Sintered Nd-Fe-B magnet manufacturing method and device

A manufacturing method and technology for sintering magnets, which are applied in the field of magnet manufacturing, can solve the problems of low coercivity, squareness, low heat resistance, increased manufacturing cost, complicated processes, etc., so as to avoid abnormal crystal grain growth and reduce manufacturing cost. , the effect of simplifying the process

Active Publication Date: 2012-12-26
FUJIAN CHANGJIANG GOLDEN DRAGON RARE EARTH CO LTD
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The lower the oxygen content in sintering, the more likely it is to cause over-sintering, which is more likely to cause abnormal grain growth, and the problems of low coercive force, squareness, and heat resistance are also more significant.
As a well-known improved method, in order to p...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sintered Nd-Fe-B magnet manufacturing method and device
  • Sintered Nd-Fe-B magnet manufacturing method and device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0014] A manufacturing method of a sintered neodymium-iron-boron magnet of the present invention is that in the process of manufacturing a Nd-Fe-B system sintered magnet whose oxygen content in the sintered magnet is 2500ppm or less, the oxygen content in the inert gas during pulverization In the process of crushing under the condition of 1000ppm or less, the classification step is removed, so that the original separated ultrafine powder continues to be mixed with the finished crushed powder, and enters the subsequent processing process together.

[0015] The step of removing and grading is to add a filter connected to the compressor through a pipeline in the classification device, and set the filter to block the passage of ultrafine powder, so that the ultrafine powder will not be separated in the classification device, Continue to mix in the finished powder and be collected by the finished powder collection device.

[0016] see figure 2 As shown, a pulverizing device of a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a sintered Nd-Fe-B magnet manufacturing method and device. The method comprises the following steps: in the manufacturing procedure of Nd-Fe-B system sintered magnet in which the oxygen content is below 2,500 ppm and in the crushing procedure under the condition that the oxygen content in inert gas is below 1,000 ppm, and the grading step is omitted, so that ultrafine powder which is originally separated is continually mixed in finished crushed powder and enters the follow-up processing procedure together with the finished crushed powder. By adopting the method, in the follow-up sintering procedure, AGG (Abnormal Grain Growth) can not be easily caused in the follow-up sintering procedure, and the characteristics such as simplifying the procedure and lowering the production cost, are achieved.

Description

technical field [0001] The invention relates to the technical field of magnet manufacture, in particular to a manufacturing method and device for a sintered neodymium-iron-boron (Nd-Fe-B) magnet. Background technique [0002] A magnet is an object that can generate a magnetic field. It is a magnetic dipole that can attract ferromagnetic substances such as iron, nickel, cobalt and other metals. Neodymium-iron-boron (Nd-Fe-B) magnet is a kind of magnet. It is the magnet with the highest commercial performance found at present. It is known as the magnet king. It has extremely high magnetic properties and its maximum magnetic energy product (BH )max is more than 10 times higher than ferrite (Ferrite); its own machining performance is also quite good, the working temperature can reach up to 200 degrees Celsius, and its texture is hard, stable performance, and good cost performance, so its application extremely broad. [0003] Nd-Fe-B (Nd-Fe-B) magnets are manufactured in two wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01F41/02H01F1/057H01F7/02B22F9/04
Inventor 永田浩吴冲浒
Owner FUJIAN CHANGJIANG GOLDEN DRAGON RARE EARTH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap