Preparation method of high solid content epoxy modified acrylic resin emulsion
An acrylic resin, epoxy modification technology, applied in the direction of coating, can solve the problem of high solid content epoxy modified acrylic resin emulsion and other problems, achieve broad industrial application prospects, reduce energy consumption, save brushing effect of time
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0023] Example 1
[0024] (1) 179g monomer (accounting for total weight 20%) is added dropwise in the colloidal solution that is made up of emulsifier (8.79g), pH regulator (0.88g) and deionized water (840g), high-speed stirring (stirring speed (1500 rev / min) after dispersing evenly, start to heat up to 80±5°C, pass protective gas in the system, remove oxygen, then add initiator (0.88g) into the system, initiate the system to start polymerization, react for 20 minutes, Obtain nuclear seed microemulsion;
[0025] (2) Put the epoxy resin (E44, 148g) into the mixed monomer (200g), add 0.88g of emulsifier, and use a stirring speed of 500 rpm to fully dissolve it, then slowly add the remaining 500g of mixed monomer monomer, stirred for 10 minutes to obtain a pre-emulsion;
[0026] (3) at the temperature of reaction of 85 ± 5 ℃, the pre-emulsion and initiator (1.8g) obtained by step 2 are slowly dripped respectively in the nuclear seed microemulsion obtained by step 1, and the sti...
Example
[0028] Comparative example 1
[0029] (1) Add epoxy resin (E44, 148g) to 379g of monomers, stir at a stirring speed of 500 rpm until uniformly dispersed, then add emulsifier (8.79g), pH regulator (0.88g) and remove Ionized water (840g), high-speed stirring (stirring speed 1500 rev / min) after dispersing evenly, start to heat up to 80±5°C, pass protective gas in the system to remove oxygen, and then add the initiator (0.88g) into the system In the process, the initiation system starts to polymerize, reacts for 20 minutes, and obtains the nuclear seed microemulsion;
[0030] (2) Add 0.88g of emulsifier to the remaining 500g of homogeneously mixed monomers, and stir at a stirring speed of 500 rpm for 10 minutes to obtain a pre-emulsion;
[0031] (3) at the temperature of reaction of 85 ± 5 ℃, the pre-emulsion and initiator (1.8g) obtained by step 2 are slowly dripped respectively in the nuclear seed microemulsion obtained by step 1, and the stirring speed is at 200 rpm, 3 hours ...
Example Embodiment
[0033] Example 2
[0034] (1) 263.7g monomer (accounting for total weight 30%) is added dropwise in the colloidal solution that is made up of emulsifier (17.58g), pH regulator (0.88g) and deionized water (840g), high-speed stirring (stirring After the speed is 1700 rev / min), the temperature starts to rise to 80±5°C, and the protective gas is passed through the system to remove oxygen, and then the initiator (0.88g) is added to the system, and the initiation system starts to polymerize, and the reaction is 30 minutes , to obtain nuclear seed microemulsion;
[0035](2) Put the epoxy resin (E44, 148g) into the mixed monomer (200g), add 0.88g of emulsifier, and use a stirring speed of 500 rpm to fully dissolve it, then slowly add the remaining 415.3g and mix well monomer, stirred for 20 minutes to obtain a pre-emulsion;
[0036] (3) at the reaction temperature of 85 ± 5 ℃, the pre-emulsion and initiator (1.8g) that step 2 obtains are slowly dripped respectively in the nuclear se...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology