Production method for high-purity electronic-grade barium carbonate

A production method, barium carbonate technology, applied in the direction of calcium carbonate/strontium/barium, nanotechnology, etc., can solve the problems of complex production process, large amount of dispersant, high production cost, etc., and achieve simple production process, shortened production time, and high production efficiency. The effect of cost reduction

Inactive Publication Date: 2012-08-29
SHANDONG YINBEI TECH
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the method of producing high-purity barium carbonate is to react barium chloride and ammonium bicarbonate. The reaction raw materials are liquid, the production process is complex, there are many by-products, and the specific surface area is 1-10m 2 / g, small specific surface area, low dispersion
Moreover, the current amount of dispersant is relatively large, for example: the amount of N-acyl ED3A is generally 4% of the total solution, and the production cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method for high-purity electronic-grade barium carbonate
  • Production method for high-purity electronic-grade barium carbonate
  • Production method for high-purity electronic-grade barium carbonate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Dissolve 75kg of barium hydroxide in 1200kg of deionized water at 30°C, add 300kg of deionized water to form a barium hydroxide solution, raise the temperature of the solution to 50°C while stirring, and add 1.0‰ to the barium hydroxide solution dispersant polyacrylamide, ultrasonic treatment for 10min, continue to stir and stir at a constant temperature of 50°C for 10min; in a closed container, 20kg of carbon dioxide gas is passed into the barium hydroxide solution through a disc microporous aerator while stirring , stop stirring after the reaction is over, and then pass in carbon dioxide at a rate of 0.2-1.0kg / min, stop the ventilation when the pH value of the solution is detected to be 6; heat the slurry to complete boiling within 45 minutes, and keep boiling for 10 minutes, then stop heating; , when the temperature of the slurry drops to 75°C, precipitate and filter, and then use an atmospheric pressure microwave dryer to dry and grind and sieve to obtain high-purity...

Embodiment 2

[0022] Dissolve 250kg of barium hydroxide in 2300kg of deionized water at 40°C, add 700kg of deionized water to form a barium hydroxide solution, raise the temperature of the solution to 60°C while stirring, and add 2.5‰ to the barium hydroxide solution The dispersant polyacrylamide was ultrasonically treated for 30 minutes, continued to stir and stirred at a constant temperature of 60°C for 20 minutes; under stirring, 55 kg of carbon dioxide gas was passed into the barium hydroxide solution through a disc microporous aerator, After the reaction, stop stirring; then pass in carbon dioxide at a rate of 0.2 to 1.0 kg / min, and stop the ventilation when the pH value of the solution is 6.5; within 45 minutes, heat the slurry to complete boiling, and keep boiling for 20 minutes, then stop heating; When the temperature of the slurry drops to 20°C, precipitate and filter, and after filtering, use a vacuum microwave dryer to dry and grind and sieve to obtain high-purity electronic-grade...

Embodiment 3

[0025] Dissolve 570kg of barium hydroxide in 3000kg of deionized water at 50°C, add 1000kg of deionized water to form a barium hydroxide solution, heat the solution to 80°C while stirring, and add 5‰ to the barium hydroxide solution The dispersant polyacrylamide was subjected to ultrasonic treatment for 60 minutes, continued to stir and stirred at a constant temperature of 80 ° C for 30 minutes; under the condition of stirring, 95 kg of carbon dioxide gas was passed into the barium hydroxide solution through a disc microporous aerator, and the reaction After the end, stop stirring; then pass in carbon dioxide at a rate of 0.2 ~ 1.0kg / min, check the pH value of the solution to 7 and stop aeration; heat the barium hydroxide solution to 50°C, stir for 60 minutes in a closed state, and then carry out precipitation and filtration. The high-purity electronic-grade barium carbonate is obtained after being dried with a freeze dryer and ground and sieved.

[0026] After testing, the pu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production method for high-purity electronic-grade barium carbonate. The production method comprises the following steps: adding barium hydroxide into deionized water, heating the barium hydroxide in the stirring process and preparing into a barium hydroxide solution; adding polyacrylamide into the barium hydroxide solution and introducing carbon dioxide into the barium hydroxide solution by using a disc type microporous aerator; heating the barium hydroxide solution until the barium hydroxide solution is boiled; cooling and filtering the precipitate to obtain the barium carbonate precipitate; and drying the barium carbonate precipitate in a microwave dryer to obtain the high-purity electronic-grade barium carbonate. The polyacrylamide serves as a dispersing agent and has a good dispersing effect, so the production cost is reduced. The carbon dioxide is introduced by the disc type microporous aerator and is mixed with the barium hydroxide completely and uniformly, so the specific area of the produced barium carbonate is large, the production time is shortened, and the production efficiency is improved.

Description

technical field [0001] The invention relates to a production method of barium carbonate, in particular to a production method of high-purity electronic grade barium carbonate. Background technique [0002] High-purity barium carbonate is one of the important raw materials for producing precision high-grade electronic components. At present, the method of producing high-purity barium carbonate is to react barium chloride and ammonium bicarbonate. The reaction raw materials are liquid, the production process is complicated, there are many by-products, and the specific surface area is 1-10m 2 / g, the specific surface area is small, and the dispersion is not high. Moreover, the current amount of dispersant is relatively large, for example, the amount of N-acyl ED3A is generally 4% of the total solution, and the production cost is high. Contents of the invention [0003] The purpose of the present invention is to provide a production method of high-purity electronic grade bar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C01F11/18B82Y40/00
Inventor 古梦菲
Owner SHANDONG YINBEI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com