Method for preparing adhesive coating and adhesive film based on layer-by-layer assembly technology

A layer-by-layer assembly and bonding film technology, applied in the direction of film/sheet adhesives, adhesives, etc.

Inactive Publication Date: 2013-11-06
JILIN UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation of self-supporting films as adhesive films via layer-by-layer assembly has never been reported.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing adhesive coating and adhesive film based on layer-by-layer assembly technology
  • Method for preparing adhesive coating and adhesive film based on layer-by-layer assembly technology
  • Method for preparing adhesive coating and adhesive film based on layer-by-layer assembly technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Example 1: Preparation and Adhesive Application of Adhesive Coatings on Glass Surfaces.

[0038] The glass substrate was alternately immersed in PAH-D (1mg / mL, pH=7.4) and HA solution (1mg / mL, pH=7.4) for 15 minutes each, and this step was repeated to obtain an adhesive coating. After each step of immersion, the substrate is washed with water and dried with nitrogen. figure 1 The process of film thickness changing with the number of deposition cycles was tracked and monitored by surface profiler. It shows that the adhesion coating grows in a typical exponential growth form, that is, the thickness of the adhesion coating increases rapidly as the number of deposition cycles increases.

[0039] In this example, the concentrations of PAH-D and HA solutions are both 1 mg / mL, and the pH values ​​are both physiological pH values, that is, 7.4. Changing the concentration of the solution will not have a significant impact on the construction of the membrane, but if the concent...

Embodiment 2

[0041] Example 2: Preparation and Adhesive Application of Adhesive Film

[0042] (PAH-D / HA)*30 membrane has very good guest molecule loading capacity. We firstly spin-coated 20 mg / mL cellulose acetate acetone solution on the glass surface at 3000 rpm to obtain ~1.5 micron cellulose acetate sacrificial layer on the glass surface. After cleaning in the plasma cleaning agent for 3 minutes, build a 30-period adhesive coating of PAH-D / HA on the surface of the cellulose acetate sacrificial layer (its concentration and pH value are as in Example 1), and soak it as a whole in 15mM pH = 7.4 ibuprofen solution for 3 hours; followed by immersing the whole in acetone for 3 minutes, so that the layer-by-layer assembled polyelectrolyte adhesive coating and the glass sheet were separated by the dissolution of cellulose acetate, thus obtaining a self-supporting Adhesive film. And transfer the self-supporting layer-by-layer assembly membrane to another container with acetone for rinsing for ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
thicknessaaaaaaaaaa
strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of film adhesion, and particularly relates to a method for preparing an adhesive coating and an adhesive film based on a layer-by-layer assembly technology. The method comprises the following steps of: treating a substrate; preparing a solution; assembling a layer-by-layer assembly film; self-supporting the layer-by-layer assembly film; bonding under the coaction of water and pressure, and the like. The method is not limited by the size and shape of a substrate, and is suitable for substrates with planes, curved surfaces and irregular surfaces. The maximum shearing tensile strength of an adhesive coating prepared on a glass surface can be up to 6.9+ / -0.9MPa, and can be up to 2.7+ / -0.9MPa after the adhesive coating is prepared into a self-support film on a periosteum surface. Meanwhile, the prepared coating has very high transmission rate, and the average transmission rate of a visible light region is over 80 percent. The method has the advantages of simple process, readily-available materials, low cost and environment-friendly process, and is suitable for occasions such as lens connection, glass bonding, clinical medical treatment and the like.

Description

technical field [0001] The invention belongs to the technical field of film bonding, and in particular relates to a method for preparing an adhesive coating and an adhesive film by using layer-by-layer assembly technology. Background technique [0002] With the rapid development of adhesive material application and production technology research, due to its unique adhesive properties, the application field of adhesive materials is also expanding and refining. Traditional adhesives are generally applied in a coating manner, which may lead to uneven distribution of the adhesive, thereby reducing the adhesive effect. At the same time, the thickness of the adhesive applied is generally at the level of millimeters or above, which leads to a large amount of adhesive and increases the cost. Moreover, most of the traditional adhesives need to be heated or use organic solvents, which are harmful to the human body and may cause environmental pollution during their bonding and later u...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J7/02
Inventor 孙俊奇张健夫
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com