Preparation method for carbon fiber surface composite coating

A technology of surface compounding and carbon fiber, applied in the direction of carbon fiber, fiber treatment, textile and papermaking, etc., can solve the problems of the weak interface between carbon fiber and resin matrix, etc., to increase surface roughness and surface energy, improve adsorption capacity, and high efficiency Effect

Active Publication Date: 2013-04-10
HARBIN INST OF TECH
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problem of weak interface between carbon fiber and resin matrix in the carbon fibe

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for carbon fiber surface composite coating

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0009] Specific Embodiment 1: This embodiment is a preparation method of a carbon fiber surface composite coating, which is specifically completed according to the following steps: 1. Pretreatment of carbon fibers: first, carbon fibers are pretreated on the fiber surface, and the pretreatment is 1min to 120min , the surface pretreated carbon fiber is obtained after taking it out, and the surface pretreated carbon fiber is washed with deionized water for 1min~120min, and then the washed surface pretreated carbon fiber is placed in an oven at a temperature of 90°C~500°C Drying for 1min~60min, the pretreatment of carbon fiber is completed, and the pretreated carbon fiber is obtained; 2. Coating: soak the pretreated carbon fiber in phenolic resin slurry for 1min~300min, and get the surface coated phenolic resin after taking it out Carbon fibers of resin prepolymers; 3. Curing: Curing the carbon fibers coated with phenolic resin prepolymers obtained in step 2 at a pressure of 0.1MPa...

specific Embodiment approach 2

[0013] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the pretreatment liquid described in step 1 is acid treatment, plasma treatment or gamma ray treatment. Others are the same as the first embodiment.

specific Embodiment approach 3

[0014] Embodiment 3: The difference between this embodiment and Embodiment 1 or 2 is that in step 1, the carbon fiber is firstly immersed in the pretreatment liquid to pretreat the surface of the fiber, and the pretreatment lasts for 5 minutes to 110 minutes. For the treated carbon fiber, use deionized water to wash the surface pretreated carbon fiber for 5min~110min, then place the washed surface pretreated carbon fiber in an oven, and dry it at a temperature of 80℃~360℃ for 5min~55min , that is, the pretreatment of carbon fibers is completed to obtain pretreated carbon fibers. Others are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Interlaminar shear strengthaaaaaaaaaa
Interlaminar shear strengthaaaaaaaaaa
Interlaminar shear strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method for a carbon fiber surface composite coating and relates to a preparation method for a composite coating. The invention aims to solve the problem that in the carbon fiber composite material prepared by the conventional method, a weak interface exists between a carbon fiber and a resin matrix. The preparation method comprises the following steps: I, preprocessing the carbon fiber; II, coating; III, solidifying; IV, carbonizing; and V, functionalizing the coating to obtain the carbon fiber surface composite coating. The preparation method has the advantages as follows: I, the interlaminar shear strength of the composite material is increased by 16 to 62 percent respectively; II, the composite materials is tightly linked with the carbon fiber, difficult to strip and high in stability; III, different functions are given to the carbon fiber by adjusting the chemical constitution and the component proportioning of phenolic resin slurry or the preparation method can be applied to different types of resin matrix composite materials; and IV, the preparation method is a continuous method, simple, high in efficiency, good in effect and easy in industrialized production. The preparation method is mainly applied to preparation of the carbon fiber surface composite coating.

Description

technical field [0001] The invention relates to a preparation method of a composite coating. Background technique [0002] Carbon fiber is a fibrous carbon material with a lower density than metal aluminum, but higher strength than steel, and has the characteristics of corrosion resistance and high modulus. The carbon fiber industry plays an important role in the upgrading of pillar industries in developed countries and the improvement of the overall quality of the national economy. It is also of great significance to the adjustment of my country's industrial structure and the upgrading of traditional materials. Advanced carbon fiber composites play an important role in aviation, aerospace, military, construction and other fields. The interface of carbon fiber composite materials plays a decisive role in its performance, and has been recognized as a basic and common research topic throughout the development of composite materials. The interface directly affects the stress ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/41D06M11/74D06M11/79D06M11/46D06M15/643D06M11/49D06M11/83D06M10/10D06M10/06C08K9/04C08K9/02C08K9/06C08K7/06D06M101/40
Inventor 黎俊黄玉东胡帧宋元军刘丽
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap