Method for preparing joint sealant by utilizing construction wastes

A technology for construction waste and caulking agent, applied in the field of building materials, can solve the problems of occupying land, polluting water and soil resources and air environment, wasting mineral resources, etc., and achieving the effects of convenient operation and low production cost

Active Publication Date: 2012-09-19
厦门宏鹭升建筑新材料有限责任公司
View PDF16 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If such a large amount of construction waste is directly buried without proper treatment, it will not only occupy land, pollute water and soil resources and the air environment, but also waste my country's precious mineral resources.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] (1) In terms of parts by mass, weigh 30 parts of construction waste powder below 30 mesh, 30 parts of quartz sand below 40 mesh, 35 parts of cementitious material, 3.2 parts of polymer rubber powder, 0.05 part of thickening and water-retaining agent, 0.05 parts of efflorescence agent, 1.6 parts of anti-cracking and waterproofing agent, 0.1 part of air-entraining agent;

[0015] (2) Mix the above-mentioned raw materials, and prepare the caulking agent after ball milling.

[0016] The performance index of the sample complies with GB / T 20473-2006 "Building Insulation Mortar", GB25181-2010-T "Ready Mixed Mortar", JC / T 547-2005 "Ceramic Wall and Floor Tile Adhesive", JC / T1004-2006 "Ceramic Wall Floor tile grout" standard, the main performance is as follows:

[0017] Thermal conductivity 0.20w / (m.k);

[0018] Wear resistance 1800mm 3 ;

[0019] 28-day shrinkage value 2.5mm / m;

[0020] 28-day flexural strength 3.5MPa;

[0021] 28-day compressive strength 21.0MPa;

[002...

Embodiment 2

[0025] (1) In terms of parts by mass, weigh 1 part of construction waste powder below 30 mesh, 90 parts of gelling material, 8 parts of polymer rubber powder, 0.3 part of thickening and water-retaining agent, and 0.7 part of anti-cracking and waterproofing agent;

[0026] (2) Mix the above raw materials and stir to prepare the caulking agent.

[0027] The performance index of the sample complies with GB / T 20473-2006 "Building Insulation Mortar", GB25181-2010-T "Ready Mixed Mortar", JC / T 547-2005 "Ceramic Wall and Floor Tile Adhesive", JC / T1004-2006 "Ceramic Wall Floor tile grout" standard, the main performance is as follows:

[0028] Thermal conductivity 0.29w / (m.k);

[0029] Wear resistance 1960mm 3 ;

[0030] The 28-day shrinkage value is 2.7mm / m;

[0031] 28-day flexural strength 3.8MPa;

[0032] 28-day compressive strength 23.5MPa;

[0033] 30min water absorption 4.5g;

[0034] 240min water absorption 8.9g.

Embodiment 3

[0036] (1) In parts by mass, weigh 90 parts of construction waste powder below 30 mesh, 5 parts of gelling material, 2.5 parts of anti-efflorescence agent, and 2.5 parts of air-entraining agent;

[0037] (2) Mix the above raw materials and stir to prepare the caulking agent.

[0038] The performance index of the sample complies with GB / T 20473-2006 "Building Insulation Mortar", GB25181-2010-T "Ready Mixed Mortar", JC / T 547-2005 "Ceramic Wall and Floor Tile Adhesive", JC / T1004-2006 "Ceramic Wall Floor tile grout" standard, the main performance is as follows:

[0039] Thermal conductivity 0.26w / (m.k);

[0040] Wear resistance 1890mm 3 ;

[0041] The 28-day shrinkage value is 2.1mm / m;

[0042] 28-day flexural strength 2.7MPa;

[0043] 28-day compressive strength 16.0MPa;

[0044] 30min water absorption 2.2g;

[0045] 240min water absorption 3.9g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
abrasive wear resistanceaaaaaaaaaa
flexural strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a joint sealant by utilizing construction wastes, i.e. building rubbish. The method comprises the following steps: taking the building rubbish as one part of a raw material and directly preparing the heat-insulating, mould-proof, moth-proof and anti-permeable joint sealant with low cost and environment friendliness by utilizing the existing sealant production line. The joint sealant has the joint sealing and bonding double functions, is adjustable in color and is convenient to construct.

Description

technical field [0001] The invention relates to a building material, in particular to a method for preparing a ceramic tile joint filler by using construction waste, that is, construction waste. Background technique [0002] Ceramic tiles have become one of the main building decoration materials for interior and exterior walls and floors. In order to avoid hollowing between ceramic tiles due to thermal expansion and contraction, a certain gap should be reserved between ceramic tiles and a sealant should be used to Wait for building materials to fill the gaps. At present, the main caulking agents are Portland cement, quartz powder, methyl cellulose, synthetic resin and anti-fungal agent, etc., such as "thermal insulation elastic caulking agent" (CN. "Preparation method of agent" (CN.96115732.1), "Multi-color sealant for construction" (CN200510100265.X), "Color tile sealant" (CN00117192.5), "A thermal insulation body and its manufacturing method" ( CN200710011250.5), "a meth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B26/00C04B18/16
CPCY02W30/91
Inventor 谢曦阳税安泽孙皓
Owner 厦门宏鹭升建筑新材料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com