0022] C. Clean the mold;

[0023] D. Spray paint on the mold;

[0024] E. Place the mold on the mold clamping device for mold clamping;

[0025] F. Select the injection specific pressure and filling speed, the fast pressure range is 250-, the slow pressure range is 0-250mm, inject liquid metal into the cavity and fill the cavity;

[0026] The selection of injection specific pressure should be determined according to the structural characteristics of different ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a pressure casting process for a lock, which includes the steps: mounting a die; preheating the die; cleaning the die; spraying coatings on the die; placing the die on a die assembly device for die assembly; selecting injection pressure and filling speed; injecting liquid metal into a cavity and leading the cavity to be filled with the liquid metal; continuing injection under the action of an injection plunger until the liquid metal filled to a flow gate of the cavity is completely solidified; taking out a casting by opening the cavity after maintaining pressure; and cleaning the casting. The pressure casting process has the advantages that fine product quality is ensured, precision, strength and hardness are high, machining amount is small, large quantities of machining equipment and machining time are reduced, metal utilization rate is increased, both assembly time and the metal are saved, production efficiency is high, and mechanization and automation are easy to realize.

Description

Technical field: [0001] The invention relates to a lock pressure casting process. Background technique: [0002] Lock pressure casting is one of the most advanced metal forming methods. It is an effective way to achieve less chips and no chips. It is widely used and developed rapidly. At present, die-casting alloys are no longer limited to non-ferrous metals such as zinc, aluminum, magnesium and copper, and are gradually expanded to be used for die-casting cast iron and steel castings. However, the traditional lock die-casting method has disadvantages: poor product quality, precision, strength, hardness Low, large processing volume, increased a large number of processing equipment and man-hours, low production efficiency, difficult to achieve mechanization and automation. Invention content: [0003] The purpose of the present invention is to overcome the above disadvantages and provide a lock pressure casting process that ensures good product quality, high production effi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D17/00
Inventor 顾丽宋宏彬
Owner 南通顶点科技服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap