Anti-noise sheath for headphone cables

An earphone cable and anti-noise technology, which is applied in the sheath field of anti-noise earphone cables, can solve the problems such as inability to effectively prevent earplug noise, and achieve good anti-noise performance and noise prevention effects

Inactive Publication Date: 2013-03-20
HUBEI YINGTONG ELECTRONICS +1
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the sheath is still not effective in pr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] A sheath of an anti-noise earphone cable, the sheath of the anti-noise earphone cable is processed from the following components by mass percentage:

[0050] Hydrogenated styrene-butadiene block copolymer: 50% to 60%;

[0051] Polypropylene: 10% to 13%;

[0052] Filler: 15% to 20%;

[0053] Lubricant: 5% to 20%;

[0054] Colorant: 1% to 5%;

[0055] Stabilizer: 0.1% to 0.3%.

[0056] Among them, the hydrogenated styrene-butadiene block copolymer is a kind of hot-melt rubber, the chemical formula is (C 8 h 8 .C 4 h 6 ) x. The filler is calcium carbonate, the chemical formula is CaCO 3 . The lubricant is white mineral oil. The stabilizer is zinc stearate, the chemical formula is C 8 h 16 o 4 . The colorant is toner.

[0057] A total of 100 sheaths of anti-noise earphone cables were prepared according to the above-mentioned composition ratio, assembled on the earphone cables and connected with earplugs for noise testing. The test results show that 86% of t...

Embodiment 2

[0060] A sheath of an anti-noise earphone cable, the sheath of the anti-noise earphone cable is processed from the following components by mass percentage:

[0061] Hydrogenated styrene-butadiene block copolymer: 52% to 58%;

[0062] Polypropylene: 11%~12.5%;

[0063] Filler: 16%~19%;

[0064] Lubricant: 8% to 17%;

[0065] Coloring agent: 2% to 4%;

[0066] Stabilizer: 0.15% to 0.25%.

[0067] Among them, the hydrogenated styrene-butadiene block copolymer is a kind of hot-melt rubber, the chemical formula is (C 8 h 8 .C 4 h 6 ) x. The filler is calcium carbonate, the chemical formula is CaCO 3 . The lubricant is white mineral oil. The stabilizer is zinc stearate, the chemical formula is C 8 h 16 o 4 . The colorant is toner.

[0068] A total of 100 sheaths of anti-noise earphone cables were prepared according to the above-mentioned composition ratio, assembled on the earphone cables and connected with earplugs for noise testing. The test results show that 90% ...

Embodiment 3

[0071] A sheath of an anti-noise earphone cable, the sheath of the anti-noise earphone cable is processed from the following components by mass percentage:

[0072] Hydrogenated styrene-butadiene block copolymer: 53% to 57%;

[0073] Polypropylene: 11.5% to 12%;

[0074] Filler: 17%~18%;

[0075] Lubricant: 10% to 15%;

[0076] Colorant: 2.5% to 3.5%;

[0077] Stabilizer: 0.18% to 0.20%.

[0078] Among them, the hydrogenated styrene-butadiene block copolymer is a kind of hot-melt rubber, the chemical formula is (C 8 h 8 .C 4 h 6 ) x. The filler is calcium carbonate, the chemical formula is CaCO 3 . The lubricant is white mineral oil. The stabilizer is zinc stearate, the chemical formula is C 8h 16 o 4 . The colorant is toner.

[0079] A total of 100 sheaths of anti-noise earphone cables were prepared according to the above-mentioned composition ratio, assembled on the earphone cables and connected with earplugs for noise testing. The test results show that 93%...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

An anti-noise sheath for headphone cables is processed from the following components by mass: 50%-60% of hydrogenated styrene-butadiene block copolymer, 10%-13% of polypropylene, 15%-20% of a filler, 5%-20% of lubricant, 1%-5% of a coloring agent, and 0.1%-0.3% of a stabilizer. The hydrogenated styrene-butadiene block copolymer, with a chemical formula of (C8H8-C4H6)x, is a hot melt-type rubber. The filler is calcium carbonate with a chemical formula of CaCO3. The lubricant is white mineral oil. The stabilizer is zinc stearate with a chemical formula of C8H16O4. The coloring agent is carbon powder. The anti-noise sheath for headphone cables of the present invention can prevent noise and has good anti-noise performance after being assembled in the cable, due to the use of the specific component composition and ratio.

Description

technical field [0001] The invention relates to the technical field of cables, in particular to a sheath for anti-noise earphone wires. Background technique [0002] Headphones are one of the indispensable components of the sound system of modern electronic equipment, and the quality of the headphones directly affects the hearing effect. Earphones usually include earplugs and wires connected to the earplugs. In the process of listening, there will always be unavoidable vibration of the wires, which will cause noise in the earplugs and affect the quality of hearing. [0003] In the prior art, in order to overcome the noise generated in the earplugs caused by the vibration of the earphone wire, a sheath is usually provided outside the earphone wire to prevent the noise caused by the vibration of the earphone wire. However, such sheaths are still not effective in preventing noise generation in the earbuds. [0004] Therefore, in view of the deficiencies of the prior art, it i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L53/02C08L23/12C08K13/02C08K3/26C08K5/01C08K5/098C08K3/04H04R1/10
Inventor 黄晖傅华良
Owner HUBEI YINGTONG ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap