Cold bending electrical protective casing and manufacturing method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A sheathing and electrical technology, applied in electrical components and other directions, can solve the problem that customers are difficult to distinguish and distinguish, and achieve the effect of improving cold bending performance, fast plasticization, and improved thermal strength.
Active Publication Date: 2012-10-03
安徽玉发塑业有限公司
View PDF3 Cites 12 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In different seasons, the production technology and formula of the product need to be adjusted, otherwise it will become brittle in cold weather and soft in summer, and it is often difficult for customers to distinguish and distinguish in the sales process
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0028] PVC resin 75kg
[0029] Composite stabilizer 3.8kg
[0030] Stearic acid 0.5kg
[0031] Chlorinated polyethylene 0.5kg
[0032] Titanium dioxide 3kg
[0033] Paraffin 0.6kg
[0034] Light calcium carbonate 30kg
[0035] 401 additive 1kg.
[0036] After the components are mixed, they are processed by extruding through an extruder.
Embodiment 2
[0038] Cold-formed electrical sheathing tubing, made from the following components:
[0039] PVC resin 70kg
[0040] Composite stabilizer 3.5kg
[0041] Stearic acid 0.3kg
[0042] Chlorinated polyethylene 0.4kg
[0043] Titanium dioxide 3kg
[0044] Paraffin 0.5kg
[0045] Light calcium carbonate 28kg
[0046] 401 additive 0.8kg.
[0047] After the components are mixed, they are processed by extruding through an extruder.
Embodiment 3
[0049] Cold-formed electrical sheathing tubing, made from the following components:
[0050] PVC resin 80kg
[0051] Composite stabilizer 4.1kg
[0052] Stearic acid 0.6kg
[0053] Chlorinated polyethylene 0.6kg
[0054] Titanium dioxide 4kg
[0055] Paraffin 0.8kg
[0056] Light calcium carbonate 32kg
[0057] 401 additives 1.2kg.
[0058] After the components are mixed, they are processed by extruding through an extruder.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a PVC (Polyvinyl Chloride) tube, in particular to a manufacturing method of a cold bending electrical protective casing. The cold bending electrical protective casing is prepared from the following components by weight: 75 kg of PVC resin, 3.8 kg of composite stabilizer, 0.5 kg of stearic acid, 0.5 kg of chlorinated polyethylene, 3 kg of titanium dioxide, 0.6 kg of paraffin, 30 kg of light calcium carbonate and 1 kg of 401 auxiliary agent. The formula of the cold bending electrical protective casing is not influenced by seasonal temperature. The 401 processing modification auxiliary agent is added after adjustment, so that plasticizing, toughening and weathering resistance of the PVC product are promoted by a low-temperature modification toughing agent. By adding 401 into the PVC product, the PVC gelling and plasticizing effects can be promoted. Through plasticizing process operation, the PVC multiple particle structure is damaged, the release of primary particles of the PVC is promoted, a PVC extrusion processing process is formed, the plasticizing is quick, the viscosity is increased, and the thermal state strength is improved.
Description
technical field [0001] The invention relates to a PVC pipe material, in particular to a method for manufacturing a cold-formed electrical sheath pipe. Background technique [0002] Cold-formed electrical sheath pipes are mainly used to pre-buried underground wires in the early stage of buildings. In different seasons, the production technology and formula of the product need to be adjusted, otherwise it will become brittle in cold weather and soft in summer, and it is often difficult for customers to distinguish and distinguish during the sales process. Contents of the invention [0003] In order to solve the above technical problems, the object of the present invention is to provide a method for manufacturing cold-formed electrical sheath tubes that are not affected by seasonal temperatures. [0004] The technical scheme that the present invention adopts is as follows: [0005] The cold-formed electrical sheath pipe is characterized in that it is made of the following c...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more