Surface treating agent and surface treating process of glass fiber filter cloth
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A surface treatment agent and glass fiber technology, applied in the field of glass fiber surface treatment agent, can solve problems such as poor high temperature resistance, and achieve the effects of good flexibility, enhanced wetting effect, and moderate air permeability
Active Publication Date: 2014-05-07
SICHUAN FIBERGLASS GRP
View PDF8 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Since alkali-free glass fiber is less resistant to high temperature than basalt fiber, the formula mentioned in this patent is not suitable for glass fiber
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0045] A surface treatment agent for glass fiber filter cloth, comprising the following components by weight percentage:
[0046] PTFE dispersion 8%
[0047]Emulsion type high temperature softener 5%
[0048] Inorganic antistatic agent 1%
[0049] Penetrant 0.5%
[0050] Fluorosilane coupling agent 1%
[0051] Fluorocarbon Surfactant 0.5%
[0052] Demineralized water balance.
Embodiment 2
[0054] A surface treatment agent for glass fiber filter cloth, comprising the following components by weight percentage:
[0055] PTFE dispersion 15%
[0056] Emulsion type high temperature softener 10%
[0057] Inorganic antistatic agent 2%
[0058] Penetrant 1%
[0059] Fluorosilane coupling agent 2%
[0060] Fluorocarbon Surfactant 1%
[0061] Demineralized water balance.
Embodiment 3
[0063] A surface treatment agent for glass fiber filter cloth, comprising the following components by weight percentage:
[0064] PTFE dispersion 11.5%
[0065] Emulsion type high temperature softener 7.5%
[0066] Inorganic antistatic agent 1.5%
[0067] Penetrant 0.75%
[0068] Fluorosilane coupling agent 1.5%
[0069] Fluorocarbon Surfactant 0.75%
[0070] Demineralized water balance.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a surface treating agent and a surface treating process of a piece of glass fiber filter cloth, belonging to the technical field of the surface treating agent of the glass fiber. The surface treating agent disclosed by the invention comprises 8-15% of PTFE (Polytetrafluoroethylene) dispersing agent, 5-10% of emulsion type high-temperature softening agent, 1-2% of inorganic antistatic agent, 0.5-1% of penetrating agent, 1-2% of silane coupling agent, 0.5-1% of fluorocarbon surfactant and the balance of softened water. The glass fiber filter cloth produced after the treatment of the surface treating agent solves the problems that the corrosion resistance is poor and the air permeability is large in the prior art, and has the advantages that the surface colors are uniform, the flexibility is good, the folding number is large, the air permeability is moderate, and the service life is long.
Description
technical field [0001] The invention relates to a surface treatment agent and a treatment process using the treatment agent, more specifically, the invention relates to a surface treatment agent for glass fiber filter cloth and a surface treatment process for glass fiber filter cloth, belonging to the glass fiber surface treatment agent technology field. Background technique [0002] Glass fiber filter material has the advantages of high strength, stable size, high temperature resistance, good corrosion resistance and high filtration efficiency, but glass fiber also has obvious disadvantages, that is, it is brittle, not resistant to folding, and not wear-resistant. Gray, easy to wear and break, affecting service life. The quality of the surface treatment of glass fiber filter cloth has a great difference in improving the properties of folding resistance, wear resistance and water repellency. Each link is of great significance to improving the performance of the product. ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.