Feather protein viscose filament yarn and manufacturing method thereof

A technology of feather protein and viscose filament, which is applied in the direction of cellulose/protein conjugated artificial filament, chemical post-treatment of cellulose/protein artificial filament, artificial filament made of viscose, etc., which can solve the shortage of silk , expensive and other problems, to achieve the effect of solving the problem of shedding, low price, and conducive to environmental protection

Inactive Publication Date: 2013-01-02
HMEI THREAD CO LTD OF YINBIN SICHUAN +2
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to overcome the shortage of silk in the existing silk products and the high cost of alternative raw materials, the present invention provides a non-spinnable protein feather regeneration protein stock solution and cellulose xanthate solution through static mixing and pre-spinning injection for spinning. Feather protein viscose filament and manufacturing method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A feather protein viscose filament obtained from feather protein liquid and cellulose sulfonate solution at a weight ratio of 1:99% through static blending-spinning-coagulation-post-treatment, the feather protein viscose filament The loss rate of protein in the production process is 5%, and after the finished product is washed 50 times, the loss rate of fiber protein is 2%.

[0033] The manufacture method of described feather protein viscose filament is carried out according to the following processing steps:

[0034] A. Preparation of Feather Protein Liquid

[0035] Weigh the feather protein and sodium hydroxide according to the solid weight ratio of 10:1, first dissolve the feather protein in an aqueous sodium hydroxide solution with a temperature of 40°C and a concentration of 0.1% (w / w), and stir at a constant temperature for 2 hours. After obtaining the feather protein solution, filter to obtain a uniform modified feather protein solution;

[0036] B Blending of ...

Embodiment 2

[0047] A feather protein viscose filament is obtained by static blending-spinning-coagulation-post-treatment of feather protein liquid and cellulose sulfonate solution at a weight ratio of 10%:90%, and the feather protein viscose has a length of The protein loss rate of silk in the production process is 25%, and the fiber protein shedding rate of the finished product is 5% after 50 times of washing.

[0048] The manufacture method of described feather protein viscose filament is carried out according to the following processing steps:

[0049] A. Preparation of Feather Protein Liquid

[0050] Weigh the feather protein and sodium hydroxide according to the solid weight ratio of 1:1, first dissolve the feather protein in an aqueous sodium hydroxide solution with a temperature of 90°C and a concentration of 10% (w / w), and stir at a constant temperature for 3 hours. After obtaining the feather protein solution, filter to obtain a uniform modified feather protein solution;

[005...

Embodiment 3

[0062] A feather protein viscose filament is obtained by static blending-spinning-coagulation-post-treatment of feather protein liquid and cellulose sulfonate solution at a weight ratio of 40%:60%, and the feather protein viscose is long The protein loss rate of silk during the production process is 30%, and the fiber protein shedding rate of the finished product is 1% after 50 times of washing.

[0063] The manufacture method of described feather protein viscose filament is carried out according to the following processing steps:

[0064] A. Preparation of Feather Protein Liquid

[0065] Weigh the feather protein and sodium hydroxide according to the solid weight ratio of 10:1, first dissolve the feather protein in an aqueous sodium hydroxide solution with a temperature of 60°C and a concentration of 20% (w / w), and stir at a constant temperature for 30 minutes. After obtaining the feather protein solution, filter to obtain a uniform modified feather protein solution;

[006...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to feather protein viscose filament yarn and a manufacturing method thereof. The invention belongs to the material field of textile industry. According to the invention, feather protein liquid and a cellulose sulfonate solution with a weight ratio of 1-40%:60-99% are adopted; the materials are subjected to static blending, spinning, solidifying, and post-processing, such that the feather protein viscose filament yarn is obtained. During the production process, a protein loss of the feather protein viscose filament yarn is lower than 30%. After 50 times of washing upon a finished product, a fiber protein loss rate is no higher than 5%. According to the invention, the feather protein viscose filament yarn is manufactured by using waste feathers. The fiber performance is good, the cost is low, and the raw material sources are wide. The filament yarn and the manufacturing method are beneficial for environment protection.

Description

technical field [0001] The invention relates to a composite viscose filament and a manufacturing method thereof, in particular to a feather protein viscose filament and a manufacturing method thereof, belonging to the material field of the textile industry. Background technique [0002] Silk products are light and soft, with elegant luster, good hygroscopicity, and comfortable to wear. They are very popular among domestic consumers. However, due to the shortage of silk, the raw material for producing silk products, they cannot meet the needs of people's lives, and people turn to seek an alternative. The raw material of silk. Foreign countries have developed regenerated protein fibers, using casein, soybean protein, peanut protein and corn protein as raw materials, all of which were eliminated by other fibers due to low humidity, and then developed fibers such as vinylon, which have high strength. But the wearing comfort is poor. People try to blend and spin casein with pol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F8/02D01F2/08D01F11/02
Inventor 廖周荣贾卫平黄金洪
Owner HMEI THREAD CO LTD OF YINBIN SICHUAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap