Trademark leather and preparation method thereof
A trademark leather and dry process technology, applied in the field of synthetic leather, can solve the problems of poor surface wear resistance and scratch resistance, poor pressure change effect, inconspicuous color change and pressure change texture, etc., and achieve good tensile strength and elongation. rate, to achieve natural luster, good effect of hot pressing
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0043] Example one
[0044] Trademark leather and its preparation method:
[0045] (1) Top coat: 100 parts by weight of weak solvent type dry PU resin with 200 modulus are fully dissolved in 50 parts by weight of DMF to prepare the top base slurry, and the base is coated on the release with a doctor blade On the paper, the coating thickness is 0.05mm, and then it is dried at 120°C and normal pressure for 3 minutes.
[0046] (2) Coating discoloration layer: Add the following parts by weight to the B90-2F mixer produced by Hangzhou Instrument Factory: 223 parts of aliphatic dry PU resin with 50 modulus, 24 parts of DMF, 18 parts of ethyl acetate, high modulus Measure 3 parts of PU resin particles, 6 parts of fumed silica and 34 parts of polypropylene wax powder. Stir evenly at 2000 rpm to make color-changing PU resin. Add 4 parts by weight of rainbow RP color paste and mix evenly. Use a doctor blade to coat the base slurry into the color-changing layer on the top layer with a coating...
Example Embodiment
[0048] Example two
[0049] Trademark leather and its preparation method:
[0050] (1) Top coat: 100 parts by weight of low-solvent dry PU resin with 200 modulus is fully dissolved in 60 parts by weight of DMF to prepare the top base slurry, and the base is coated on the release with a doctor blade On the paper, the coating thickness is 0.05mm, and then it is dried at 120°C under normal pressure for 3 minutes.
[0051] (2) Coating discoloration layer: Add the following parts by weight to the B90-2F mixer produced by Hangzhou Instrument Factory: 23 parts by weight of aliphatic dry PU resin with 50 modulus, 26 parts of DMF, 19 parts of ethyl acetate, high modulus Measure 4 parts of PU resin particles, 7 parts of fumed silica and 36 parts of polypropylene wax powder, stir evenly at 2000 rpm to make color-changing PU resin, add 6 parts by weight of rainbow RP color paste, stir evenly, configure Use a doctor blade to coat the base slurry into the color-changing layer on the top layer wi...
Example Embodiment
[0053] Example three
[0054] Trademark leather and its preparation method:
[0055] (1) Top coat: 100 parts by weight of weak solvent type dry PU resin with 200 modulus is fully dissolved in 70 parts by weight of acetone to prepare the top base slurry, and the base is coated on the release with a doctor blade. On the paper, the coating thickness is 0.05mm, and then it is dried at 120°C and normal pressure for 3 minutes.
[0056] (2) Coating discoloration layer: Add the following parts by weight to the B90-2F mixer produced by Hangzhou Instrument Factory: 21 parts of aliphatic dry PU resin with 50 modulus, 23 parts of DMF, 18 parts of ethyl acetate, high modulus Measure 3 parts of PU resin particles, 6 parts of fumed silica and 33 parts of polypropylene wax powder. Stir uniformly at 2000 rpm to make color-changing PU resin. Add 5 parts by weight of rainbow RP color paste and mix evenly. Use a doctor blade to coat the base slurry into the color-changing layer on the top layer with a...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap