Oil corrosion-resistant agent for concrete and preparation method thereof

An corrosive agent and concrete technology, which is applied in the field of high-strength concrete oil-resistant corrosion agent and its preparation, can solve the problems of poor oil resistance of concrete and achieve the effects of improving oil resistance, improving oil resistance, and reducing pore structure

Active Publication Date: 2013-04-17
北京东方建宇混凝土科学技术研究院有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to solve the poor oil resistance of concrete in the p

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048]Weigh 10 kg of sodium methyl siliconate, 20 kg of water glass, 0.03 kg of sodium rosinate, 5 kg of polyethylene glycol, and 49 kg of water, and stir well to prepare the concrete oil corrosion resistance agent A described in this example.

Embodiment 2

[0050] Weigh 15kg of potassium ethyl siliconate with a molecular weight of 100-200, 15kg of water glass with a modulus of 2.2, 0.06kg of sodium dodecylbenzenesulfonate, 7kg of glycerol, and 56kg of water, and stir them well to obtain Concrete oil corrosion resistance agent B described in this example.

Embodiment 3

[0052] Weigh 20 kg of sodium phenylsilanolate with a molecular weight of 100 to 200, 10 kg of water glass with a modulus of 2.3, 0.03 kg of sodium abietate, 9 kg of polyethylene glycol, and 54 kg of water, and stir well to obtain the mixture prepared in this example. Concrete anti-oil corrosion agent C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an oil corrosion-resistant agent for concrete, belonging to the field of building material preparation. The oil corrosion-resistant agent comprises organic silicon, water glass, an air entraining agent, polyol and water, wherein the addition amounts of the above components by weight percent are respectively 10-30%, 10-20%, 0-0.05%, 5-15% and 35-75%. According to the invention, when the oil corrosion-resistant agent for concrete is used in the concrete, the oil corrosion resistance and the durability of the concrete can be improved significantly. Tests show that when the oil corrosion-resistant agent accounting for 2-3% of the total weight of the concrete is added to the concrete, the oil-resistant penetration height ratio of the concrete can be increased by more than 35%, the oil absorption rate can be increased by more than 40%, and the compressive strength of the concrete at various ages can be increased by more than 16%.

Description

technical field [0001] The invention relates to an anti-oil erosion agent for high-strength concrete and a preparation method thereof. The invention belongs to the field of building material preparation. Background technique [0002] In the production process of machinery industry, the oil splashed out due to transmission, metal cutting and grinding, such as some mineral oil or vegetable oil, has the characteristics of low viscosity and strong penetration ability, which makes it very difficult to contact with concrete. It is easy to penetrate into concrete and destroy the bond between cement and aggregate in concrete. In addition, some oils penetrating into concrete will also contain some meta-acids or esters, which will damage the strength and durability of reinforced concrete components. [0003] For the above problems, the damage to concrete caused by the penetration of oil substances can be effectively solved by improving the oil resistance of concrete. Oil-resistant ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/40
Inventor 王安岭段遵莉武俊宇
Owner 北京东方建宇混凝土科学技术研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap