Dual-purpose adhesive for adhering tiles and filling seams

An adhesive and dual-purpose technology, applied in the field of environmentally friendly building adhesive materials, can solve the problems of waste of materials, duplication of working hours, etc., and achieve the effects of reducing construction waste, improving constructability, and saving construction batching time

Inactive Publication Date: 2013-04-03
能高共建(北京)新型建材有限公司
View PDF2 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the different formulations of the two products, the tile adhesive and the filling agent need to be formulated separately during on-site construction, resulting in duplication of working hours and easy waste of materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dual-purpose adhesive for adhering tiles and filling seams
  • Dual-purpose adhesive for adhering tiles and filling seams
  • Dual-purpose adhesive for adhering tiles and filling seams

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Weigh 25.5g of Portland cement, 59g of quartz sand, mix and stir for five minutes to obtain mixture A, and set aside; continue to weigh 10g of Portland cement, 0.4g of wood fiber, 3g of redispersible latex powder, and 0.1g of cellulose ether g, 0.7g early strength agent, 0.5g thixotropic lubricant, 0.2g water repellent, 0.2g anti-pantherine agent, 0.2g antifungal agent, 0.2g dispersant, stir for five minutes to get mixture B, pour B Put it into A and stir for five minutes to get tile adhesive.

Embodiment 2

[0021] Weigh 25g of Portland cement, 57g of quartz sand, mix and stir for five minutes to obtain mixture A, and set aside; continue to weigh 10g of Portland cement, 1g of wood fiber, 4g of redispersible latex powder, 0.2g of cellulose ether, 0.8g early strength agent, 0.5g thixotropic lubricant, 0.3g water repellent, 0.3g anti-pantherine agent, 0.3g antifungal agent, 0.6g dispersant, stir for five minutes to get mixture B, pour B into A In the middle, stir for five minutes to get tile adhesive.

Embodiment 3

[0023] Weigh 20g of Portland cement, 61g of quartz sand, mix and stir for five minutes to obtain mixture A, and set aside; continue to weigh 10g of Portland cement, 0.7g of wood fiber, 5g of redispersible latex powder, and 0.2g of cellulose ether , early strength agent 1g, thixotropic lubricant 0.7g, water-repellent agent 0.4g, anti-pantherine agent 0.2g, anti-fungal agent 0.3g, dispersant 0.5g, stir for five minutes to get mixture B, pour B into A In the middle, stir for five minutes to get tile adhesive.

[0024] The technical indicators of 1 to 3 of the embodiment in Table 1 are compared with the current standard technical indicators of "Ceramic Wall and Floor Tile Adhesive" JC / T547-2005 and "Ceramic Wall and Floor Tile Joint Filler" JC / T1004-2006. The detection condition of the technical index of the ceramic tile adhesive inspection item provided by the present invention is the standard detection condition in " ceramic wall and floor tile adhesive " JC / T547-2005; The techn...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a dual-purpose adhesive for adhering tiles and filling seams. The dual-purpose adhesive comprises, by weight percent, 20%-40% of cement, 50%-70% of filler, 2%-5% of redispersible latex powder, 0.05%-0.2% of cellulose ether, 0.4%-1.5% of early strength agent, 0.2%-0.8% of thixotropic lubricant, 0.3%-1.5% of wood fiber, 0.1%-0.4% of water repellent 0.1%-0.6% anti-whiskering agent, 0.1%-1% of mildew preventive and 0.1%-0.6% of dispersant. The dual-purpose adhesive belongs to the field of construction adhering materials, is efficient, energy-saving, low-carbon and environment-friendly, can be used for adhering tiles and processing tile seams, and working hour repetition and material waste are avoided.

Description

technical field [0001] The invention relates to the technical field of environment-friendly building adhesive materials, in particular to a dual-purpose adhesive for pasting and filling ceramic tiles. Background technique [0002] The traditional way of cement mortar or cement slurry is widely used in pasting tiles in our country. But adopting this traditional method often has many disadvantages. If the adhesive is applied unevenly, the tiles are prone to hollowing and falling off; ordinary adhesives have poor adhesion, and large tiles or stones attached to them must be mechanically fixed or reinforced, and they do not have slip resistance. Therefore, the tiles must be pasted from the bottom, and a locator needs to be used between the tiles to ensure that the pasted tiles are horizontal and vertical, and the surface is flat. It can be seen that this method is very time-consuming, inefficient, requires a large amount of materials, and requires a high level of construction s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04
Inventor 袁泽辉赵学云董晓昆姚玉祥
Owner 能高共建(北京)新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com