A butterfly optical cable and production process technology, applied in the direction of fiber mechanical structure, etc., can solve the problems of low production speed and high use cost, and achieve the effect of high production speed, low use cost and high cost performance.

Inactive Publication Date: 2012-07-25
南通科鼎复合材料科技有限公司
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process must be completed by heating in the mold, so the production speed is low, only about 5 meters per minute
KFRP surface coating requires a special plastic coating production line for plastic coating production, and the cost of use is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reinforcement for thermoplastic GFRP (Glass Fiber Reinforced Polymer) butterfly cable and production process of reinforcement
  • Reinforcement for thermoplastic GFRP (Glass Fiber Reinforced Polymer) butterfly cable and production process of reinforcement
  • Reinforcement for thermoplastic GFRP (Glass Fiber Reinforced Polymer) butterfly cable and production process of reinforcement

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Such as Figure 1-2 As shown, the reinforcing member for thermoplastic GFRP butterfly cable of the present invention includes a body 1 , the body 1 is a round rod bonded by glass fiber and resin glue, and the surface of the body 1 is coated with a plastic coating layer 2 .

[0020] The production process of reinforcing parts for thermoplastic GFRP butterfly optical cable. Multiple glass fibers are released from their own active pay-off racks, and pass through the yarn guide frame that can guide the glass fibers into the center of the molding mold. The glass fibers are surface treated through a solvent-impregnated resin hopper. The hopper The inner temperature is 60°C, the glass fiber in the hopper passes through the immersion of the alcohol-soluble nylon resin solution in the hopper at a constant speed of 40 m / min, is dried in a drying tunnel at a temperature of 120°C, and then enters the extrusion mold through the guide holes of the extrusion molding mold. Out of the m...

Embodiment 2

[0023] The production process of reinforcing parts for thermoplastic GFRP butterfly optical cable. Multiple glass fibers are released from their own active pay-off racks, and pass through the yarn guide frame that can guide the glass fibers into the center of the molding mold. The glass fibers are surface treated through a solvent-impregnated resin hopper. The hopper The inner temperature is 65°C, the glass fibers in the hopper pass through the immersion of the alcohol-soluble nylon resin solution in the hopper at a constant speed of 50 m / min, and are dried in a drying tunnel with a temperature of 130°C, and then enter the extrusion mold through the guide holes of the extrusion molding mold. Out of the mold for secondary impregnation of resin glue, the volume content of the resin glue is controlled by the mold to 18%, cooled and formed in a mold at a temperature of 55°C, and then air-cooled to room temperature by three blowers, and then coated by extrusion One layer of plastic ...

Embodiment 3

[0026] The production process of reinforcing parts for thermoplastic GFRP butterfly optical cable. Multiple glass fibers are released from their own active pay-off racks, and pass through the yarn guide frame that can guide the glass fibers into the center of the molding mold. The glass fibers are surface treated through a solvent-impregnated resin hopper. The hopper The inner temperature is 70°C, the glass fibers in the hopper pass through the immersion of the alcohol-soluble nylon resin solution in the hopper at a constant speed of 60 m / min, and are dried in a drying tunnel with a temperature of 150°C, and then enter the extrusion mold through the guide holes of the extrusion molding mold. Out of the mold for secondary impregnation of resin glue, the volume content of the resin glue is controlled by the mold to 20%, cooled and formed in a mold with a temperature of 60°C, and then air-cooled to room temperature by three blowers, and then coated by extrusion One layer of plasti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a reinforcement for a thermoplastic GFRP (Glass Fiber Reinforced Polymer) butterfly cable and a production process of the reinforcement. The reinforcement for the thermoplastic GFRP butterfly cable is characterized by comprising a reinforcement body, wherein the reinforcement body is a round rod formed by adhering glass fiber and thermoplastic resin, and a plastic-coated layer is coated on the surface of the reinforcement layer. The production process of the thermoplastic GFRP butterfly cable comprises the steps of: letting the glass fiber out, guiding in and forming, processing the surface, drying in a drying tunnel, secondarily dipping resin adhesive, cooling for forming, air-cooling to room temperature, coating the plastic-coated layer, water-cooling in a water trough, mold-stripping and then blowing, dragging, rolling a tension tower, winding on a rolling rack and completing all production processes of the reinforcement so that the reinforcement of the thermoplastic GFRP butterfly cable is obtained. The reinforcement has the advantages of minimum bending radius of not more than 10D(material diameter), tensile strength of not less than 1100Mpa, elongation at break of not more than 4 percent, tensile modulus of not less than 50Gpa, high production speed, low use cost and high cost performance.

Description

technical field [0001] The invention relates to the field of optical cable materials, in particular to a reinforcing member for a thermoplastic GFRP butterfly optical cable. [0002] The invention relates to the field of optical cable materials, in particular to a production process of a reinforcing member for a thermoplastic GFRP butterfly optical cable. Background technique [0003] FRP fiber optic cable strength member is an indispensable fiber optic cable strength member for non-metallic fiber optic cables and butterfly cables for FTTH. Although the thermosetting KFRP fiber optic cable strength member currently used has a small bending radius, the reinforcing material used is expensive aramid fiber, which is poor in cost performance. . The small bending radius of another thermosetting GFRP cannot meet the small bending performance requirements of the butterfly cable. The production process of thermosetting KFRP and GFRP optical cable reinforcement is a typical FRP pult...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G02B6/44
Inventor 周惠斌
Owner 南通科鼎复合材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap