The technology of silicone emulsion and thermal insulation material is applied in the waterproof field of inorganic building thermal insulation materials. Convenience and the effect of ensuring storage stability
Active Publication Date: 2013-04-17
山东环绿康新材料科技有限公司
View PDF7 Cites 14 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0009] In addition, these patents all relate to the use of silicone aqueous emulsions in the waterproofing of building materials such as bricks, stones, concrete, mortar and cement slurry, etc., but they have many types of materials, or relatively complicated processes, and none of them involve the use of Application of waterproofing agent for wall rock wool insulation material
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0041] Embodiment 1 prepares a kind of organosilicon emulsion for the waterproofing agent of building exterior rock wool thermal insulation material
[0042] ⑴ Raw material composition
[0043]
[0044] All raw materials are local commercially available chemical commodities.
[0045] ⑵ Preparation method
[0046] First add 20kg of water and 1kg of emulsifier into the reaction kettle, raise the temperature to 60-70°C, stir well, add 5kg of methyl alkoxy silicone oil, 5kg of amino silicone oil, and 5kg of polyethylene glycol, and stir at this temperature for pre- Emulsified for 1 hour, and cooled to obtain a pre-emulsion.
[0047] Add 100kg of methyl silicone oil to the above-mentioned pre-emulsion in a high-speed emulsifier with a rotational speed of 5000-8000r / min, perform high-speed emulsification for 2-3 hours, and then add the remaining 50kg of water and 0.1kg of blasticidin fungicide in the dosing water part, and continue to emulsify for about 1 hour to obtain a sili...
Embodiment 2
[0054] Example 2 Preparation of a silicone emulsion for waterproofing agent of building exterior rock wool insulation material
[0055] ⑴Material Composition
[0056]
[0057] All the other are with embodiment 1.
Embodiment 3
[0058] Embodiment 3 prepares a kind of organosilicon emulsion for building exterior wall rock wool insulation material waterproofing agent
[0059] ⑴Material Composition
[0060]
[0061] All the other are with embodiment 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses application of an organic silicone emulsion waterproof agent in an outer wall rock wool heat insulating material waterproof agent. The waterproof agent is prepared from the following raw materials in percentage by mass: 100 parts of methyl silicone oil, 5-30 parts of methyl alkoxy silicone oil, 2-10 parts of amino silicone oil, 5-10 parts of polyethylene glycol, 0.2-1.0 part of an emulsifier, 0.1-1.0 part of a sterilizing agent and 6-100 parts of distilled water or deionized water. The preparation method comprises the following steps of: proportioning 20%-40% of water and the emulsifier, stirring the solution uniformly at 60-70 DEG C, adding methyl silicone oil, methyl alkoxy silicone oil, amino silicone oil and polyethylene glycol, pre-emulsifying the mixture for 1 hour, cooling to room temperature for later use, putting the pre-emulsifying liquid in a high-speed emulsifying machine of which the rotating speed is 5000-8000r / min, adding methyl silicone oil into the pre-emulsifying liquid for high-speed emulsification for 2-3 hours, adding the rest 60%-80% of water and the sterilizing agent, performing high-speed emulsification again for 1 hour, and then obtaining a waterproof organic silicone emulsion waterproof agent for an outer wall rock wool heat insulating material, wherein the organic silicone emulsion waterproof agent is white emulsion in appearance, pH value of the 10% of water solution is 6.5-7.0, solid content is 50%-70%, good centrifugation stability is achieved, the emulsion is not layered after being centrifuged at the rotating speed of 3000r / min for 30min, good thermal stability is achieved, and the emulsion is not layered after being maintained for 4 hours at 70+ / -2 DEG C. The organic silicone emulsion waterproof agent disclosed by the invention is used for soaking and spraying the outer wall rock wool heat insulating material or added into an adhesive for manufacturing rock wool heat insulating materials.
Description
technical field [0001] The invention belongs to the field of waterproofing of inorganic building thermal insulation materials, and in particular relates to the application of an organic silicon emulsion waterproofing agent in the waterproofing agent of rock wool thermal insulation materials for external walls. Background technique [0002] Rock wool is a high-quality and efficient thermal insulation material. It has good thermal insulation, sound insulation and sound absorption properties. Compared with traditional thermal insulation materials, rock wool and its products have light bulk density, small thermal conductivity, non-combustible, fireproof and non-toxic. Toxicity, stable chemical performance, long service life and so on. Due to its good thermal insulation and fire safety performance, rock wool products are widely used in external wall insulation materials. [0003] In order to ensure the good thermal insulation performance of rock wool insulation materials for ext...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.