EVA (ethylene vinyl acetate) packaging adhesive film for solar photovoltaic modules and preparation method thereof

A solar photovoltaic and packaging film technology, applied in photovoltaic power generation, adhesives, electrical components, etc., can solve the problems of low production efficiency, high production energy consumption, and large time consumption, and achieve improved production efficiency and excellent light transmission. The effect of stable performance and storage performance

Inactive Publication Date: 2012-07-25
SUN YAT SEN UNIV +1
View PDF3 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the curing temperature of EVA packaging film for solar photovoltaic modules is generally 140-145 ℃, the time is 20-30 minutes, and the degree of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1

[0029] The EVA packaging film contains the following components: 100 parts of ethylene-vinyl acetate copolymer; 0.8 parts of tert-amyl peroxide-2-ethylhexyl carbonate; 0.1 parts of tris(2,4 di-tert-butylphenyl) phosphite Parts; 0.5 parts of polysuccinic acid (4-hydroxy-2,2,6,6-tetramethyl-1-piperidine ethanol) ester. When the lamination temperature of the solar photovoltaic module is 130 ℃ and the lamination time is 12 minutes, the curing rate of the EVA encapsulating film can reach more than 80%.

Example Embodiment

[0030] Example 2

[0031] The EVA packaging film contains the following components: 100 parts of ethylene-vinyl acetate copolymer; 1.5 parts of tert-amyl peroxide-2-ethylhexyl carbonate; 3 parts of dibenzoyl peroxide; 4,4'-thio 0.2 part of bis(6-tert-butyl-3-methylphenol); 0.4 part of bis(1,2,2,6,6-pentamethylpiperidinol) sebacate. When the lamination temperature of the solar photovoltaic module is 130°C and the lamination time is 12 minutes, the curing rate of the EVA encapsulating film can reach more than 80%.

Example Embodiment

[0032] Example 3

[0033] The EVA packaging film contains the following components: 100 parts of ethylene-vinyl acetate copolymer; 1.0 part of tert-amyl peroxide-2-ethylhexyl carbonate; 3 parts of tert-butyl peroxide-2-ethylhexyl carbonate; four [β-(3',5'-Di-tert-butyl-4'-hydroxyphenyl) propionic acid] 0.2 parts of pentaerythritol ester; polysuccinic acid (4-hydroxy-2,2,6,6-tetramethyl -1-piperidine ethanol) ester 0.3 parts. When the lamination temperature of the solar photovoltaic module is 125℃ and the lamination time is 15 minutes, the curing rate of the EVA encapsulating film can reach more than 80%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an EVA (ethylene vinyl acetate) packaging adhesive film for solar photovoltaic modules and a preparation method thereof. The EVA packaging adhesive film consists of the following components in parts by weight: (1) 100 parts of ethylene vinyl acetate copolymer; (2) 0.5 to 5 parts of compound peroxide crosslinking agent; (3) 0.5 to 3 parts of silane coupling agent; (4) 0.1 to 0.5 parts of antioxidant; (5) 0.1 to 0.5 parts of light stabilizer. The ultrafast curing type EVA packaging adhesive film for the solar photovoltaic modules has the advantages that the curing temperature of the adhesive film is low, the curing time is short, the production efficiency of the solar modules can be effectively increased, energy consumption in production can be effectively reduced, and moreover, the adhesive film has excellent light transmission, anti-aging property and storability.

Description

technical field [0001] The invention relates to an EVA encapsulating adhesive film for solar photovoltaic components and a preparation method thereof. Background technique [0002] Ethylene Vinyl Acetate (EVA) is a copolymer of ethylene and vinyl acetate. The introduction of vinyl acetate structural units endows EVA resin with excellent flexibility; in addition, EVA resin has the advantages of high light transmittance, high bonding strength, good processing adaptability, and low price, so it is selected as a solar photovoltaic cell module. Adhesives for lamination packaging. However, EVA is a thermoplastic resin with low elasticity. Its heat resistance, solvent resistance, and cohesive strength are not good enough. It becomes soft and stretched when heated in the sun, and shrinks and hardens in severe cold weather. It is not suitable for direct use in solar cell packaging. , it is necessary to improve its deficiencies through cross-linking and curing. On the other hand, w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J7/02C09J123/08C09J131/04C09J11/06H01L31/048
CPCY02E10/50
Inventor 阮文红薛涵与章明秋容敏智余鹏
Owner SUN YAT SEN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap