High-strength durable type rotational-molded automobile urea box

A urea tank, durable technology, applied in the field of automotive urea tank materials, can solve the problems of not being able to adapt to the conditions of urea tank molding and use, poor long-term aging resistance of polyethylene, poor UV resistance, etc., to achieve long-term aging Good performance and light, simple and easy preparation method, and prolonged service life

Inactive Publication Date: 2012-07-04
FAW GROUP
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the material of automotive rotomoulding urea tank is linear low-density polyethylene, which cannot meet the requirements of the molding and use conditions of the urea tank.
The problem of environmental stress cracking resistance of polyethylene materials is a common problem; the use temperature of a single polyethylene is at 80°C for a long time, in order to produce deformation and collapse, if it is under pressure, the situation will Worse; the unmodified sin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength durable type rotational-molded automobile urea box
  • High-strength durable type rotational-molded automobile urea box

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0013] The present invention makes the required material of urea tank masterbatch and consists of:

[0014] Linear Low Density Polyethylene (LLDPE) 20 High Density Polyethylene (HDPE) 30

[0015] POE 50 Calcium stearate 1~2 Antioxidant 1010 2~3

[0016] Antioxidant 168 4~6 Antistatic agent---------Hydroxyethylalkylamine 3-8;

[0017] The parts by weight of the materials needed to make the urea tank consist of:

[0018] Masterbatch 8-10 Linear low-density polyethylene 90-92. The masterbatch and LLDPE are mixed in this ratio, avoiding the re-pelletization of all the materials in the twin-screw extruder, causing unnecessary degradation of the material.

[0019] Weigh linear low-density polyethylene, high-density polyethylene, POE, calcium stearate, antioxidant 1010, antioxidant 168, negative ion powder and antistatic agent according to the proportion, and the antistatic agent adopts hydroxyethyl alkanes base amine; after weighing, put linear low-density polyethylene, high-den...

Embodiment 1

[0021] Linear Low Density Polyethylene (LLDPE) 20 High Density Polyethylene (HDPE) 30

[0022] POE 50 Calcium stearate 1 Antioxidant 1010 2

[0023] Antioxidant 168 4 Antistatic agent---------hydroxyethyl alkylamine 3;

[0024] The parts by weight of the materials needed to make the urea tank consist of:

[0025] Masterbatch 10 Linear Low Density Polyethylene 90. The masterbatch and LLDPE are mixed in this ratio, avoiding the re-pelletization of all the materials in the twin-screw extruder, causing unnecessary degradation of the material.

[0026] Weigh linear low-density polyethylene, high-density polyethylene, POE, calcium stearate, antioxidant 1010, antioxidant 168, negative ion powder and antistatic agent according to the proportion, and the antistatic agent adopts hydroxyethyl alkanes base amine; after weighing, put linear low-density polyethylene, high-density polyethylene, POE, calcium stearate, antioxidant 1010, antioxidant 168, negative ion powder and antistatic ag...

Embodiment 2

[0028] Linear Low Density Polyethylene (LLDPE) 20 High Density Polyethylene (HDPE) 30

[0029] POE 50 Calcium stearate 1 Antioxidant 1010 2

[0030] Antioxidant 168 4 Antistatic agent---------hydroxyethyl alkylamine 3;

[0031] The parts by weight of the materials needed to make the urea tank consist of:

[0032] Masterbatch 9 Linear Low Density Polyethylene 91. The masterbatch and LLDPE are mixed in this ratio, avoiding the re-pelletization of all the materials in the twin-screw extruder, causing unnecessary degradation of the material.

[0033] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melt indexaaaaaaaaaa
Densityaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-strength durable type rotational-molded automobile urea box, belongs to the field of chemical industry, and relates to a material for an automobile urea box. The invention aims at solving the durability problem of the high-strength durable type rotational-molded automobile urea box by changing the urea box material. The urea box master batch is prepared from the following materials in parts by weight: linear low-density polyethylene, high-density polyethylene, POE (Polyoxyethylene), calcium stearate, antioxidant 1010, antioxidant 168, and ethoxyl alkylamine serving as an antistatic agent. The urea box is prepared from the following materials in parts by weight: the master batch and linear low-density polyethylene. According to the invention, the rotational-molded urea box material is advanced in formula and strong in popularization property, and solves the problem that the urea box material has poor environmental stress resistance; the urea box material satisfies the rotational molding processing process requirements; the service life of the manufactured automobile urea box is prolonged by 30%, and the manufactured automobile urea box is applicable to use environments in high-temperature and cold areas; and the preparation method is simple and feasible, and easy for mass production.

Description

technical field [0001] The invention belongs to the field of chemical industry and relates to a material for an automobile urea tank. Background technique [0002] At present, the material of urea tank for automotive rotomolding is linear low density polyethylene, which cannot meet the requirements of forming and using the urea tank. The problem of environmental stress cracking resistance of polyethylene materials is a common problem; the use temperature of a single polyethylene is at 80°C for a long time, in order to produce deformation and collapse, if it is under pressure, the situation will Worse; the unmodified single linear low-density polyethylene has poor long-term aging resistance, and it will turn yellow or even powder after a long time, especially the ability to resist ultraviolet rays is worse; the melting point of linear polyethylene is low. It is also very difficult to modify the plastic molding characteristics. It is difficult to control the melting point of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L23/08C08K5/098C08K5/17
Inventor 杨彬
Owner FAW GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka