Aluminum alloy for compression casting and casting of aluminum alloy

A technology of aluminum alloy castings and pressure casting, which is applied in the field of aluminum alloys for pressure casting and the castings of the aluminum alloys, which can solve the problems of difficulty in meeting the use requirements and poor conductivity, achieve uniform and fine grain structure, and suppress grains The effect of growing up and improving castability

Inactive Publication Date: 2012-09-19
东莞市闻誉实业有限公司
View PDF4 Cites 32 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The casting aluminum alloys provided by CN 102301021A and CN 101248200A have good yield strength and elongation, but poor electrical conductivity, which makes it difficult to meet the requirements for materials with high requirements on yield strength, elongation, and electrical conductivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum alloy for compression casting and casting of aluminum alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Si: 5.5% by weight, Mg: 0.3% by weight, Cu: 0.05% by weight, Fe: 0.2% by weight, Mn: 0.2% by weight, Ti: 0.3% by weight, Cr: 0.1% by weight, V: 0.3% by weight, balance Contains Al and unavoidable impurities. The aluminum alloy ingot is prepared according to the preparation method provided by the invention.

Embodiment 2

[0036] Si: 11.0 wt%, Mg: 0.7 wt%, Cu: 0.3 wt%, Fe: 0.1 wt%, Mn: 0.5 wt%, Ti: 0.05 wt%, Cr: 0.05 wt%, V: 0.05 wt%, Sr: 0.01% by weight, and the balance contains Al and unavoidable impurities. The aluminum alloy ingot is prepared according to the preparation method provided by the invention.

Embodiment 3

[0038] Si: 9.0% by weight, Mg: 0.6% by weight, Cu: 0.2% by weight, Fe: 0.1% by weight, Mn: 0.4% by weight, Ti: 0.1% by weight, Cr: 0.05% by weight, V: 0.05% by weight, Sr: 0.1% by weight, Sb: 0.050% by weight, and the balance contains Al and unavoidable impurities. The aluminum alloy ingot is prepared according to the preparation method provided by the invention.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides aluminum alloy for compression casting and a high-toughness aluminum alloy casting formed of the alloy through compression casting. The aluminum alloy has the advantages of superior yield strength and extensibility, low probability of sintering and superior thermal conductivity. The aluminum alloy is characterized by comprising the following components in percentage by weight: 5.5-11.0 percent of Si, 0.3-0.7 percent of Mg, 0.05-0.3 percent of Cu, 0.2-0.8 percent of Fe, 0.2-0.5 percent of Mn, 0.05-0.3 percent of Ti, 0.05-0.1 percent of Cr, 0.05-0.3 percent of V and the balance of Al and inevitable impurities. The aluminum alloy for compression casting and the casting of the aluminum alloy provided by the invention have the advantages of high yield strength and extensibility, superior thermal conductivity and low probability of sintering.

Description

technical field [0001] The present invention relates to an aluminum alloy for pressure casting and a casting of the aluminum alloy, in particular to an aluminum alloy for pressure casting with high yield strength and elongation and excellent thermal conductivity and a casting of the aluminum alloy. Background technique [0002] Aluminum alloy is a general term for alloys based on aluminum. The main alloying elements are copper, silicon, magnesium, zinc, manganese, and the secondary alloying elements are nickel, iron, titanium, chromium, lithium, etc. Aluminum alloy is the most widely used non-ferrous metal structural material in the industry. It is light in weight and has many characteristics such as excellent thermal conductivity and high corrosion resistance. It is widely used in aviation, aerospace, automobile, machinery manufacturing, shipbuilding and chemical industries. has been widely applied. [0003] According to the processing method, aluminum alloy can be divide...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/02
Inventor 叶伟炳
Owner 东莞市闻誉实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap