Cullet-doped aerated block production method

A kind of technology of aerated block and cullet, which is applied in the direction of climate sustainability, sustainable waste treatment, solid waste management, etc. It can solve the problems of difficult comprehensive utilization of cullet and has not been put into industrial realization, so as to achieve light bulk density, Solve the problem of environmental pollution, the effect of a large amount of use

Active Publication Date: 2012-11-28
安徽中龙建材科技有限公司
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] For a long time, the comprehensive utilization of cullet has been a worldwide problem. Although a lot of research has been done on the comprehensive utilization of cullet at home and abroad, due to various technical and economic reasons, most of them have not been put into industrial realization.
[0004] In summary, there have been reports of using cullet as an auxiliary raw material to produce cement, wall bricks, and road materials, but there has been no report of using cullet as the main raw material for the production of aerated blocks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] A method of doping cullet to produce an aerated block, the method comprising the following steps:

[0019] 1) After crushing the river sand and phosphogypsum respectively, take 15 parts by mass of river sand and 3 parts of phosphogypsum;

[0020] 2) Take 65 parts by mass of phosphate slag, 0.02 parts of aluminum powder, 1.5 parts of lignocellulose, 4 parts of redispersible latex powder, 5 parts of cement, and 12 parts of quicklime, and crush the River sand, phosphogypsum and phosphate rock slag are mixed and finely ground, then mixed with aluminum powder, lignocellulose, redispersible latex powder, cement and quicklime;

[0021] 3) Crushing the cullet, and taking 10 parts by mass of cullet;

[0022] 4) Put the crushed broken glass and the mixed dry material into the mixing equipment, add water to stir well, and add 2 parts of 10% sodium lauryl sulfate solution, 2 parts of epoxidized soybean oil and Put 3kg of soda ash in each cubic meter of aerated and stirred raw...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a cullet-doped aerated block production method. The method comprises the following steps: 1) respectively crushing river sand and ardealite, and preparing 12 to 19 parts of river sand and 3 to 5 parts of ardealite in parts by mass; and 2) preparing 60 to 70 parts of phosphorus slag, 0.02 to 0.03 part of powdered aluminum, 0.5 to 2 parts of methyl cellulose, 2 to 5 parts of re-dispersible polymer powder, 5 to 6 parts of cement, and 10 to 15 parts of quick lime in parts by mass, mixing and finely grinding the crushed river sand, the crushed ardealite and the phosphorus slag, and mixing with the powdered aluminum, the methyl cellulose, the re-dispersible polymer powder, the cement and the quick lime; and foaming and performing autoclaved curing. The method has the advantages that use amount of cullet is large, energy saving and environmental-friendliness effects are achieved, the problem of environmental pollution caused by cullet accumulation treatment is relieved, and a new raw material of hollow bricks is provided.

Description

technical field [0001] The invention relates to the field of new building materials, in particular to a method for producing aerated blocks by doping broken glass. Background technique [0002] Broken glass is the product of broken glass, furniture, etc., and a large amount of cullet is produced in my country every year. These cullets need to occupy a large amount of storage space, cannot be decomposed, and the cost of recycling is very high. [0003] For a long time, the comprehensive utilization of cullet has been a worldwide problem. Although a lot of research has been done on the comprehensive utilization of cullet at home and abroad, due to various technical and economic reasons, most of them have not been put into industrial realization. [0004] In conclusion, it has been reported that cullet is used as an auxiliary raw material to produce cement, wall bricks, and road materials, but there is no report on the production of aerated blocks with cullet as the main raw ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B38/10C04B18/04
CPCY02W30/91
Inventor 强晓震
Owner 安徽中龙建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products