Rubber hose

A rubber hose and natural rubber technology, applied in the field of rubber hose, can solve problems such as easy breakage, cracks, and high specific weight, and achieve the effects of improved cold resistance and high tensile strength

Inactive Publication Date: 2013-01-09
NANTONG HUANGHAI MOTOR
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing construction machinery vibrator rubber hoses are prone to cracks after being exposed to the sun and under harsh environmental conditions. The original rubber hoses were made of natural rubber, styrene-butadiene rubber and regenerated rubber, but they used clay as a filler. The surface of the hose is rough, hard at room temperature, and has a large specific gravity, so it is easy to break

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A rubber hose, including raw materials and additives, raw materials include chlorinated polyethylene, natural rubber and recycled rubber; additives include fillers, reinforcing agents, sunscreen agents, plasticizers, light calcium powder and auxiliary agents, the filler is carbonic acid Calcium, the enhancer is carbon black, the sunscreen is paraffin, and the plasticizer is fatty alcohol phosphate.

[0015] The composition of raw materials and additives is as follows: raw materials include 20 kg of chlorinated polyethylene, 20 kg of natural rubber and 10 kg of recycled rubber; additives include 1 kg of filler, 2 kg of reinforcing agent, 3 kg of sunscreen, 2 kg of plasticizer and auxiliary Dosage 2kg.

Embodiment 2

[0017] A rubber hose, including raw materials and additives, raw materials include chlorinated polyethylene, natural rubber and recycled rubber; additives include fillers, reinforcing agents, sunscreen agents, plasticizers, light calcium powder and auxiliary agents, the filler is carbonic acid Calcium, the enhancer is carbon black, the sunscreen is paraffin, and the plasticizer is adipate.

[0018] The composition of raw materials and additives is as follows: raw materials include 25 kg of chlorinated polyethylene, 25 kg of natural rubber and 12 kg of recycled rubber; additives include 2 kg of fillers, 3 kg of reinforcing agents, 4 kg of sunscreen agents, 2 kg of plasticizers and auxiliary Dosage 2kg.

Embodiment 3

[0020] A rubber hose, including raw materials and additives, raw materials include chlorinated polyethylene, natural rubber and recycled rubber; additives include fillers, reinforcing agents, sunscreen agents, plasticizers, light calcium powder and auxiliary agents, the filler is carbonic acid calcium, the enhancer is white carbon black, the sunscreen is paraffin, and the plasticizer is epoxidized soybean oil.

[0021] The composition of raw materials and additives is as follows: raw materials include 30 kg of chlorinated polyethylene, 30 kg of natural rubber and 15 kg of recycled rubber; additives include 3 kg of fillers, 5 kg of reinforcing agents, 5 kg of sunscreen agents, 3 kg of plasticizers and auxiliary Dosage 3 kg.

[0022] The invention adopts chlorinated polyethylene, natural rubber and regenerated rubber, has cold resistance and aging resistance, and the cold resistance increases with the increase of the amount of natural rubber, and the rubber hose produced by the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rubber hose. The hose comprises raw materials and additives. Raw materials comprise chlorinated polyethylene, natural rubber and regenerated rubber. Additives comprise a filling agent, a reinforcing agent, a sun-screening agent, a plasticizing agent and an accessory agent, wherein the filling agent is calcium carbonate, the reinforcing agent is carbon black, the sun-screening agent is paraffin, and the plasticizing agent is phosphoric acid fat alcohol ester, adipate or epoxidized soybean oil. The hose has the advantages that the chlorinated polyethylene, the natural rubber and the regenerated rubber are used, the hose is cold resistant and age resistant, the cold resistance of the hose is increased if the natural rubber amount is increased, and the hose is high in tension intensity and free from cracks.

Description

technical field [0001] The invention relates to a rubber hose. Background technique [0002] Existing construction machinery vibrator rubber hoses are prone to cracks after being exposed to the sun and under harsh environmental conditions. The original rubber hoses were made of natural rubber, styrene-butadiene rubber and regenerated rubber, but they used clay as a filler. The surface of the hose is rough, hard at room temperature, and has a large specific gravity, so it is easy to break. Therefore, it is necessary to provide a new technical solution to solve the above problems. Contents of the invention [0003] The object of the present invention is to provide a rubber hose. [0004] The technical scheme adopted in the present invention: [0005] A rubber hose, including raw materials and additives, the raw materials include chlorinated polyethylene, natural rubber and recycled rubber; the additives include fillers, reinforcing agents, sunscreen agents, plasticizers a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/28C08L7/00C08L17/00C08K13/02C08K3/26C08K3/04C08K3/36
Inventor 许丽琴
Owner NANTONG HUANGHAI MOTOR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap