Nano rare-earth silicon crystal anticorrosion wear-resistant material

An anti-corrosion and wear-resistant nano-rare earth technology is applied in the field of composite materials to achieve the effects of increased strength, high interface bonding strength, and low material cost

Inactive Publication Date: 2012-09-12
HENAN CHAOBEI ENG EQUIP
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a nano-rare-earth silicon crystal composite material, which has the advantages of wear resistance, corrosion resistance, erosion resistance, high temperature resistance, low cost, and long service life, so as to solve the problems existing in existing materials and technologies. insufficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1, successively weigh the aggregate, powder, binder, rare earth, glass fiber 100kg, 45kg, 45kg, 0.5kg, 8kg prepared by step 1; carry out mixing processing, after mixing evenly, Packed into appropriate packaging specifications, that is, the finished product.

Embodiment 2

[0015] Embodiment 2, take successively the aggregate prepared by step 1, powder, binder, rare earth, glass fiber 100kg, 55kg, 55kg, 0.7kg, 12kg; carry out mixing processing, after mixing evenly, Packed into appropriate packaging specifications, that is, the finished product.

Embodiment 3

[0016] Embodiment 3, successively weigh the aggregate prepared by step 1, powder, binder, rare earth, glass fiber 100 kg, 50 kg, 50 kg, 0.6 kg, 10 kg; carry out mixing processing, after mixing evenly, Packed into appropriate packaging specifications, that is, the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of composite materials, particularly an anticorrosion wear-resistant antiscour high-temperature-resistant silicon crystal composite material. The nano rare-earth silicon crystal anticorrosion wear-resistant material is prepared by mixing the following components in parts by weight: 100 parts of aggregate, 45-55 parts of powder, 45-55 parts of binder, 0.5-0.7 part of rare-earth and 8-12 parts of glass fiber. The invention adopts factory waste subjected to high-temperature smelting as the main material, so the material cost is low; by using the nano powder as the auxiliary material, the nano rare-earth silicon crystal anticorrosion wear-resistant material has the advantages of reasonable particle size distribution, closely packed particles, high product density and high interface binding strength; the rare-earth material and the inorganic material can effectively enhance the strength, hardness, temperature resistance, corrosion resistance, fire resistance and wear resistance of the nano rare-earth silicon crystal anticorrosion wear-resistant material; and the nano rare-earth silicon crystal anticorrosion wear-resistant material can be widely used in many industries, such as thermal power generation, cement construction materials, metallurgy, mining, chemical engineering, national defense and the like.

Description

technical field [0001] The invention relates to the field of composite materials, in particular to a silicon crystal composite material which is corrosion-resistant, wear-resistant, scour-resistant and high-temperature resistant. Background technique [0002] In many industries such as thermal power generation, cement building materials, metallurgy, mining, chemical industry, etc., there are a large number of equipment or devices in the operation process. Due to the corrosion, wear and erosion of the medium, the service life of these equipment or devices is seriously affected. Directly It leads to equipment downtime, resulting in decreased equipment efficiency, increased production costs, and serious environmental pollution and other adverse consequences. At present, the usual solution is to install cast stone plates, ceramic sheets, ceramic tiles, polymer wear-resistant plates, wear-resistant steel plates, or spray wear-resistant ceramic coatings on the parts of these equip...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B14/30C04B14/32C04B14/42
Inventor 胡鹏飞胡志德赵焕军
Owner HENAN CHAOBEI ENG EQUIP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products