High-gloss real stone lacquer and marble simulation lacquer

A technology of imitating marble and real stone paint, applied in the field of high gloss real stone paint and imitation marble paint, can solve the problems of inability to brush and roll, flooding, easy to dry quickly, etc., and achieve the effect of improving construction speed and convenient use.

Inactive Publication Date: 2012-08-01
尚怀兴
View PDF7 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The different proportions have different application effects, but the real stone paint used above has the disadvantages of blackish color, blooming during construction, and easy to dry quickly. At the same time, the construction method can only be sprayed, not brushed and painted. Roller coating, resulting in inconvenient construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] High-gloss real stone paint and imitation marble paint are characterized in that: it is made of the following raw materials in weight percentage:

[0020] Silicone acrylic emulsion 23.3%; HEC hydroxyethyl cellulose with a concentration of 2.5% 5.3%; film-forming aid alcohol ester twelve 0.61%; ethylene glycol 0.4%; 40-80 mesh colored sand 12.76%; 80-120 mesh Colored sand 18%; 120-200 mesh colored sand 38.6%; Huake 108 antifungal agent 0.01%; Huake 981 preservative 0.01%; fungicide HF 0.01%; concentration of 1% polyacrylamide solution 0.4%; concentration of 50 % titanium dioxide solution 0.6%;

[0021] Silicone acrylic emulsion 23.3%, HEC hydroxyethyl cellulose with a concentration of 2.5% 5.3%, film-forming aid alcohol ester twelve 0.61%, ethylene glycol 0.4%, 60 mesh colored sand 12.76%, 100 mesh colored sand 18 %, 38.6% of 160-mesh colored sand, 0.01% of Huake 108 antifungal agent, 0.01% of Huake 981 preservative and 0.01% of fungicide HF are put into a stirring tank...

Embodiment 2

[0029] High-gloss real stone paint and imitation marble paint are characterized in that: it is made of the following raw materials in weight percentage:

[0030]Silicone acrylic emulsion 22.9%; HEC hydroxyethyl cellulose solution with a concentration of 2.5% 6%; film-forming aid alcohol ester twelve 0.57%; ethylene glycol 0.45%; 40-80 mesh colored sand 12%; 80-120 Mesh colored sand 20%; 120-200 mesh colored sand 37%; Huake 108 antifungal agent 0.008%; Huake 981 preservative 0.012%; fungicide HF 0.01%; concentration of 1% polyacrylamide solution 0.35%; 50% titanium dioxide solution 0.7%;

[0031] 22.9% of silicon-acrylic emulsion, 6% of HEC hydroxyethyl cellulose solution with a concentration of 2.5%, 0.57% of alcohol ester twelve, 0.45% of ethylene glycol, 12% of 60-mesh colored sand, and 100-mesh colored sand 20%, 37% of 160-mesh colored sand, Huake 108 antifungal agent 0.008%, Huake 981 preservative 0.012% and fungicide HF 0.01% are put into a stirring tank together, the st...

Embodiment 3

[0034] High-gloss real stone paint and imitation marble paint are characterized in that: it is made of the following raw materials in weight percentage:

[0035] Silicone acrylic emulsion 24%; HEC hydroxyethyl cellulose with a concentration of 2.5% 4%; film-forming aid alcohol ester twelve 0.67%; ethylene glycol 0.35%; 40-80 mesh colored sand 15%; 80-120 mesh Colored sand 16%; 120-200 mesh colored sand 39%; Huake 108 antifungal agent 0.01%; Huake 981 preservative 0.008%; fungicide KSG-105S 0.012%; concentration of 1% polyacrylamide solution 0.45%; 0.5% of 50% titanium dioxide solution;

[0036] Mix 24% of silicon-acrylic emulsion, 4% of HEC hydroxyethyl cellulose solution with a concentration of 2.5%, 0.67% of alcohol ester twelve, 0.35% of ethylene glycol, 15% of 60-mesh colored sand, and 100-mesh colored sand 16%, 39% of 160-mesh colored sand, Huake 108 antifungal agent 0.01%, Huake 981 preservative 0.008% and fungicide KSG-105S 0.012% are put into a stirring tank together,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
decomposition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-gloss stone lacquer and a marble simulation lacquer. The high-gloss stone lacquer is characterized by being prepared from the following raw materials in weight percentage: 20.7%-25.8% of silicone-acrylic emulsion, 4%-6% of HEC (Hydroxy Ethyl Cellulose) solution with the concentration being 2.5%, 0.5%-0.7% of coalescent alcohol ester-12, 0.35%-0.45% of ethylene glycol, 10.4%-15.5% of color sand in 40-80 meshes, 15.55-20.6% of color sand in 80-120 meshes, 36.1%-41.3% of color sand in 120-200 meshes, 0.008%-0.012% of mildew preventive, 0.008%-0.012% of corrosion preventive, 0.008%-0.012% of fungicide, 0.35%-0.45% of moisturizing and polishing agent and 0.5%-0.7% of dye leveler. The high-gloss stone lacquer can be changed into the marble simulation lacquer by adding rock sheets. According to the high-gloss stone lacquer and the marble simulation lacquer, the color is not dark any more, the flower-appearing cannot be caused in construction any more, fast-drying cannot be generated any more, and the high-gloss stone lacquer and the marble simulation lacquer can be subjected to spraying, roller painting and brush coating and are convenient to use.

Description

technical field [0001] The invention belongs to a kind of architectural coating product, which relates to the improvement of various raw material ratios and production methods of real stone paint and imitation marble paint, especially a paint that can not only be sprayed, but also can be painted, brushed, rolled, and not bloomed. , High-gloss real stone paint and imitation marble paint that are not black and easy to construct. Background technique [0002] As we all know, natural granite stone is a high-grade decorative material that has attracted much attention in the market. But this natural granite stone has limited reserves, its patterns and colors are deterministic, and cannot be regenerated, so it is more and more difficult to use natural granite stone as building decoration materials. Also because of this, the production of real stone paint and imitation marble paint has become a hot topic in the field of architectural decoration. In recent years, the imitation ston...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/32
Inventor 尚怀兴
Owner 尚怀兴
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com