A complete set of equipment and castable technology, which is applied in the direction of insulators, circuits, electrical components, etc., can solve the problems of brittleness and poor weather resistance of epoxy insulating materials, and achieve good outdoor weather resistance, high insulation and mechanical properties, and excellent mechanical properties. Effect

Active Publication Date: 2013-02-20
TAICANG LIANAN NEW INSULATION MATERIAL MFG WORKS
View PDF2 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Purpose of the invention: The technical problem to be solved by this invention is to ove

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dry outdoor type electric power complete equipment insulation casting material and preparation method thereof
  • Dry outdoor type electric power complete equipment insulation casting material and preparation method thereof
  • Dry outdoor type electric power complete equipment insulation casting material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] 1. Insulation castables for dry-type outdoor electric complete sets of equipment are composed of the following raw materials:

[0025] EHL-55A Modified High Purity Flexible Cycloaliphatic Epoxy Resin

100 parts (weight ratio)

EHLS-60 modified methyl hexahydrophthalic anhydride

80 copies

EHLP-200 reactive toughening agent

17 copies

[0026] N,N benzyldimethylamine accelerator

0.2 parts

EHLA-400 coupled silica powder

300 copies

LA epoxy stain

1 copy

[0027] 2. The preparation method of the insulating castable for dry-type outdoor electric complete sets of the present invention is as follows:

[0028] a. First, weigh each raw material according to the above weight components, preheat EHL-55A modified high-purity flexible cycloaliphatic epoxy resin at 90°C for 1.5 hours, add EHLA-400 coupled silica powder, EHLP-200 Reactive toughening agent, EHLS-60 modified methyl hexahydrophthalic anhydri...

Embodiment 2

[0035] 1. Insulation castables for dry-type outdoor electric complete sets of equipment are composed of the following raw materials:

[0036] EHL-55A Modified High Purity Flexible Cycloaliphatic Epoxy Resin

100 parts (weight ratio)

EHLS-60 modified methyl hexahydrophthalic anhydride

83 copies

EHLP-200 reactive toughening agent

18.5 servings

[0037] N,N benzyldimethylamine accelerator

0.25 parts

EHLA-400 coupled silica powder

325 copies

LA epoxy stain

2 copies

[0038] 2. The preparation method of the insulating castable for dry-type outdoor electric complete sets of the present invention is as follows:

[0039] a. First, weigh each raw material according to the above weight components, preheat the epoxy resin at 95°C for 1.2 hours, add EHLA-400 coupled silica powder, EHLP-200 reactive toughening agent, EHLS-60 modified formaldehyde Base hexahydrophthalic anhydride, N. N benzyldimethylamine a...

Embodiment 3

[0046]1. Insulation castables for dry-type outdoor electric complete sets of equipment are composed of the following raw materials:

[0047] EHL-55A Modified High Purity Flexible Cycloaliphatic Epoxy Resin

100 parts (weight ratio)

EHLS-60 modified methyl hexahydrophthalic anhydride

85 copies

EHLP-200 reactive toughening agent

20 copies

[0048] N,N benzyldimethylamine accelerator

0.3 parts

EHLA-400 coupled silica powder

350 copies

LA epoxy stain

3 copies

[0049] 2. The preparation method of the insulating castable for dry-type outdoor electric complete sets of the present invention is as follows:

[0050] a. First, weigh each raw material according to the above weight components, preheat the epoxy resin at 100°C for 1 hour, add EHLA-400 coupled silica powder, EHLP-200 reactive toughening agent, EHLS-60 modified formaldehyde Base hexahydrophthalic anhydride, N. N benzyldimethylamine accelera...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Impact strengthaaaaaaaaaa
Bending strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Login to view more

Abstract

The present invention discloses a dry outdoor type electric power complete equipment insulation casting material, which comprises the following raw materials, by weight, 100 parts of an EHL-55A modified high purity and flexibility alicyclic epoxy resin, 80-85 parts of an EHLS-60 modified methylhexahydrophthalic anhydride, 17-20 parts of an EHLP-200 reactive toughener, 0.2-0.3 part of a N,N-benzyldimethylamine accelerator, 300-350 parts of EHLA-400 coupling silicon micropowder, and 1-3 parts of an LA epoxy resin colorant. The invention further discloses a preparation method for the dry outdoor type electric power complete equipment insulation casting material. The dry outdoor type electric power complete equipment insulation casting material has characteristics of good outdoor weathering resistance, excellent mechanical performance, excellent dielectric performance and excellent heat resistance, can not deform and crack under high temperature impact and low temperature impact (-40 to 125 DEG C), and has high insulation and mechanical properties.

Description

technical field [0001] The invention relates to an epoxy casting insulating material, in particular to a dry type outdoor electrical complete equipment insulating casting material. Background technique [0002] Epoxy resin is used as casting insulation, which started around 1950 in foreign countries, but China has gradually applied it to the casting and encapsulation insulation of motors, electrical components and large electronic components since the 1970s. After decades of introduction, digestion and independent research and development, China has completed high-level research on continuous full vacuum casting and full vacuum casting technology. It realizes the air-gap-free casting product process with high degree of automation and large casting output, which creates conditions for the development of high-voltage products. At the same time, with the improvement of casting technology and equipment, higher requirements are put forward for the technology of epoxy casting ins...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/00C08K9/00C08K3/02C08G59/42H01B19/00
Inventor 闵延兵
Owner TAICANG LIANAN NEW INSULATION MATERIAL MFG WORKS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap