Laser induced metal surface layer composite TiC reinforcing method with TiO2 and acetylene as components

A laser-induced, metal surface technology, applied in the coating process of metal materials, coatings, etc., can solve the problems of high cost, easy peeling of coatings, and poor coating properties, and achieve good hardness and wear resistance.

Active Publication Date: 2013-03-20
山东润蒙应急救援装备有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The deposition temperature of the CVD method is high, exceeding the heat treatment temperature of most steel materials, and CVD uses chlorides as raw materials, and requires a set of equipment for preparing Ti-containing halide gases. The process is complicated and the cost is high, which is different from the current green industry. contradict
The PVD method has a lower formation temperature, thinner coating, low bonding strength with the substrate, easy peeling of the coating from the substrate, and poor wrapping properties
[0004] Whether it is CVD method or PVD method, the TiC coating obtained is relatively thin, with a thickness of only a few microns (μm), and the coating is mechanically bonded to the substrate, the bonding surface strength is low, and the coating is prone to peeling off during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] 1. Surface treatment of Q235A, 20 steel, 40 steel, 45 steel, 20G, 20Mn, 40Mn and 60Mn carbon structural steel:

[0017] 1. Apply industrial pure TiO on the surface of carbon structural steel 2 Powder, 1.5 mm thick;

[0018] 2. With the movement of the laser spot, acetylene is passed through, and the flow rate of acetylene is 8L / min;

[0019] 3. The laser beam scans at a speed of 500mm / min, the laser power is 900W, the laser wavelength is 1.06μm, and the spot diameter is 2mm.

[0020] 4. According to the test results, a TiC layer with a thickness of up to 500 microns is formed in situ on the surface of carbon structural steel, and the microhardness can reach above HV2600.

[0021] 2. Surface treatment of 40Cr, 35CrMoV and 20CrMnSi alloy structural steel respectively:

[0022] 1. Coating industrial pure TiO on the surface of alloy structural steel 2 Powder, 1.5 mm thick;

[0023] 2. With the movement of the laser spot, acetylene is passed through, and the flow rate o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
melting pointaaaaaaaaaa
microhardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a laser induced metal surface layer composite TiC reinforcing method with TiO2 and acetylene as components, and relates to the technical field of metal surface reinforcement. The method comprises the following steps: applying TiO2 powder on a metal surface, and in acetylene atmosphere, scanning with laser beams on the metal surface to which the TiO2 powder is applied. By adopting the above method, TiCN can be generated on the metal surface layer in an in-situ composite manner, thus enhancing the metal surface and improving the wear resistance.

Description

technical field [0001] The invention relates to the technical field of metal surface strengthening. Background technique [0002] Titanium carbide (TiC) is a typical transition metal carbide, the bond type is mixed in the same crystal structure by ionic bonds, covalent bonds and metal bonds, and its melting point is as high as 3160 °C. As a surface coating, TiC has excellent comprehensive mechanical properties such as high hardness, high melting point, wear resistance, and high temperature oxidation resistance. It is one of the most widely researched and applied thin film materials at present. [0003] The preparation technologies of TiC coating are mainly chemical vapor deposition (CVD) and physical vapor deposition (PVD). The deposition temperature of the CVD method is high, exceeding the heat treatment temperature of most steel materials, and CVD uses chlorides as raw materials, and requires a set of equipment for preparing Ti-containing halide gases. The process is comp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C24/10
Inventor 王辉左健民张荣荣童涵肖圣亮
Owner 山东润蒙应急救援装备有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap