Method for reducing zinc ash and zinc residues in zinc pot

A technology of zinc pot and zinc ash, which is applied in the field of zinc slag and zinc ash reduction, and can solve the problems of affecting the quality of the galvanizing layer, increasing the cost of hot-dip galvanizing, and rough coating, so as to reduce heat loss, prevent oxidation, and prevent zinc gray effect

Inactive Publication Date: 2013-03-06
天津市东林热镀锌有限公司
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the whole production process, the zinc ash and zinc slag in the zinc pot not only seriously affects the quality of the galvanizing layer, but also causes the coating to be rough and produces zinc nodules.
Moreover, the cost of hot-dip galvanizing is greatly increased

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for reducing zinc ash and zinc residues in zinc pot

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] As shown in the accompanying drawing: a method for reducing zinc ash and zinc slag in the zinc pot 1. Add alumina-containing ceramic beads 3 with a diameter of ∮7-15mm on the surface of zinc 2 in zinc pot 1, and spread them densely and evenly on the surface of zinc 2, about three to four layers of alumina-containing ceramic beads 3, The thickness is about 20-45mm. Thereby, the formation of zinc ash and zinc slag in the prevention and control of the zinc pot is achieved.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for reducing zinc ash and zinc residues in a zinc pot. Alumina ceramic beads with the diameters phi of 7-15mm are added to the surface of zinc in the zinc pot, and are densely and uniformly tiled on the zinc surface in a three-layer or four-layer manner, and the thickness is about 20-45mm. The method has the following advantages: the heat loss can be reduced and the oxidation can be prevented because the alumina contained ceramic beads have the characteristics of anti-oxidation function, small heat conductivity, high melting point, small specific gravity, and no reaction with molten zinc. Alumina has an iron removal function, so the formation of iron impurities of the zinc pot is reduced. The beads which are balls can be pushed away by workpieces, and do not adhere to the workpieces. The method well controls the generation of the zinc ash and the zinc residues in the zinc pot.

Description

(1) Technical field [0001] The invention relates to a method for reducing zinc dust and zinc slag. The invention relates in particular to a method for reducing zinc ash and zinc slag in a zinc pot. (2) Background technology [0002] Hot-dip galvanizing, also known as hot-dip galvanizing, is a method in which steel components are immersed in molten zinc to obtain a metal coating. In recent years, with the rapid development of high-voltage power transmission, transportation, and communication, the requirements for the protection of steel parts are getting higher and higher, and the demand for hot-dip galvanizing is also increasing. However, in the whole production process, the zinc ash and zinc slag in the zinc pot not only seriously affects the quality of the galvanizing layer, but also causes the coating to be rough and produces zinc nodules. Moreover, the cost of hot-dip galvanizing is greatly increased. Usually, 40-80kg of zinc is consumed per 1 ton of workpiece to be p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C2/06C23C2/30
Inventor 刘玉金刘家祥
Owner 天津市东林热镀锌有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap