Sodium-potassium-hydrogen type ferrierite and method for preparing same

A technology of ferrierite and sodium potassium hydrogen, applied in the field of sodium potassium hydrogen type ferrierite and its preparation, can solve problems such as unsuitable zeolite preparation, and achieve the effects of inhibiting side reactions, high application prospect and high isobutene selectivity

Active Publication Date: 2015-07-22
CHINA PETROLEUM & CHEM CORP +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the conventional ion exchange method is not suitable for the preparation of such zeolites

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] 20 g of NaK-FER zeolite, 0.21 g of NH 4 Cl and 400 g deionized water were mixed evenly to make a slurry, stirred at room temperature (25°C) for 2 hours, then filtered, and the filter cake was thoroughly rinsed with deionized water 30 times the dry weight of NaK-FER zeolite, and dried at 110°C Drying and roasting at 550°C yielded the sample NH-1 of the present invention, whose properties are shown in Table 1.

Embodiment 2

[0015] 20 g of NaK-FER zeolite, 0.43 g of NH 4 Cl and 400 g deionized water were mixed evenly to make a slurry, stirred at room temperature (25°C) for 2 hours, then filtered, and the filter cake was thoroughly rinsed with deionized water 30 times the dry weight of NaK-FER zeolite, and dried at 110°C Drying and roasting at 550°C yielded the sample NH-2 of the present invention, the properties of which are shown in Table 1.

Embodiment 3

[0017] 20 g of NaK-FER zeolite, 0.86 g of NH 4 Cl and 400 g deionized water were mixed evenly to make a slurry, stirred at room temperature (25°C) for 2 hours, then filtered, and the filter cake was thoroughly rinsed with deionized water 30 times the dry weight of NaK-FER zeolite, and dried at 110°C Drying and roasting at 550°C yielded the sample NH-3 of the present invention, the properties of which are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses sodium-potassium-hydrogen type ferrierite and a method for preparing the same. The sodium-potassium-hydrogen type ferrierite comprises 0.02%-0.1wt% of Na2O, 1.0%-5.0wt% of K2O, wherein the molar ratio of SiO2 to Al2O3 is 8-50. The method adopts a sodium-potassium-hydrogen type ferrierite partial ammonium exchange method. The method comprises that the sodium-potassium-hydrogen type ferrierite and an inorganic ammonium salt water solution with a certain concentration are pulped uniformly, and the exchanged pulp is filtered, eluted, dried and calcinated. After the method is adopted, the pH value of the exchange fluid does not need to be adjusted, the concentration of the inorganic ammonium salt water solution only needs to be changed, and the sodium-potassium-hydrogen type ferrierite with an appropriate total alkali metal content can be obtained through one or two times of exchange at room temperature and has good usability in straight-chain olefin isomerization reaction.

Description

technical field [0001] The invention relates to a sodium potassium hydrogen type ferrierite and a preparation method thereof. Background technique [0002] Ferrierite, or FER zeolite, is a zeolite with a mesopore structure. Its basic structural unit is a five-membered ring, and these five-membered rings are organically connected by ten-membered rings, eight-membered rings and six-membered rings to form a FER zeolite framework. . FER zeolite has a one-dimensional ten-membered ring straight channel (0.42×0.54 nm) along the [001] direction, and a one-dimensional eight-membered ring straight channel (0.35×0.48 nm) along the [010] direction. The surface is elliptical, and the space diameter of the cage-like structure formed at the intersection of two channels is about 0.6 to 0.7 nm. Due to the unique shape-selective effect of FER-type zeolite pores, it is suitable for various shape-selective catalytic reactions. In recent years, it has been found that FER zeolite exhibits good...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J29/40C01B39/50
Inventor 周峰陈明张淑梅张宝国翟庆铜苏杰
Owner CHINA PETROLEUM & CHEM CORP