High-performance eutectic aluminum silicon alloy piston material of vehicle engine

A vehicle engine, eutectic aluminum-silicon technology, applied in the field of eutectic aluminum-silicon alloy piston materials for high-performance vehicle engines, can solve the problems of piston engine pistons that cannot adapt to the load and performance, model breakage, combustion chamber port cracking, etc. problem, to achieve the effect of small thermal expansion coefficient, excellent high temperature performance, and promote heterogeneous nucleation

Active Publication Date: 2012-09-19
天津新立中合金集团有限公司
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the traditional alloy grades such as ZL109, which are still widely used in the domestic industry, can no longer meet the requirements of the newly developed higher load and performance pistons, especially the high-performance vehicle engine pistons. In recent years, broken heads or Cracked combustion chamber port

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance eutectic aluminum silicon alloy piston material of vehicle engine
  • High-performance eutectic aluminum silicon alloy piston material of vehicle engine
  • High-performance eutectic aluminum silicon alloy piston material of vehicle engine

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] (1) According to mass percentage Si: 12.3%, Cu: 4.2%, Mg: 0.8%, Ni: 2.8%, Zr: 0.060%, V: 0.060%, P: 0.010%, Al is the balance, weighed for remelting Aluminum ingots, magnesium ingots for remelting, industrial silicon, electrolytic copper, pure nickel plates and AlV5 (aluminum vanadium master alloy), AlZr10 ((aluminum zirconium master alloy), AlP3 (aluminum phosphorus master alloy); industrial silicon is broken Good 1~5cm 3 small pieces;

[0058] (2) Take the sodium-free refining agent by 0.15% of the total feeding mass;

[0059] (3) Put the industrial silicon, electrolytic copper, magnesium ingot for remelting, pure nickel plate, AlV5, AlZr10, ALP3, aluminum ingot for remelting and sodium-free refining agent in step (1), step (2) into the temperature Dry in a constant temperature preheating drying oven at 250°C for 3 hours;

[0060] (4) Put the dried industrial silicon, pure nickel plate, and aluminum ingot for remelting in step (3) into the CX-GR-150 industrial elec...

Embodiment 2

[0071] (1) Si: 12.5%, Cu: 4.4%, Mg: 0.8%, Ni: 3.0%, Zr: 0.065%, V: 0.065%, P: 0.010%, based on the mass percentage of the alloying elements in the aluminum-silicon alloy , and Al is the balance, respectively weigh the industrial silicon, electrolytic copper, magnesium ingots for remelting, pure nickel plate, AlV5, AlZr10, aluminum ingots for remelting and AlP3 master alloy; wherein industrial silicon is crushed 1 ~5cm 3 small pieces;

[0072] (2) take by weighing 0.15% of the total feeding quality of step (1) sodium-free refining agent;

[0073] (3) Put the industrial silicon, electrolytic copper, magnesium ingot for remelting, pure nickel plate, AlV5, AlZr10, AlP3, aluminum ingot for remelting and sodium-free refining agent in step (1), step (2) into the temperature Dry in a constant temperature preheating drying oven at 250°C for 3 hours;

[0074] (4) Put the dried industrial silicon, pure nickel plate and aluminum ingot for remelting in step (3) into the industrial elect...

Embodiment 3

[0084] (1) According to mass percentage Si: 12.5%, Cu: 4.0%, Mg: 0.9%, Ni: 3.0%, Zr: 0.07%, V: 0.07%, P: 0.014%, Al is the balance, and remelted Aluminum ingots, magnesium ingots for remelting, industrial silicon, electrolytic copper, AlNi20 (aluminum-nickel master alloy), AlV5 (aluminum-vanadium master alloy), AlZr10 ((aluminum-zirconium master alloy), AlP3 (aluminum-phosphorus master alloy); Industrial silicon is crushed 1~5cm 3 small pieces;

[0085] (2) Take the sodium-free refining agent by 0.16% of the total feeding mass;

[0086] (3) Put the industrial silicon, electrolytic copper, magnesium ingots for remelting, AlNi20, AlV5, AlZr10, AlP3, aluminum ingots for remelting and sodium-free refining agent in step (1) and step (2) at a temperature of 250°C Dry in a constant temperature preheating drying oven for 2 hours;

[0087] (4) Put the dried industrial silicon and aluminum ingots for remelting in step (3) into the CX-GR-150 industrial electric furnace, and set the te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-performance eutectic aluminum silicon alloy piston material of a vehicle engine. On the basis of ZL109 alloy, the novel eutectic alloy material with high strength and low thermal expansion coefficient can be prepared by adjusting the alloy composition and adding trace elements such as V, Zr and P. The eutectic aluminum silicon alloy has the characteristics of being excellent in high-temperature property, high in hardness, low in thermal expansion coefficient, good in wear resistance and the like, thus being better in accordance with the requirements of the high-performance vehicle engine.

Description

technical field [0001] The invention belongs to the field of nonferrous metal material preparation technology and metamorphic treatment technology, and specifically relates to a high-performance vehicle engine eutectic aluminum-silicon alloy piston material. Background technique [0002] The piston is the heart of the engine, it bears alternating mechanical and thermal loads, and is one of the key components in the engine with the worst working conditions. Working at high temperature, high pressure and high speed determines the working efficiency of the engine, so the piston alloy is required to have better volume stability and higher high temperature strength. The continuous improvement of engine performance has led to a significant increase in the working load of the piston, thus putting forward higher requirements on the performance of the piston, especially the high temperature performance, and the piston material is the first to bear the brunt. [0003] At present, tra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/04
Inventor 黄海军李志琴田红杰霍会娟刘维维
Owner 天津新立中合金集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products